Purpose: The objective was to assess the effect of various etching techniques on the shear bond strength(SBS) of resin infiltrated sound/ demineralized enamel.
Materials and methods: A total of 180 extracted human upper incisors' enamel surfaces were utilized. Half of these specimens underwent artificial demineralization, which involved exposing to an acidic buffer with a pH of 4.8(14 days). The remaining half of the specimens were kept in their original sound condition. Subsequently, both the sound/ demineralized specimens were divided into 6 groups according to the presence (I)/absence (NI) of resin infiltrant and etching methods (35% phosphoric acid (PA), 9% hydrofluoric acid (HFA), and Er,Cr:YSGG laser(L) (n=15): Following different etching procedures, an etch-and-rinse adhesive system was used, before the application of a nanohybrid composite to the enamel surfaces. Then all specimens were submitted to SBS test (MPa). three-way ANOVA and Bonferroni test were used for statistical analysis(p=0.05).
Results: PA showed the highest SBS in the I groups compared with L and HFA groups, both in demineralized and sound enamel (p<0.05). On sound enamel, L showed higher SBS than HFA (p<0.05). On demineralized enamel, L showed similar values with HFA(p>0.05). In the NI groups, L showed similar SBS to HFA on both demineralized and sound enamel(p>0.05).
Conclusion:Resin-infiltrated enamel can be etched by 35% phosphoric acid without jeopardize bond strength.
resin infiltration shear bond strength etching laser composite resin
Baskent University Research Fund
Project no: D-DA17/03
We would like to thank Prof. Dr. Neslihan Arhun for her mentoring and consistent support .
Project no: D-DA17/03
Birincil Dil | İngilizce |
---|---|
Konular | Restoratif Diş Tedavisi |
Bölüm | Original Research Articles |
Yazarlar | |
Proje Numarası | Project no: D-DA17/03 |
Erken Görünüm Tarihi | 31 Aralık 2023 |
Yayımlanma Tarihi | 31 Aralık 2023 |
Gönderilme Tarihi | 31 Temmuz 2023 |
Yayımlandığı Sayı | Yıl 2023 Cilt: 50 Sayı: 3 |