@article{article_1145856, title={The Adsorption of Eriochrome Black T onto the Activated Carbon Produced from Pepper Stalks}, journal={Journal of Engineering Technology and Applied Sciences}, volume={8}, pages={107–118}, year={2023}, DOI={10.30931/jetas.1145856}, author={Dolaş, Hacer}, keywords={Pepper Stalk, phosphoric acid, activated carbon, eriochrome black T, adsorption}, abstract={The aim of this paper is to present the evaluation of the adsorption of Eriochrome Black T (EBT) on the activated carbon (trH-BS) produced from pepper stalk by activating with 50% phosphoric acid solution (H3PO4) and then by carbonizing at 650 oC for 30 min. in atmosphere of nitrogen (N2) was presented. The isotherm of trH-BS was Type IV, representing micro, meso and macroporous structures. The micropore volume and micropore surface area values of trH-BS were 0.39 cc/g and 1107.294 m2/g, respectively. Also, its meso and macropores had a volume of about 15-17 cc/g and an average surface area of 400 m2/g. The adsorption energy was 18.156 kJ/mol and the BET surface area was 756.257 m2/g. Depending on Langmuir parameters, monolayer capacity was determined as 55,56 mg/g. the enthalpy change was calculated as 30.78 kJ/mol. The structure of trH-BS was clarified structurally and morphologically and the formations like nano rod were seen at Scanning Electron Microscopy (SEM) images. By using trH-BS, the adsorption of EBT from the aqueous medium was investigated using 5 different parameters. As a result, it was found that the adsorbents obtained from pepper stalks are suitable for use in EBT adsorption with a ratio of about 50% under suitable conditions.}, number={2}, publisher={Muhammet KURULAY}