TY  - JOUR
T1  - THE INVESTIGATION OF MICROSTRUCTURE AND HARDNESS OF Cu-Al/B4C COMPOSITES PRODUCED BY USING HOT PRESS
TT  - SICAK PRESLEME İLE ÜRETİLEN Cu-Al/B4C KOMPOZİTİN MİKROYAPI VE SERTLİK İNCELEMESİ
AU  - Özel, Serkan
AU  - Çelik, Ertugrul
AU  - Turhan, Hüseyin
PY  - 2009
DA  - February
DO  - 10.12739/nwsaes.v4i1.5000067171
JF  - Engineering Sciences
PB  - E-Journal of New World Sciences Academy
WT  - DergiPark
SN  - 1308-7231
SP  - 106
EP  - 112
VL  - 4
IS  - 1
LA  - tr
AB  - In this study, Cu-Al-B4C metal matrix composite (MMC) material was produced by using hot pressing at powder metallurgy (PM) process. Powder samples were prepared in proportion as 5%, 10% and 20% B4C was added in to Cu-%5 Al powder mixture.  Prepared powder samples subject to hot pressing at 600 oC, 4 minutes under argon inert gas atmosphere, 30 MPa/cm2 pressure.  Pressed specimens were investigated hardness and microstructure.  At the result of the experiments, it's fastened down; B4C affected the hardness and microstructure of the materials, which added at the different rates in matrix.
KW  - Cu matrix composite
KW  - 
KW  - B4C
KW  - 
KW  - Powder metallurgy
KW  - 
KW  - Hot press
KW  - .
KW  - 
N2  - Bu çalışmada, Cu-Al-B4C metal matrisli kompoziti (MMK), toz metalurjisi (TM) yöntemi kullanılarak sıcak presleme ile üretilmiştir. Cu-%5 Al toz karışımı içerisine %5, %10 ve %20 oranında B4C ilave edilerek toz karışımları hazırlanmıştır. Hazırlanan toz karışımları argon gazı atmosferinde, 30 MPa/cm2 basınç altında, 600 oC'de 4 dakika bekletilerek sıcak presleme işlemine tabi tutulmuştur.  Preslenen numunelerin optik mikroyapı incelemeleri ile birlikte sertlik değerleri ölçülmüştür. Deneyler sonucunda, farklı oranlarda ilave edilen B4C'nin mikro yapı ve sertliği etkilediği görülmüştür. %20 B4C ilaveli numunede en yüksek sertlik değeri tespit edilmiştir.
UR  - https://doi.org/10.12739/nwsaes.v4i1.5000067171
L1  - https://dergipark.org.tr/en/download/article-file/186405
ER  -