T1  - Beton Parke Taşı Özelliklerine Taş Unu Katkısının Etkileri
TT  - The Effects of Stone Powder Additive on Concrete Parquet Stone Properties
AU  - Görhan, Gökhan
AU  - Demir, İsmail
AU  - Başpınar, M. Serhat
AU  - Kahraman, Erhan
PY  - 2019
DA  - June
JF  - Journal of Innovations in Civil Engineering and Technology
JO  - JICivilTech
PB  - Hüseyin AKBULUT
WT  - DergiPark
SN  - 2687-2129
SP  - 21
EP  - 27
VL  - 1
IS  - 1
LA  - tr
AB  - Bu çalışmada taş unu katkılı beton parke taşlarının özellikleri araştırılmıştır. Buamaçla karışımlarda CEM I 42,5 R tipi çimento, 0-4 ve 6-12 mm’lik iki farklı agregagradasyonu kullanılmıştır. Taş unu katkısı, çimentonun ağırlıkça % 5’i ve % 10’uoranında, Na2SO4 katkısı ise çimentonun % 1’i oranında kullanılmıştır. Biri kontrolkarışımı olmak üzere toplam 6 farklı karışımda deney örnekleri hazırlanmıştır. Tümkarışımlarda su/çimento oranı sabit tutulmuş ve bu oran 0,3 olarak alınmıştır.Bileşenler pan mikserde homojen bir hale gelinceye kadar karıştırılmış ve ardındanvibrasyonlu parke makinesinde şekillendirilmiştir. Her karışım serisinden 12 adetparke örneği üretilmiş ve dayanım kazanmaları amacıyla 28 gün su kürüne tabitutulmuşlardır. Kür uygulanan örnekler üzerinde; yarmada çekme dayanımı, böhmeaşınma oranı, su emme, görünür porozite, birim hacim ağırlık ve görünür yoğunlukdeneyleri gerçekleştirilmiştir. Elde edilen bulgulara göre, karışımlara eklenen taş unukatkısı örneklerin yarmada çekme dayanımı, birim hacim ağırlığı ve görünüryoğunluk değerlerini düşürürken; böhme aşınması, su emme ve porozite değerleriniarttırmıştır. Na2SO4 ve taş unu katkısının beraber uygulandığı karışımlarda ise taşunu katkısının artmasıyla birlikte yarmada çekme dayanımı ve böhme aşınmadeğerlerinde artışlar belirlenmiştir.
KW  - Parke
KW  - Çimento
KW  - Taş Unu
N2  - In this study, the properties of concrete parquet stones with stone powder areinvestigated. For this purpose, CEM I 42,5 R type cement, two aggregate gradations(0-4 and 6-12 mm) were used. Stone powder was used as 5% and 10% by weight ofcement, and Na2SO4 additive was used as 1% of cement. Test samples were preparedin 6 different mixtures, one of which was a control mixture. Water / cement ratio waskept constant in all mixtures and this rate was taken as 0.3. The components weremixed in the pan mixer until they were homogenous and then shaped in a vibratingparquet machine. 12 pieces of parquet were produced from each series of mixturesand subjected to water curing for 28 days in order to gain strength. Curing on thesamples applied; tensile strength, Bohme abrasion rate, water absorption, apparentporosity, unit weight and apparent density tests were performed. According to thefindings, the added stone powder to the mixtures decreased the tensile strength, unitweight and apparent density values of the specimens. However, bohme abrasion rate,water absorption and porosity increased. With the addition of Na2SO4 and stonepowder admixture, it was concluded that the tensile strength and bohme abrasionrate values were increased.
CR  - Durmuş, G., Şimşek, O., 2008. Uçucu Küllerin Beton Kilitli Parke Taşı Üretiminde Kullanımının Araştırılması. Tubav Bilim Dergisi, Cilt 1, Sayı 1, ss.1-6.
CR  - Çelik, M. Y., 2003. Dekoratif Doğal Yapı Taşlarının Kullanım Alanları ve Çeşitleri. Madencilik, Cilt 42, Sayı 1, ss. 3-15.
CR  - Tunay, C., 2008. Dekoratif Kaplama Sistemlerinde Asfalt Kullanımı ve Alternatif Yöntemler ile Teknik-Ekonımik Yönden Karşılaştırılması. Yüksek Lisans Tezi, S.D.Ü., Fen Bil. Ens., Isparta.
CR  - TS 802, 1985. Beton Karışım Tasarımı Hesap Esasları, TSE, Ankara.
CR  - TS 2824 EN 1338, 2005. Zemin Döşemesi için Beton Kaplama Blokları-Gerekli Şartlar ve Deney Metotları, TSE, Ankara.
UR  - https://dergipark.org.tr/en/pub/jiciviltech/issue//604113
L1  - https://dergipark.org.tr/en/download/article-file/782757
ER  -