MICROSTRUCTURE AND ABRASIVE WEAR BEHAVIOUR OF GAS TUNGSTEN ARC SYNTHESIZED Fe-Cr-C-Ti COATTING ON AISI 304 STAINLESSS STEEL
Abstract
AISI 304 stainless steel was coated by using Fe-Cr-C-Ti alloy powders and gas tungsten arc processing method. The microstructure and microhardness values of the coating surfaces were investigated. Gas tungsten arc processing parameters to be committed dentritic structure was seen. In the coating ground plates primary MxCy carbides and secondary phases that is largely with Ti elements was determined. The result of rise 660 Hv. This increase is parallel powder amount. When the look at wear performance of coating samples, which has high powder amount.
Keywords
TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI
Abstract
AISI 304 paslanmaz çelik yüzeyinde, gaz tungsten ark kaynak yöntemiyle Fe-Cr-C-Ti tozları ergitilerek kaplama tabakası oluşturuldu. Oluşan kaplama tabakalarının mikroyapı görüntüleri ve mikrosertlik değerleri incelendi. Kaplama derinlik parametrelerine bağlı olarak, dendritik yapıların oluştuğu izlendi. Ayrıca kaplama alt tabaka arayüzeyine yakın bölgelerde birincil MxCy karbürleri ve Ti ağırlıklı ikincil fazların oluştuğu tespit edildi. Kaplama tabakalarının mikrosertlik değerleri bakıldığında 660 Hv'ye kadar çıktığı gözlendi. Bu artış toz miktarının artışıyla paraleldir. Kaplama numunelerinin aşınma performansına bakıldığında ise; ençok toz miktarına sahip kaplama numunesinin en iyi aşınma direncini gösterdiği izlendi.
Keywords
Details
| Primary Language | Turkish |
|---|---|
| Journal Section | Electrical Machines |
| Authors | |
| Publication Date | May 1, 2007 |
| Published in Issue | Year 2007 Volume: 2 Issue: 4 |