In this study, Creep behaviour of Inconel 718 superalloy, which is widely used at aviation, has been investigated at different temperatures and stresses to understand the effect of different temperature and stresses. The experiments were performed at 750°C, 800°C temperatures, and stress range of 200-350MPa. The stress exponent (n), creep rate (έ), and activation enegy(Q) were calculated from experimental results. According to the calculated results; creep rates which increase with the increasing of the stress, in addtion to; creep rates which increase much more with the increasing of temperature. Likewise, activation energy which increases with the increasing of stress. Active deformation mechanism is dislocation creep, which was determined concerning stress exponent obtaining from experiment results. In order to estimate of the creep rupture life of Inconel 718, Larson-Miller graphic was plotted. High temperature creep lifes of Inconel 718 might be calculated with this graphic.
Bu çalışmada, havacılıkta yaygın olarak kullanılan Inconel 718 süper alaşımının sürünme davranışına sıcaklık ve gerilmenin etkileri incelenmiştir. Deneyler; 750°C, 800°C sıcaklıklarında ve 200 350MPa gerilme aralığında gerçekleştirilmiştir. Deneysel çalışma sonuçlarından, gerilme üssü (n), sürünme hızı (έ) ve aktivasyon enerjisi (Q) hesaplanmıştır. Hesaplanan sonuçlara göre; sürünme hızlarının artan gerilme ile arttığı, ayrıca sıcaklığın artmasıyla birlikte sürünme hızları çok daha fazla artmaktadır. Aynı şekilde, artan gerilme ile birlikte aktivasyon enerjisi artmaktadır. Deney sonuçlarından elde edilen gerilme üssü değerlerine göre; etkin deformasyon mekanizmasının dislokasyon sürünmesi olduğu tespit edilmiştir. Inconel 718 süper alaşımının kopma sürünme ömrünü tahmin etmek için, Larson Miller grafiği çizilmiştir. Bu grafikle, Inconel 718’in yüksek sıcaklık sürünme ömürleri hesaplanabilir.