EXTRACTION OF NICKEL FROM A MIXED NICKEL-COBALT HYDROXIDE PRECIPITATE

Yıl 2019, Cilt: 58 Sayı: 1, 45 - 52, 01.03.2019

Sait Kurşunoglu

https://doi.org/10.30797/madencilik.537644

Cited By: 3

Öz

The extraction of nickel from a mixed nickel-cobalt hydroxide precipitate (MHP) was conceived

and experimentally explored. The effect of sulphuric acid concentration, leaching time, leaching

temperature and stirring speed on nickel extraction was investigated. After 60 min leaching time,

more than 90% of nickel and approximately 80% of cobalt were taken into the leach solution

under the following conditions: 0.75M sulphuric acid concentration, 30°C leaching temperature

and 400 rpm stirring speed. pH of the leach slurry was determined as 1.23 under the conditions

explored. It was observed that there is no beneficial effect of leaching temperature and stirring

speed on the extraction of nickel from the MHP sample. The XRD pattern of the fresh MHP

sample revealed the data and peak of the sample widening which is indicative of amorphous

solid structure.

Anahtar Kelimeler

Nickelextraction, Mixed nickelcobalt hydroxide precipitate, Sulphuricacid, Amorphous solid structure

Kaynakça

• Brock, G., Mccarthy, F., 2014. Direct Nickel Test Plant Progr: 2013 in review. In: ALTA Nickel-Cobalt-Copper Conference, Perth, Western Australia.
• Donegan, S., 2006. Direct Solvent Extraction of Nickel at Bulong operations. Miner. Eng., 19, 1234–1245.
• Dreisinger, D., Clucas, J. In: Battle, T., et al. (Eds.), 2013. The Starved Acid Leaching Technology (Salt) for Recovery of Nickel and Cobalt from Saprolites and Caron Plant Residues. John Wiley & Sons, Inc., Hoboken, NJ, USA.
• Harris, G.B., Magee, T.J., Lakshmanan, V.I., Sridhar, R. 2004. The Jaguar Nickel Inc. Sechol Laterite Project Atmospheric Chloride Leach Process. In: Imrie, W.P., et al. (Eds.), International Laterite Nickel Symposium. TMS, Warrendale, 219–241.
• Harvey, R., Hannah, R., Vaughan, J., 2011. Selective Precipitation of Mixed Nickel-Cobalt Hydroxide. Hydrometallurgy, 105, 222–228.
• Kyle, J., 2010. Nickel Laterite Processing Technologies- Where to Next? Alta Nickel/Cobalt/ Copper Conference, 24-27 May, Perth, Western Australia.
• Manson, P.G., Groutsch, J.V., Mayze, R.S., White, D., 1997. Process Development & Plant Design for the Cawse Nickel Project. Alta Nickel/Cobalt Forum, 1-14.
• Mason, P., Hawker, M., 1998. Ramu Nickel Process Piloting. Proceeding of ALTA Nickel Cobalt Pressure Leaching and Hydrometallurgy Forum. ALTA Metallurgical Services, 1-38.
• Mcdonald, R.G., Whittington, B.I., 2008 Atmospheric Acid Leaching of Nickel Laterites Review Part I. Sulphuric Acid Technologies. Hydrometallurgy, 91, 35–55.
• Mihaylov, I., Krause, E., Colton, D.F., Okita, Y., Duterque, J.P., Perraud, J.J., 2000. The Development of a Novel Hydrometallurgical Process for Nickel and Cobalt Recovery from Goro Laterite Ore. Metall. Soc. CIM, 93, 124–130.
• Motteram, G., Ryan, M., Berezowsky, R., Raudsepp, R., 1996. Murrin Nickel/Cobalt Project Development Overview. Alta Nickel/Cobalt Forum, 1-17.
• Nofal, P., Allen, S., Hosking, P., Showell, T., 2001. Gypsum Control at Bulong: the final hurdle?. Proceedings of ALTA Nickel Cobalt Conference. ALTA Metallurgical Services, 1-15.
• O’Callghan, J., 2003. Process Improvements at Bulong Operations. Pty Ltd. Alta Nickel/Cobalt Forum, 1-23.
• Rajamathi, M., Gonur, N., Subbannab, N., Kamatha, P. V., 1997. J. Mater. Chem., 7, 2293–2296.
• Tang, J.A., Valix, M., 2006. Leaching of Low Grade Limonite and Nontronite Ores by Fungi Metabolic Acids. Miner. Eng., 19, 1274–1279.
• Taylor, A., 1995. Laterites-Has the Time Finally Come? Min. Mag., 172 (3), 167-170.
• Valix, M., Usai, F., Malik, R., 2001. Fungal Bio-Leaching of Low Grade Laterite Ores. Miner. Eng., 14 (2), 197-203.
• Verbaan, N., Sist, F., Mackie, S., Todd, I., 2007. Development and Plotting of Skye Resources’ Atmospheric Leach (SAL) Process at SGS Minerals. Alta Nickel/ Cobalt Conference, Perth. Alta Metallurgical Services, Melbourne.