TY  - JOUR
T1  - The Effect Of Laying Direction On the Characteristics of Nonwoven Fabrics
TT  - Dokusuz Kumaşların Özelliklerine Serim Yönünün Etkisi
AU  - Gürkan Ünal, Pelin
PY  - 2018
DA  - December
JF  - European Journal of Engineering and Applied Sciences
JO  - EJEAS
PB  - Tekirdağ Namık Kemal Üniversitesi
WT  - DergiPark
SN  - 2651-3412
SP  - 59
EP  - 62
VL  - 1
IS  - 2
LA  - en
AB  - In this study, the effect of laying directions (cross or cross/parallel) on the mechanical and permeability properties of nonwoven fabrics produced with polyester/viscose blends was investigated. For this purpose, nonwoven fabrics made of 70% viscose/30% polyester were produced with card line and these webs were overlaid in cross-wise or cross/parallel directions to obtain the final fabric. Then, mechanical properties such as breaking strength and elongation, air permeability properties, water absorption percentages were measured in order to determine the effect of laying direction on the properties of the fabrics. Increasing the parallel web ratio in the cross direction decreased the breaking strength values, on the contrary, increasing the parallel webs ratio in the machine direction increased the breaking strength values of the final product based on the fibre orientation.
KW  - Nonwoven
KW  - Parallel
KW  - Cross
KW  - Mechanical
KW  - Permeability
KW  - Spunlace
N2  - Bu çalışmada, polyester/viskon karışımlı üretilendokusuz kumaşların mekanik ve geçirgenlik özelliklerine serme yönlerinin(çapraz veya çapraz/paralel) etkisi araştırılmıştır. Bu amaçla, % 70 viskon /%30 polyester karışımı içeren dokusuz kumaşlar tarak hattı kullanılaraküretilmiş ve bu tülbentler nihai kumaşı elde etmek için çapraz veyaçapraz/paralel yönlerde serilmiştir. Daha sonra, kumaşın özelliklerine sermeyönünün etkisini belirlemek için kopma mukavemeti ve uzama, hava geçirgenliközellikleri, su emme yüzdeleri gibi mekanik özellikler ölçülmüştür. Enine yöndeparalel serimli tülbent oranının arttırılması, kopma mukavemeti değerleriniazaltmış, aksine, makine doğrultusundaki paralel serimli tülbent oranınınarttırılması, elyaf oryantasyonuna dayanan nihai ürünün kopma mukavemetdeğerlerini arttırmıştır.
CR  - Russell, S.J. (2007). Handbook of Nonwovens. CRC Press.
CR  - Midha, V.K., & Mukhopadyay A. (2005). Bulk and physical properties of needle-punched nonwoven fabrics. Indian Journal of Fibre & Textile Research, 30, 218-229.
CR  - Maity S., & Singha K. (2012). Structure-Property Relationships of Needle-Punched Nonwoven Fabric, Frontiers in Science, 2(6), 226-234.
CR  - Sakthivel S., Ezhil Anban J.J., Ramachandran T. (2014). Development of needle-punched nonwoven fabrics from reclaimed fibers for air filtration applications. Journal of Engineered Fibers and Fabrics, 9, 149-154.
CR  - Ray S.C., & Ghosh, P. (2017). Studies on nature of anisotrophy of tensile properties and fibre orientation in cross-laid needle-punched nonwoven fabrics. Indian Journal of Fibre & Textile Research, 42, 160-167.
CR  - Ahmad F., Tausif M., Hassan M. Z., Ahmad S., Malik M. H. (2018). Mechanical and comfort properties of hydroentangled nonwovens from comber noil. Journal of Industrial Textiles, 47 (8). 2014-2028.
CR  - Gürkan Ünal P. (2018). The Effect of Laying Direction on the Mechanical and Comfort Properties of Cross and Cross/Parallel Laid Nonwoven Fabrics, In I. Uluslararası Bilimsel Çalışmalarda Yenilikçi Yaklaşımlar Sempozyumu.
UR  - https://dergipark.org.tr/tr/pub/ejeas/issue//469209
L1  - https://dergipark.org.tr/tr/download/article-file/599683
ER  -