Production of Ti-Al-B Based Composites by Reduction Combustion Synthesis Technique

Yıl 2014, Cilt: 14 Sayı: 3, 489 - 492, 01.12.2014

Öz

In this study, Ti-Al-B composites were carried out in an electrical resistance furnace in open air under the uniaxial pressure of 150 MPa at 1200°C for 4 hours, using by the reduction combustion synthesis technique. Initial powder mixture used in this study is Al+TiO2+B2O3. The X-ray diffraction analysis shown that the produced samples consist of TiB2 and Al2O3 phases. Densities of the samples were measured by using the Archimedes’ technique with a 0.0001gr sensitive balance. The relative density and micro-hardness were determined as 94.2% and 1832±496HV0.1 for the composites, respectively. © Afyon Kocatepe Üniversitesi

Kaynakça

  • Deqing W., 2009. Effects of additives on combustion synthesis of Al2O3-TiB2 ceramic composite. Journal of the European Ceramic Society. 1485-1492.
  • Garip Y., 2010. İndirgen Yanma Sentezi Yöntemi ile Ti-Al- B Esaslı Kompozit Üretimi. Yüksek Lisans Tezi, Sakarya Üniversitesi, Fen Bilimleri Enstitüsü, 148.
  • Hunt M., 2009. Pressureless Densification of SHS Produced Alumina-Titanium Diboride Ceramic Matrix Composites. Master of Science, Virginia State University
  • Sharifi M., Karımzadeh E., Enayati F., 2010. Synthesis of titanium diboride reinforced alumina matrix nanocomposite by mechanochemical reaction of Al- TiO2-B2O3’. Journal of Alloys and Compounds.
  • Sundaram V., Logan K. V., Speyer R. F., 1997. Aluminothermic reaction path in the synthesis of a TiB2-Al2O3 composite. Journal of Materials Research, 1681-1684.
  • Varma A., Mukasyan A. S., 1998. Combustion Synthesis of Advanced Materials. Powder Metal Technologies and Application, Vol. 7, ASM Handbook. 523-540.
  • Yeh C. L., Li R. F., 2009. Formation of TiB2-Al and NbB2-Al2O3 composite by combustion synthesis involving thermite reactions. Chemical Engineering Journal. 405-411.
  • Zhu H., Wang H., Ge L., Chen S., Wu S., 2007. Formation of composites fabricated by exothermic dispersion reaction in Al-TiO2-B2O3 system. Transactions of Nonferrous Metals Society of China. 590-594.

İndirgen Yanma Sentezi Yöntemi ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492)

Yıl 2014, Cilt: 14 Sayı: 3, 489 - 492, 01.12.2014

Öz

Bu çalışmada, indirgen yanma sentezi yöntemi ile Ti-Al-B kompozit malzeme üretimi gerçekleştirilmiştir. Proses girdi maddesi olarak TiO2, B2O3 ve Al tozu kullanılmış olup alümina-termik indirgen yöntemi ile açık atmosferli fırında 150 MPa basınç altında, 1200°C’ de 4 saat süreyle tutulmak suretiyle kompozit üretimi gerçekleştirilmiştir. Numunelerin mikroyapı ve faz analizleri taramalı elektron mikroskobu (SEMEDS) ve x-ışınları difraksiyon (XRD) analizi yardımıyla yapılmıştır. Belirlenen şartlar altında üretilen numunelerin XRD paternlerinden dönüşümün tamamlandığı ve Al2O3-TiB2 fazlarının elde edildiği görülmüştür. Archimed prensibine göre 0,0001 gr hassasiyetle yapılan yoğunluk ölçümlerinde, üretilen malzemenin nispi yoğunluğunun %94.2, mikrosertlik cihazında Vickers sertlik ucu kullanılarak belirlenen sertlik değerinin 1832.25±496 HV0.05 olduğu tespit edilmiştir

Kaynakça

  • Deqing W., 2009. Effects of additives on combustion synthesis of Al2O3-TiB2 ceramic composite. Journal of the European Ceramic Society. 1485-1492.
  • Garip Y., 2010. İndirgen Yanma Sentezi Yöntemi ile Ti-Al- B Esaslı Kompozit Üretimi. Yüksek Lisans Tezi, Sakarya Üniversitesi, Fen Bilimleri Enstitüsü, 148.
  • Hunt M., 2009. Pressureless Densification of SHS Produced Alumina-Titanium Diboride Ceramic Matrix Composites. Master of Science, Virginia State University
  • Sharifi M., Karımzadeh E., Enayati F., 2010. Synthesis of titanium diboride reinforced alumina matrix nanocomposite by mechanochemical reaction of Al- TiO2-B2O3’. Journal of Alloys and Compounds.
  • Sundaram V., Logan K. V., Speyer R. F., 1997. Aluminothermic reaction path in the synthesis of a TiB2-Al2O3 composite. Journal of Materials Research, 1681-1684.
  • Varma A., Mukasyan A. S., 1998. Combustion Synthesis of Advanced Materials. Powder Metal Technologies and Application, Vol. 7, ASM Handbook. 523-540.
  • Yeh C. L., Li R. F., 2009. Formation of TiB2-Al and NbB2-Al2O3 composite by combustion synthesis involving thermite reactions. Chemical Engineering Journal. 405-411.
  • Zhu H., Wang H., Ge L., Chen S., Wu S., 2007. Formation of composites fabricated by exothermic dispersion reaction in Al-TiO2-B2O3 system. Transactions of Nonferrous Metals Society of China. 590-594.
Toplam 8 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Makaleler
Yazarlar

Nuri Ergin Bu kişi benim

Yiğit Garip Bu kişi benim

Özkan Özdemir Bu kişi benim

Yayımlanma Tarihi 1 Aralık 2014
Gönderilme Tarihi 8 Ağustos 2015
Yayımlandığı Sayı Yıl 2014 Cilt: 14 Sayı: 3

Kaynak Göster

APA Ergin, N., Garip, Y., & Özdemir, Ö. (2014). İndirgen Yanma Sentezi Yöntemi ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, 14(3), 489-492.
AMA Ergin N, Garip Y, Özdemir Ö. İndirgen Yanma Sentezi Yöntemi ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. Aralık 2014;14(3):489-492.
Chicago Ergin, Nuri, Yiğit Garip, ve Özkan Özdemir. “İndirgen Yanma Sentezi Yöntemi Ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492)”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 14, sy. 3 (Aralık 2014): 489-92.
EndNote Ergin N, Garip Y, Özdemir Ö (01 Aralık 2014) İndirgen Yanma Sentezi Yöntemi ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 14 3 489–492.
IEEE N. Ergin, Y. Garip, ve Ö. Özdemir, “İndirgen Yanma Sentezi Yöntemi ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492)”, Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, c. 14, sy. 3, ss. 489–492, 2014.
ISNAD Ergin, Nuri vd. “İndirgen Yanma Sentezi Yöntemi Ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492)”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 14/3 (Aralık 2014), 489-492.
JAMA Ergin N, Garip Y, Özdemir Ö. İndirgen Yanma Sentezi Yöntemi ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. 2014;14:489–492.
MLA Ergin, Nuri vd. “İndirgen Yanma Sentezi Yöntemi Ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492)”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, c. 14, sy. 3, 2014, ss. 489-92.
Vancouver Ergin N, Garip Y, Özdemir Ö. İndirgen Yanma Sentezi Yöntemi ile Ti-Al-B Esaslı Kompozit Üretimi (025777) (498-492). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. 2014;14(3):489-92.


Bu eser Creative Commons Atıf-GayriTicari 4.0 Uluslararası Lisansı ile lisanslanmıştır.