The Effect of Various Alumina Based Agregates on Physical and Mechanical Properties of High Alumina Castable Refractory

Yıl 2014, Cilt: 14 Sayı: 2, 1 - 8, 01.08.2014

Öz

In this study, it was investigated effect of tabular alümina (TA), white fused alümina (WFA) and mixtures (%50 TA+ % 50 WFA) of them as agrega on physical and mechanical properties of high alumina castable refractory which especially use in steel ladle industries. For this aim, particle size fraction and amount of refractory constituent were determined depend on q values in Andreasan’s model to be 0.30 and experimental samples from these mixtures were prepared by sintering at 1530 oC for 8 hours. Prepared samples from these compositions as green and sintered were subjected to physical and mechanical tests. Characterization results are analyzed, the castables with tabular alumina has lower porosity and water adsorption and also higher bulk density and cold compressive strength than those of white fused alumina and mixtures of them. © Afyon Kocatepe Üniversitesi

Kaynakça

  • Sahu, K.M., 2009. Study of erosion resistance of ulcc based precast with indigenous high alumina cement. Rourkela Department of Ceramic Engineering, Master of Technology Thesis, 2-8. of Technology,
  • Schacht, C. A., 2004. Refractories handbook. Schacht Consulting Services, Pittsburgh, Pennsylvania, U.S.A., 259-287.
  • Martinovic, S., Majstrovic, J., Vidojkovic, V. and Husovic, V.T., 2009. Preparation and properties of low cement castable sintered at different temperatures. Processing and Application of Ceramics, 4: 191–196.
  • Liu, X., Yanqing, X., Keming, G., Buhr, A. and Büchel, G., 2007. Tabular alumina for high purity corundum brick. Almatis Technical Papers.
  • Rout, R.R., 2009. Studies on the effect of alumina aggregates on he performances of alumina-carbon refractories. National Institute of Technology Rourkela, MTech Thesis, 4.
  • Andreev, K., Sinnema, S. and Hogenboom, M., 2009. Investigation of refractory concrete failure in furnaces of metals industry. Ceramics Research Centre, Corus RD&T, The Netherlands, 1-8.
  • Braulio, M.A.L., Bittencourt, L.R.M. and Pandolfelli, V.C., 2009. Selection of binders for in situ spinel refractory castables. Journal of the European Ceramic Society, 29: 2727–2735.
  • Abou-Sekkina, M.M., Abo-El-Enein, S.A., Khalil, N.M. and Shalma, O.A., 2011. Phase composition of bauxite-based International, 37: 411–418. castables. Ceramics
  • Myhre, B., 1994. Strength development of bauxite- based ultralow- cement castables, Am. Ceram. Soc. Bull. Vol.73, 5: 68–73.
  • Başpınar, M. S., 2005. Mullit refrakterlerde bağlayıcı fazın optimizasyonu. Anadolu Üniversitesi Fen Bilimleri Enstitüsü Doktora Tezi, 24-42.
  • Gogtas, C., 2012. Development of nano-ZrO2 reinforced self- flowing low and ultra low cement refractory castables. The University of Wisconsin-Milwaukee, Ph.D. Thesis, 18-38.
  • Liu, X., Yanqing, X., Keming, G., Buhr, A. and Büchel, G., 2007. Tabular alumina for high purity corundum brick. Almatis Technical Papers.

Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel ve Mekaniksel Özelliklerine Etkileri (025701) (1-8)

Yıl 2014, Cilt: 14 Sayı: 2, 1 - 8, 01.08.2014

Öz

Bu çalışmada, tabular alümina (TA), beyaz ergimiş alümina (WFA) ve her ikisinin karışımı (%50 TA+ % 50 WFA) taşıyıcı tanelerin özellikle çelik pota endüstrisinde yaygın olarak kullanılan yüksek alüminalı dökülebilir refrakterlerin fiziksel ve mekaniksel özelliklerine etkileri araştırılmıştır. Bu kapsamda, yüksek alümina içerikli bu taşıyıcı tanelerin ve dökülebilir refrakter bileşimindeki diğer bileşenlerin tane boyut ve % miktarları Andreasen tane paketlenme modülüne göre n değeri 0,30’u sağlayacak şekilde ayarlanarak hazırlanan numuneler 1530 oC’de hava ortamında 8 saat sinterlenmiş ve düşük çimentolu yüksek alüminalı dökülebilir refrakter numuneler üretilmiştir. Üretilen bu numuneler üzerinde taşıyıcı tanelerin fiziksel ve mekaniksel özelliklere olan etkileri standartlar dahilinde yapılan testler sonucunda belirlenmiştir. Karakterizasyon sonuçları incelendiğinde tabular alümina taşıyıcı tane içeren dökülebilir refrakterin beyaz ergimiş alümina ve her iki taşıyıcı tanenin eşit oranda karışımını içeren dökülebilir refrakter örnekleri ile özellikleri karşılaştırıldığında ham ve sinterlenmiş halde en düşük açık gözeneklilik ve su emme ile en yüksek birim hacim ağırlık ve soğukta basma mukavemeti değerlerine sahip olduğu görülmüştür

Kaynakça

  • Sahu, K.M., 2009. Study of erosion resistance of ulcc based precast with indigenous high alumina cement. Rourkela Department of Ceramic Engineering, Master of Technology Thesis, 2-8. of Technology,
  • Schacht, C. A., 2004. Refractories handbook. Schacht Consulting Services, Pittsburgh, Pennsylvania, U.S.A., 259-287.
  • Martinovic, S., Majstrovic, J., Vidojkovic, V. and Husovic, V.T., 2009. Preparation and properties of low cement castable sintered at different temperatures. Processing and Application of Ceramics, 4: 191–196.
  • Liu, X., Yanqing, X., Keming, G., Buhr, A. and Büchel, G., 2007. Tabular alumina for high purity corundum brick. Almatis Technical Papers.
  • Rout, R.R., 2009. Studies on the effect of alumina aggregates on he performances of alumina-carbon refractories. National Institute of Technology Rourkela, MTech Thesis, 4.
  • Andreev, K., Sinnema, S. and Hogenboom, M., 2009. Investigation of refractory concrete failure in furnaces of metals industry. Ceramics Research Centre, Corus RD&T, The Netherlands, 1-8.
  • Braulio, M.A.L., Bittencourt, L.R.M. and Pandolfelli, V.C., 2009. Selection of binders for in situ spinel refractory castables. Journal of the European Ceramic Society, 29: 2727–2735.
  • Abou-Sekkina, M.M., Abo-El-Enein, S.A., Khalil, N.M. and Shalma, O.A., 2011. Phase composition of bauxite-based International, 37: 411–418. castables. Ceramics
  • Myhre, B., 1994. Strength development of bauxite- based ultralow- cement castables, Am. Ceram. Soc. Bull. Vol.73, 5: 68–73.
  • Başpınar, M. S., 2005. Mullit refrakterlerde bağlayıcı fazın optimizasyonu. Anadolu Üniversitesi Fen Bilimleri Enstitüsü Doktora Tezi, 24-42.
  • Gogtas, C., 2012. Development of nano-ZrO2 reinforced self- flowing low and ultra low cement refractory castables. The University of Wisconsin-Milwaukee, Ph.D. Thesis, 18-38.
  • Liu, X., Yanqing, X., Keming, G., Buhr, A. and Büchel, G., 2007. Tabular alumina for high purity corundum brick. Almatis Technical Papers.
Toplam 12 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Makaleler
Yazarlar

Çetin Öztürk Bu kişi benim

Serhat Başpınar Bu kişi benim

Ziya Aslanoğlu Bu kişi benim

Çetin Bağlan Bu kişi benim

Yayımlanma Tarihi 1 Ağustos 2014
Gönderilme Tarihi 8 Ağustos 2015
Yayımlandığı Sayı Yıl 2014 Cilt: 14 Sayı: 2

Kaynak Göster

APA Öztürk, Ç., Başpınar, S., Aslanoğlu, Z., Bağlan, Ç. (2014). Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel ve Mekaniksel Özelliklerine Etkileri (025701) (1-8). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, 14(2), 1-8.
AMA Öztürk Ç, Başpınar S, Aslanoğlu Z, Bağlan Ç. Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel ve Mekaniksel Özelliklerine Etkileri (025701) (1-8). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. Ağustos 2014;14(2):1-8.
Chicago Öztürk, Çetin, Serhat Başpınar, Ziya Aslanoğlu, ve Çetin Bağlan. “Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel Ve Mekaniksel Özelliklerine Etkileri (025701) (1-8)”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 14, sy. 2 (Ağustos 2014): 1-8.
EndNote Öztürk Ç, Başpınar S, Aslanoğlu Z, Bağlan Ç (01 Ağustos 2014) Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel ve Mekaniksel Özelliklerine Etkileri (025701) (1-8). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 14 2 1–8.
IEEE Ç. Öztürk, S. Başpınar, Z. Aslanoğlu, ve Ç. Bağlan, “Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel ve Mekaniksel Özelliklerine Etkileri (025701) (1-8)”, Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, c. 14, sy. 2, ss. 1–8, 2014.
ISNAD Öztürk, Çetin vd. “Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel Ve Mekaniksel Özelliklerine Etkileri (025701) (1-8)”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 14/2 (Ağustos 2014), 1-8.
JAMA Öztürk Ç, Başpınar S, Aslanoğlu Z, Bağlan Ç. Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel ve Mekaniksel Özelliklerine Etkileri (025701) (1-8). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. 2014;14:1–8.
MLA Öztürk, Çetin vd. “Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel Ve Mekaniksel Özelliklerine Etkileri (025701) (1-8)”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, c. 14, sy. 2, 2014, ss. 1-8.
Vancouver Öztürk Ç, Başpınar S, Aslanoğlu Z, Bağlan Ç. Farklı Alümina Esaslı Taşıyıcı Tane Agregalarının Yüksek Alüminalı Dökülebilir Refrakterlerin Fiziksel ve Mekaniksel Özelliklerine Etkileri (025701) (1-8). Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. 2014;14(2):1-8.


Bu eser Creative Commons Atıf-GayriTicari 4.0 Uluslararası Lisansı ile lisanslanmıştır.