Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi

Habip Kırgezen; Tarık Gün; Fatih Kılıç

The Effect of Manganese Phosphate Coating Corrosion Behaviour at AISI 4140 Steel and Grey Cast Irons Used in Camshaft Production

Yıl 2015, Cilt: 15 Sayı: 1, 1 - 7, 08.08.2015

Öz

Nowadays, coverings plays an important role to the selection of material. Covering modified is provides important advantages which is temperature, corrosion, oxidation and erosion in applications. In this study were investigated which used in the production of camshafts steel of AISI 4140 and gray cast iron covered with manganese phosphate effect on the corrosion behavior. In experiments steel of AISI 4140 and gray cast iron manganese phosphate covered samples of each half and other samples were not covered. Corrosion test was performed which as corrosive environments with the solution prepared by at 25oC and at 70oC, 0,5 M HCl and 0,5 M H2SO4. Test samples the solutions prepared were subjected to corrosion in 180 minutes and material weight losses are calculated. As a result of studies at high temperatures H2SO4 weight loss was greater in corrosive environments and manganese phosphate covering was shown to improve the corrosion resistance. © Afyon Kocatepe Üniversitesi

Anahtar Kelimeler

-

Kaynakça

Narayanan, S. Surface pretreatment by phosphate conversıon
Hivart, P., Hauw, B., Bricout, J. P., Oudin J., 1997. Seizure behaviour of manganese phosphate coatings according to the process conditions. Tribology International Vol. 30, No. 8, pp. 561–570, (1997.) Hivart, et al., 2003. Numerical identification of bulk behavior law of manganese phosphate coatings. Comparison with tribological properties, J. Coat. Technol. 75 (942) 37–44. (2003)
Oyamada, T., Inoue, Y., 2003. Evaluation of the

Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi

Yıl 2015, Cilt: 15 Sayı: 1, 1 - 7, 08.08.2015

Habip Kırgezen Tarık Gün Fatih Kılıç

Öz

Günümüzde, malzeme seçiminde kaplamalar önemli bir rol oynamaktadır. Sıcaklık, korozyon, oksidasyon ve aşınmanın olduğu uygulamalarda kaplama yapılması önemli avantajlar sağlamaktadır. Bu çalışmada kam mili üretiminde kullanılan AISI 4140 çeliği ve gri dökme demirin mangan fosfat ile kaplanarak korozyon davranışı üzerine etkisi araştırılmıştır. Deneylerde AISI 4140 çeliği ve gri dökme demir numunelerinin her birinin yarısı mangan fosfat kaplanmış diğer numuneler kaplanmamıştır. Korozif ortam olarak 25oC’de ve 70oC’de 0,5 M HCl ve 0,5 M H2SO4 ile hazırlanmış solüsyonlarla korozyon testi yapılmıştır. Deney numuneleri 180 dakika hazırlanan solüsyonlarda korozyona uğratılmıştır ve malzeme ağırlık kayıpları hesaplanmıştır. Yapılan çalışma sonucunda yüksek sıcaklıklarda H2SO4 korozif ortamında ağırlık kayıpları daha fazla olmuştur ve mangan fosfat kaplamanın korozyon direncini arttırdığı görülmüştür

Anahtar Kelimeler

Korozyon, Mangan Fosfat Kaplama, AISI 4140 Çeliği, Gri Dökme Demir

Kaynakça

Narayanan, S. Surface pretreatment by phosphate conversıon
Hivart, P., Hauw, B., Bricout, J. P., Oudin J., 1997. Seizure behaviour of manganese phosphate coatings according to the process conditions. Tribology International Vol. 30, No. 8, pp. 561–570, (1997.) Hivart, et al., 2003. Numerical identification of bulk behavior law of manganese phosphate coatings. Comparison with tribological properties, J. Coat. Technol. 75 (942) 37–44. (2003)
Oyamada, T., Inoue, Y., 2003. Evaluation of the

Toplam 3 adet kaynakça vardır.

Ayrıntılar

Birincil Dil	Türkçe
Bölüm	Makaleler
Yazarlar	Habip Kırgezen Bu kişi benim Tarık Gün Bu kişi benim Fatih Kılıç Bu kişi benim
Yayımlanma Tarihi	8 Ağustos 2015
Gönderilme Tarihi	8 Ağustos 2015
Yayımlandığı Sayı	Yıl 2015 Cilt: 15 Sayı: 1

Kaynak Göster

APA	Kırgezen, H., Gün, T., & Kılıç, F. (2015). Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, 15(1), 1-7.
AMA	Kırgezen H, Gün T, Kılıç F. Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. Nisan 2015;15(1):1-7.
Chicago	Kırgezen, Habip, Tarık Gün, ve Fatih Kılıç. “Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği Ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 15, sy. 1 (Nisan 2015): 1-7.
EndNote	Kırgezen H, Gün T, Kılıç F (01 Nisan 2015) Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 15 1 1–7.
IEEE	H. Kırgezen, T. Gün, ve F. Kılıç, “Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi”, Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, c. 15, sy. 1, ss. 1–7, 2015.
ISNAD	Kırgezen, Habip vd. “Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği Ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi 15/1 (Nisan 2015), 1-7.
JAMA	Kırgezen H, Gün T, Kılıç F. Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. 2015;15:1–7.
MLA	Kırgezen, Habip vd. “Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği Ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi”. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi, c. 15, sy. 1, 2015, ss. 1-7.
Vancouver	Kırgezen H, Gün T, Kılıç F. Kam Mili Üretiminde Kullanılan AISI 4140 Çeliği ve Gri Dökme Demirlerde Mangan Fosfat Kaplanmanın Korozyon Davranışına Etkisi. Afyon Kocatepe Üniversitesi Fen Ve Mühendislik Bilimleri Dergisi. 2015;15(1):1-7.