Effects of Speed Sintering on Multilayered Monolithic Zirconia

Yıl 2019, Cilt: 22 Sayı: 1, 31 - 36, 13.03.2019

Mehmet Coskun Fatih Sarı

https://doi.org/10.7126/cumudj.510393

Cited By: 1

Öz

Objective:In dentistry, different products are being developed in order to shorten the chairside but the interactions between these materials needs further investigations. This study aims to investigate the two different short time sintering protocols on monolithic multilayered zirconia’s surface roughness (SR), translucency parameter (TP), and contrast ratio (CR).  

Material and Methods:Twenty monolithic multilayer zirconia specimens were prepared with the dimension 10x10x1 mm and divided into two sintering groups (speed sintering group 30 min at 1510 ⁰C, high speed sintering group 10 min 1580 ⁰C) and SEM analyzed were performed. Surface roughness tests were performed by using profilometer and optical measurements were performed by using spectrophotometer. The data was statistically analyzed by using Wilcoxen test at the 0.05 probability level.

Results:SR values and CR did not show any significant difference at any layer of any group. In all parts of monolithic multilayered zirconia, the difference of TP between sintering groups were statistically significant (P<.05). 

Conclusion: High speed sintering parameters has promising effects on monolithic multilayered zirconia with combined acceptable optical properties. Because of their different content, different layers show different reactions in terms of contrast ratio and translucency parameters and these changes should be taken into account in treatment planning.

Anahtar Kelimeler

sintering, contrast ratio, translucency, Zirconia

Kaynakça

• Referans1. John M. Evolution of dental ceramic in the twentieth century. J prosthet Dent 2001;85(1):61-66.
• Referans2. Rosenbulm. A review of all-ceramic restorations. JADA 1997;128(3):297-307.
• Referans3. Oh GJ, Lee K, Lee DJ, et al. Effect of metal chloride solutions on coloration and biaxial flexural strength of yttria-stabilized zirconia. Met Mater Int 2012;18(5):805-812.
• Referans4. Heintze SD, Rousson V. Survival of zirconia- and metal-supported fixed dental prostheses: a systematic review. Int J Prosthodont 2010;23(6):493-502.
• Referans5. Sailer I, Fehér A, Filser F, Gauckler LJ, Lüthy H, Hämmerle CHF. Five-year clinical results of zirconia frameworks for posterior fixed partial dentures. Int J Prosthodont 2007;20(4):383-388.
• Referans6. Stawarczyk B, Mutlu Ö, Hallmann L, Ender A, Mehl A, Hammerlet CHF. The effect of zirconia sintering temperature on flexural strength, grain size, and contrast ratio. Clin Oral Investig 2013;17(1):269-274.
• Referans7. Sulaiman T A, Abdulmajeed A A, Donovan T A, Vallittu P K, Narhi T O, Lassila L V. The effect of staining and vacuum sintering on optical and mechanical properties of partially and fully stabilized monolithic zirconia. Dent Mater J 2015;34(5):605-610.
• Referans8. Denry I, Kelly JR. Emerging ceramic-based materials for dentistry. J Dent Res 2014;93(12):1235-1242.
• Referans9. Ebeid K, Wille S, Hamdy A, Salah T, El-Etreby A, Kern M. Effect of changes in sintering parameters on monolithic translucent zirconia. Dent Mater 2014;30(12):419-424.
• Referans10. Sulaiman TA, Abdulmajeed AA, Donovan TE, et al. Optical properties and light irradiance of monolithic zirconia at variable thicknesses. Dent Mater 2015;31(10):1180-1187.
• Referans11. Jiang L, Liao Y, Wan Q, Li W. Effects of sintering temperature and particle size on the translucency of zirconium dioxide dental ceramic. J Mater Sci Mater Med 2011;22(11):2429-2435.
• Referans12. Shah K, Holloway JA, Denry IL. Effect of Coloring with Various Metal Oxides on the Microstructure, Color, and Flexural Strength of 3Y-TZP. J Biomed Mater Res - Part B Appl Biomater 2008;87(2):329-337.
• Referans13. Tuncel I, Eroglu E, Sari T, Usumez A. The effect of coloring liquids on the translucency of zirconia framework. J Adv Prosthodont 2013;5(4):448.
• Referans14. Kim H, Kim S. Comparison of the optical properties of pre- colored dental monolithic zirconia ceramics sintered in a conventional furnace versus a microwave oven. J Adv Prosthodont 2017;9(5):394-401.
• Referans15. Brodbelt RHW, O’brien WJ, Fan PL. Translucency of Dental Porcelains. J Dent Res 1980;59(1):70-75.
• Referans16. Stawarczyk B, Emslander A, Roos M, Sener B, Noack F, Keul C. Zirconia ceramics, their contrast ratio and grain size depending on sintering parameters. Dent Mater J 2014;33(5):591-598.
• Referans17. Kim MJ, Ahn JS, Kim JH, Kim HY, Kim WC. Effects of the sintering conditions of dental zirconia ceramics on the grain size and translucency. J Adv Prosthodont 2013;5(2):161-166.
• Referans18. Chen IW, Wang XH. Sintering dense nanocrystalline ceramics without final-stage grain growth. Nature 2000;404(6774):168-171.
• Referans19. Wang H, Xiong F, Zhenhua L. Influence of varied surface texture of dentin porcelain on optical properties of porcelain specimens. J Prosthet Dent 2011;105(4):242-248.
• Referans20. Obregon A, Googkind RJ, Schwabacher WB. Effects of opaque and porcelain surface texture on the color of ceramometal restorations. Res Educ 1981;46(3):330-340.
• Referans21. Ersoy NM, Aydoğdu HM, Değirmenci BÜ, Çökük N, Sevimay M. The effects of sintering temperature and duration on the flexural strength and grain size of zirconia. Acta Biomater Odontol Scand 2015;1(2-4):43-50.
• Referans22. Johnston WM, Ma T, Kienle BH. Translucency parameter of colorants for maxillofacial prostheses. Int J Prosthodont 1995;8(1):79-86.
• Referans23. Vichi A, Sedda M, Fabian Fonzar R, Carrabba M, Ferrari M. Comparison of contrast ratio, translucency parameter, and flexural strength of traditional and “augmented translucency” zirconia for CEREC CAD/CAM system. J Esthet Restor Dent 2016;28:32-39.
• Referans24. Zhang Y. Making yttria-stabilized tetragonal zirconia translucent. Dent Mater 2014;30(10):1195-1203.