Effect of zinc oxide nanoparticles on the flexural strength of polymethylmethacrylate denture base resin

Year 2020, Volume: 54 Issue: 1, 31 - 35, 23.01.2020

Santhanam Vıkram N. Gopi Chander

https://doi.org/10.26650/eor.20200063

Abstract

Purpose This study evaluated the flexural strength of polymethyl methacrylate (PMMA) reinforced with various concentrations of zinc oxide (Zn O) nanoparticles Materials and Methods Nano ZnO was added in 0, 0.4, 0.6, 0.8, 1.2 and 1.4 percentage to PMMA denture base material. 60 specimens of heat cure polymerizing acrylic resin of dimensions 10mm x 4mm x 80mm were fabricated in accordance to ISO 20795-1-2013. The specimens were divided into 6 groups. Acrylic specimens were processed according to manufacturer’s instruction. Three-point bending test was performed to evaluate the flexural strength. Surface analysis was performed with scanning electron microscopy (SEM) to observe the fracture surfaces of specimens. ANOVA and Tukey tests were used for the statistical analysis (p < 0.05). Results Statistical analysis revealed significant differences in strength between groups. The flexural strength improved with the addition ZnO nanoparticles. Highest mean value was observed in Group nZn -14 (91.31 MPa) and lowest in control Group nZn-0 (61.36 MPa). ANOVA and Tukey’s honestly significance test found statistical significant differences among the groups ( p<0.001). Conclusion The addition of ZnO nanoparticles in all concentrations increased the flexural strength of acrylic resin when compared to the control group.

Keywords

Flexural strength, heat cure acrylic, nano particles, poly methyl metha acrylate, zinc oxide

Supporting Institution

The authors declared that this study has received no financial support.

References

• 1. Salman et al. The influence of adding of modified ZrO2-TiO2 nanoparticles on certain physical and mechanical properties of heat polymerized acrylic resin. J Bagh College Dentistry 2015;27:33-9. [CrossRef]
• 2. Zappini et al. Comparison of fracture tests of denture base materials. J Prosthet Dent 2003;90:578-85. [CrossRef]
• 3. McCabe JF, Walls AWG. Applied Dental Materials. John Wiley & Sons; 2013. 591.
• 4. Jasim BS, Ismail IJ. The effect of silanized alumina nano-fillers addition on some physical and mechanical properties of heat cured polymethyl methacrylate denture base material. J Bagh College of Dentistry 2014;26:18-23. [CrossRef]
• 5. Asar et al Influence of various metal oxides on mechanical and physical properties of heat-cured polymethyl methacrylate denture base resins. J Adv Prosthodont 2013;5:241-247. [CrossRef]
• 6. Aljafery AM, Hussain BM. Effect of addition ZrO2-Al2O3 nanoparticles mixture on some properties and denture base adaptation of heat cured acrylic resin denture base material. J Bagh College of Dentistry 2015;27:15-21. [CrossRef]
• 7. Ochi M, Shimaoka S. Phase structure and toughness of siliconemodified epoxy resin with added silicone graft copolymer. Polymer 1999;40:1305-12.
• 8. Vojdani M, Khaledi AA. Transverse strength of reinforced denture base resin with metal wire and E-glass fibers. JDT 2006;3:159-66.
• 9. Kassab BT, Al-Nema LM. Evaluation of some mechanical properties of reinforced acrylic resin denture base material (An In vitro study). Al-Rafidain Dent J 2009;9:57-65.
• 10. Raszewski Z, Nowakowska D. Mechanical properties of hot curing acrylic resin after reinforced with different kinds of fibers. Int J Biomedical Materials Res 2013;1:9-13. [CrossRef]
• 11. Deepan N, Prakash A, Rao B, Sonthalia A. In vitro Evaluation and comparison of transverse and impact strength of heat polymerized acrylic resin reinforced with polyethylene fibers and polypropylene fibers. J Adv Med Dent Sci 2014;2:46-56.
• 12. Jagger DC, Harrison A, Jandt KD. The reinforcement of dentures. J Oral Rehabil 1999;26:185-94. [CrossRef] 13. Sandhu JS, Kaur G. Nanodentistry: The Changing Trends in Dentistry. IntJ Nanomedicine 2011;6:2799-804.
• 14. Khaled SM, Miron RJ, Hamilton DW, Charpentier PA, Rizkalla AS. Reinforcement of resin based cement with titanium nanotubes. Dent Mater 2010;26:169-78. [CrossRef]
• 15. Gad MM, Fouda SM, Al-Harbi FA, Näpänkangas R, Raustia A. PMMA denture base material enhancement: a review of fiber, filler, and nanofiller addition. Int J Nanomedicine 2017;12:380112. [CrossRef]
• 16. Cevik P, Yildirim-Bicer AZ. The Effect of Silica and Prepolymer Nanoparticles on the Mechanical Properties of Denture Base Acrylic Resin. J Prosthodont 2018;27(8):763-70. [CrossRef]
• 17. Ladha K, Shah D. An in-vitro evaluation of the flexural strength of heat-polymerized poly (methyl methacrylate) denture resin reinforced with fibers. J Indian Prosthodont Soc 2011;11(4):21520. [CrossRef]
• 18. Rahim et al. Incorporation of silica nanoparticles to increase the mechanical properties. J Phys Sci 2011;22:32-105.
• 19. Pfeiffer P, Rolleke C, Sherif L. Flexural strength and moduli of hypoallergenic denture base materials. J Prosthet dent 2005;30;93:372-7. [CrossRef]
• 20. Maruo Y, Nishigawa G, Oka M, Minagi S, Suzuki K, Irie M. Does plasma irradiation improve shear bond strength of acrylic resin to cobalt-chromium alloy? Dent Mater 2004;30;20:509-12. [CrossRef]
• 21. Yan Z, Liqin G, Xiuli Q, Lixia G. Study on PET fiber modified by silver carrying zinc oxide nanoparticles. China Synthetic Fiber Industry 2005-04.
• 22. Ayad NM, Badawi MF, Fatah AA. Effect of reinforcement of high impact acrylic resin with zirconia on some physical and mechanical properties. Rev ClinPesqOdontol 2008;4:145-51.
• 23. Harini P, Mohamed K, Padmanabhan TV. Effect of Titanium dioxide nanoparticles on the flexural strength of polymethylmethacrylate: An in vitro study. J Dent Res 2014;25:459. [CrossRef]
• 24. Bhavikatti SK, Bhardwaj S,Prabhuji ML. Current applications of nanotechnology in dentistry: a review. Gen Dent 2014;62:72-7.
• 25. Harishanand et al, Comparitive Study on Mechanical Properties of ZnO, ZrO2 and CeO2 Nanometal Oxides Reinforced Epoxy Composites, Advances in Polymer Science and Technology: Int J 2013;3:7-13.
• 26. Alexandre M, Dubois P. Polymer-layered silicate nanocomposites: preparation, properties and uses of a new class of materials. Materials Science and Engineering: R: Reports 2000;28:1-63. [CrossRef]
• 27. Xie Y, Irwin PL, Jin T,Shi X.Antibacterial activity and mechanism of action of zinc oxide nanoparticles against Campylobacter jejuni. Appl Environ Microbiol. 2011 Apr;77:2325-31. [CrossRef]
• 28. Zhang XY, Wu WL, Bian YM, Zhu BS, Yu WQ. The effect of different dispersive methods on flexural strength nano-ZrO (2) reinforced denture polymethyl methacrylate. Shanghai Kou Qiang Yi Xue 2009;18:313-6.
• 29. Raj I, Mozetic M, Jayachandran VP, Jose J, Thomas S, Kalarikkal N. Fracture resistant, antibiofilm adherent, self-assembled PMMA/ ZnO nano formulations for biomedical applications: physicochemical and biological perspectives of nano reinforcement. Nanotechnology 2018;29(30):305704. [CrossRef]