THE EFFECT OF FIRING TEMPERATURE ON THE PROPERTIES OF GLAZES PREPARED WITH BARIUM-BASED FRITS
Abstract
Barium-based frits are widely used in the ceramic tile industry for the production of matte glazes. In these glazes, the microstructure—and consequently, the opacity and matte finish—vary depending on factors such as composition, application conditions, and firing temperatures. This study investigates the effects of different firing temperatures on the microstructure and properties of glazes prepared with barium-based frits. For this purpose, compositions containing 92 wt% barium-based frit and 8 wt% kaolin were milled, applied to the tile surface, and then fired in a laboratory furnace at four different peak temperatures (900, 1000, 1100, and 1200°C). The results indicate that the primary phase formed in the glaze structure is celsian at peak temperatures of 1100°C and 1200°C. As the temperature increases, the glassy phase expands, and crystal size increases. A decrease in the whiteness value (L*) value was observed with rising temperature; however, the glaze generally maintained its matte finish, as indicated by the 60° gloss value.
Keywords
References
- [1] Casasola R, Rincon JMa, Romero M. Glass–ceramic glazes for ceramic tiles: a review. J. Mater. Sci., 2012; 47, 553-582.
- [2] Kurama S, Gürkan, EA, Ozturk ZB, Karaca Y, Ubay E. Bazalt kesim atıklarının yer karosu mat sırlarda kullanım potansiyelinin araştırılması. ESOGÜ Müh. Mim. Fakültesi Dergisi, 2023; 31 (3), 816-825.
- [3] Ozturk ZB, Karaca Y, Ubay E. Enhancing thermal properties and surface quality of lappato glazed porcelain tiles through milling time optimization. Journal of Thermal Analysis and Calorimetry, 2024; 149, 7279-7287.
- [4] Yazırlı B, Sarı H, Kayacı K, Kara F. Effect of nucleating agent additions on gahnite based glass-ceramic glazes. J. Eur. Ceram. Soc., 2024; 44, 3344-3351.
- [5] Eppler RA, Eppler DR. Glazes and Glass Coatings. The American Ceramic Society, Ohio, 2000.
- [6] Taylor JR, Bull AC. Ceramic Glaze Technology. Oxford: Pergamon Press, 1986.
- [7] Bou E, Bordes MC, Felıu C, Gazulla MF, Ferrer F, Pasies G. Variables that determine the matt appearance of some ceramic floor and wall tile glazes. Proceeding of VII world congress on ceramic tile quality Qualicer, 2002; 349-364.
- [8] Campa F, Ginés F, Robles J. Matting of a transparent porous wall tile glaze by adding alumina. Proceeding of VI world congress on ceramic tile quality Qualicer, 2000; 115-117.
- [9] Kronberg T, Hupa L. The impact of wollastonite and dolomite on chemical durability of matte fast-fired raw glazes. J. Eur. Ceram. Soc., 2020; 40, 3327-3337.
- [10] Fortuna D. Sanitaryware. Faenza: Gruppo Editoriale; 2000.