Investigation Regarding Al-Al2O3 Composite Material Production and Its Weldability to Aluminum by Diffusion Welding

Year 2017, Volume: 4 Issue: 4, 101 - 111, 27.12.2017

Halil Arık , Ramazan Sandal

Abstract

In this study, firstly, a
composite material aluminum based and containing 10 % Al₂O₃
by weight is produced by powder metallurgy method. In the production of composite samples being 10 mm in diameter and
15 mm in length, first Al and Al₂O₃ powders were mixed
for 2 hours in a high – energy  attritor
and then pressed in a unidirectional axial die  at 800  MPa
pressure. The pressed samples were sintered in a tubular furnace in a
protective argon gas ambiance at 650°C for 2 hours. As for the second stage, the
composite samples have been welded by diffusion welding to an Al block material
in 99.5% purity and in the same dimensions at 5 MPa – constant load at
different temperatures and durations by diffusion welding. The strength values
of welded samples were determined by making shear tests from the welding zones
versus composite material.

Keywords

Powder metallurgy, Composite, Diffusion welding

References

• 1. Prof. Dr. Nizamettin KAHRAMAN (Karabük Üniversitesi, Teknoloji Fakültesi, İmalat Müh. Böl, Demir Çelik Kampüsü, 78050 KARABÜK) [e-mail], Tel: [phone] / 1328
• 2. Prof. Dr. Mustafa AYDIN (Manisa Celal Bayar Üniversitesi, Hasan Ferdi Turgutlu Teknoloji Fakültesi, İmalat ve Makina Mühendisliği Bölümü, Turgutlu/MANİSA). (0236) 314 10 10, [e-mail]
• 3. Prof. Dr. Adem KURT (Gazi Üniversitesi, Teknoloji Fakültesi, Metalurji ve Malzeme Müh. Böl. 06500, Beşevler/ANKARA), [e-mail], 3122028778.