Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing

Emre Demir; Ayşe Bedeloğlu

doi:10.61112/jiens.1787646

Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing

Öz

In this study, the effect of auxetic core structures with a negative Poisson's ratio on the mechanical performance of sandwich composites was systematically investigated using additive manufacturing (AM). Compared to conventional honeycomb structures with a positive Poisson's ratio, three different core configurations (re-entrant and improved re-entrant) were fabricated from polylactic acid (PLA) using the fused deposition modeling (FDM) technique. These core structures were then bonded with carbon fiber-reinforced epoxy surface layers to form sandwich composite panels. Tensile, three-point bending, and compression tests were conducted in accordance with ASTM standards, and Poisson ratios were determined experimentally. The results were then comparatively evaluated using finite element analyses (FEA). The results revealed that the cores with a negative Poisson's ratio significantly improved the mechanical performance of the sandwich composites. Among the tested designs, the improved re-entrant geometry achieved the highest strength values, reaching 160.83 MPa in the flexural test and 125 MPa in the compression test. These findings demonstrate that auxetic geometry design has the potential to improve the comparative mechanical performance of sandwich composites.

Anahtar Kelimeler

Kaynakça

Bitzer TN (1997) Honeycomb technology: Materials, design, manufacturing, applications and testing. Chapman & Hall, London.
Zenkert D (1995) An introduction to sandwich construction. Engineering Materials Advisory Services Ltd, London.
Gibson LJ, Ashby MF (1997) Cellular solids: Structure and properties, 2nd edn. Cambridge University Press, Cambridge.
Grenestedt JL (1998) Influence of wavy imperfections in cell walls on elastic stiffness of cellular solids. J Mech Phys Solids 46:29-50. https://doi.org/10.1016/s0022-5096(97)00035-5
Wang CC, McDowell DL (2004) In-plane stiffness and yield strength of periodic metal honeycombs. J Eng Mater Technol 126:137-156. https://doi.org/10.1115/1.1688363
Lakes RS (1987) Foam structures with a negative Poisson's ratio. Science 235:1038-1040. https://doi.org/10.1126/science.235.4792.1038
Erdoğan İ, Toktaş İ (2023) Investigation of the auxetic of a novel geometric structure and improvement of Poisson’s ratio at different inner thicknesses. Gazi Univ Fen Bilimleri Derg Part C Tasarım ve Teknoloji 11:893-902. https://doi.org/10.29109/gujsc.1346281
Alderson A, Alderson KL (2007) Auxetic materials. Proc Inst Mech Eng G J Aerosp Eng 221:565-575. https://doi.org/10.1243/09544100JAERO211

Li Y, Yang X, Wang H (2015) Mechanical performance of sandwich structures with auxetic honeycomb cores. Mater Des 85:204-211. https://doi.org/10.1016/j.matdes.2015.06.138
Yang H, Li S, Zhang L (2020) Auxetic honeycomb structures with enhanced energy absorption under out-of-plane impact. Int J Mech Sci 182:105735. https://doi.org/10.1016/j.ijmecsci.2020.105735
Ren X, Das R, Tran P, Ngo TD, Xie YM (2018) Auxetic metamaterials and structures: A review. Smart Mater Struct 27:023001. https://doi.org/10.1088/1361-665X/aaa61c
Lim TC, Huynh NP, Lee HP (2019) Auxetic materials and structures. Springer, Cham. https://doi.org/10.1007/978-3-030-12444-1
Kolken HMA, Zadpoor AA (2017) Auxetic mechanical metamaterials. RSC Adv 7:5111-5129. https://doi.org/10.1039/C6RA27300E
Choi JB, Lakes RS (1992) Non-linear properties of polymer cellular materials with a negative Poisson’s ratio. J Mater Sci 27:5375-5381. https://doi.org/10.1007/BF00541621
Grima JN, Evans KE (2000) Auxetic behavior from rotating squares. J Mater Sci Lett 19:1563-1565. https://doi.org/10.1023/A:1006781224002
Wang Y, Yang H, Li S (2016) Finite element modeling of auxetic structures with re-entrant hexagon topology. Mater Res Express 3:065301. https://doi.org/10.1088/2053-1591/3/6/065301
Ngo TD, Kashani A, Imbalzano G, Nguyen KTQ, Hui D (2018) Additive manufacturing (3D printing): A review of materials, methods, applications and challenges. Compos Part B Eng 143:172-196. https://doi.org/10.1016/j.compositesb.2018.02.012
Gibson I, Rosen DW, Stucker B (2021) Additive manufacturing technologies: 3D printing, rapid prototyping, and direct digital manufacturing, 3rd edn. Springer, Cham. https://doi.org/10.1007/978-3-030-56127-7
Dizon JRC, Espera AH, Chen Q, Advincula RC (2018) Mechanical characterization of 3D-printed polymers. Addit Manuf 20:44-67. https://doi.org/10.1016/j.addma.2017.12.002
Farah S, Anderson DG, Langer R (2016) Physical and mechanical properties of PLA, and their functions in widespread applications—A comprehensive review. Adv Drug Deliv Rev 107:367-392. https://doi.org/10.1016/j.addr.2016.06.012
Torrado AR, Roberson DA (2016) Failure analysis and anisotropy evaluation of 3D-printed tensile test specimens of different geometries. J Fail Anal Prev 16:154-164. https://doi.org/10.1007/s11668-016-0060-x
Li H, Zhang X, Yuan W (2022) Design and evaluation of modified re-entrant honeycomb structures for improved compressive performance. Mater Today Commun 31:103758. https://doi.org/10.1016/j.mtcomm.2022.103758
Günay M, et al (2020) PLA esaslı numunelerde çekme dayanımı için 3D baskı işlem parametrelerinin optimizasyonu. Politeknik Derg 23:73-79
Kaygusuz B, Özerinç S (2018) 3 boyutlu yazıcı ile üretilen PLA bazlı yapıların mekanik özelliklerinin incelenmesi. Makina Tasarım ve İmalat Derg 16:1-6.
Askeland DR (1996) Mechanical testing and properties. In The science and engineering of materials ss 140-187. Boston, MA: Springer US.
Hassan AKF, Abdullah OA (2015) New methodology for prestressing fiber composites. Univ J Mech Eng 3:252-261
Bedeloğlu A, et al (2024) The flexural and compressive properties of sandwich composites with different 3D-printed core structures. Journal of Innovative Engineering and Natural Science 4:98-112
Li T, et al (2018) Exploiting negative Poisson's ratio to design 3D-printed composites with enhanced mechanical properties. Mater Des 142:247-258. https://doi.org/10.1016/j.matdes.2018.01.034
Lekesiz H, Bhullar SK, Karaca AA, Jun MB (2017) Mechanical characterization of auxetic stainless steel thin sheets with reentrant structure. Smart Mater Struct 26:085022. https://doi.org/10.1088/1361-665x/aa73a4
Grima JN, Alderson A, Evans KE (2005) Auxetic behaviour from rotating triangles. J Mater Sci 40:4721-4727. https://doi.org/10.1007/s10853-005-2679-y
Zhang X, Wang X, Ren X, Liu X (2021) Mechanical performance of sandwich structures with different auxetic cores under quasi-static compression. Mater Des 203:109592. https://doi.org/10.1016/j.matdes.2021.109592
Sadikbasha S, Pandurangan V (2023) High velocity impact response of sandwich structures with auxetic tetrachiral cores: analytical model, finite element simulations and experiments. Compos Struct 317:117064. https://doi.org/10.1016/j.compstruct.2023.117064
Xiao P, Lei B, Vescovini R, Shi Z (2024) Optimal design of composite sandwich panel with auxetic reentrant honeycomb using asymptotic equivalent model and PSO algorithm. Compos Struct 328:117761. https://doi.org/10.1016/j.compstruct.2023.117761
Türkoğlu İK, Kasım H, Yazıcı M (2022) Experimental investigation of 3D-printed auxetic core sandwich structures under quasi-static and dynamic compression and bending loads. Int J Protect Struct 14:63-86. https://doi.org/10.1177/20414196221079366

Ayrıntılar

Birincil Dil

İngilizce

Konular

Polimer Teknolojisi, Polimerler ve Plastikler

Bölüm

Araştırma Makalesi

Yazarlar

Emre Demir
0000-0002-4079-4218
Türkiye

Ayşe Bedeloğlu ^*
0000-0003-2960-5188
Türkiye

Yayımlanma Tarihi

30 Temmuz 2026

Gönderilme Tarihi

21 Eylül 2025

Kabul Tarihi

13 Mayıs 2026

Yayımlandığı Sayı

Yıl 2026 Cilt: 6 Sayı: 2

DOI

https://doi.org/10.61112/jiens.1787646

IZ

https://izlik.org/JA72RK74LK

Kaynak Göster

RIS / Bibtex

APA

Demir, E., & Bedeloğlu, A. (2026). Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing. Journal of Innovative Engineering and Natural Science, 6(2), 339-351. https://doi.org/10.61112/jiens.1787646

AMA

1.Demir E, Bedeloğlu A. Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing. JIENS. 2026;6(2):339-351. doi:10.61112/jiens.1787646

Chicago

Demir, Emre, ve Ayşe Bedeloğlu. 2026. “Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing”. Journal of Innovative Engineering and Natural Science 6 (2): 339-51. https://doi.org/10.61112/jiens.1787646.

EndNote

Demir E, Bedeloğlu A (01 Temmuz 2026) Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing. Journal of Innovative Engineering and Natural Science 6 2 339–351.

IEEE

[1]E. Demir ve A. Bedeloğlu, “Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing”, JIENS, c. 6, sy 2, ss. 339–351, Tem. 2026, doi: 10.61112/jiens.1787646.

ISNAD

Demir, Emre - Bedeloğlu, Ayşe. “Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing”. Journal of Innovative Engineering and Natural Science 6/2 (01 Temmuz 2026): 339-351. https://doi.org/10.61112/jiens.1787646.

JAMA

1.Demir E, Bedeloğlu A. Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing. JIENS. 2026;6:339–351.

MLA

Demir, Emre, ve Ayşe Bedeloğlu. “Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing”. Journal of Innovative Engineering and Natural Science, c. 6, sy 2, Temmuz 2026, ss. 339-51, doi:10.61112/jiens.1787646.

Vancouver

1.Emre Demir, Ayşe Bedeloğlu. Invesitigation of mechanical behaviour of auxetic core sandwich composite panels produced by 3D printing. JIENS. 01 Temmuz 2026;6(2):339-51. doi:10.61112/jiens.1787646