Öz
In the current study, mica glass-ceramic materials were produced by basalts including other oxides forming glass structure apart from SiO2 thanks to sintering method, and sintering-machining properties were investigated. For better properties, the composition prepared with some additives such as B2O3, MgO, K2O, and MgF2 was exposed to mixing and grinding process by Al2O3 ball mill for 2 h. The mixture sieved by 75 μm sieves was shaped by one axial pressing under 110 MPa load; obtained cylindrical specimens were sintered at 900 – 1200 °C for 1 h. X ray diffraction analysis (XRD) and Scanning electron microscopy (SEM) were used for characterization. Furthermore, machining tests were carried out. The results showed that suitable sintering and machining were determined.
Anahtar Kelimeler
Öz
Bu çalısmada, SiO2’nin yanı sıra diğer cam yapıcı oksitleri de içeren doğal kayaç bazaltlardan sinterleme yöntemiyle mika esaslı cam-seramik malzemeler üretilerek sinterlenme ve islenebilirlik özellikleri arastırılmıstır. Bu özellikleri iyilestirmek için bilesime B2O3, MgO, K2O ve MgF2 gibi ilaveler yapılarak hazırlanan karısım Al2O3 bilyalı değirmende 2 saat karıstırma ve öğütme islemine tabi tutulmustur. Değirmen islemi sonrası 75 μm’lik elekten geçirilen tozların elek altları tek eksenli preste 110 MPa ‘da preslenerek silindirik numuneler üretilmis ve 900 – 1200 °C sıcaklık aralığında 1 saat sinterlenmistir. X-ısınları difraksiyonu (XRD) ve taramalı elektron mikroskobu (SEM) ile faz ve mikroyapı karakterizasyonları yapılan sinterlenmis numunelerde islenebilirlik testleri de gerçeklestirilmistir. Elde edilen sonuçlar yeterli sinterlemenin gerçeklestiğini ve islenebilirliğin elde edildiğini göstermistir.
Anahtar Kelimeler
Ayrıntılar
| Birincil Dil | Türkçe |
|---|---|
| Bölüm | TOPLANTI BILDIRILERI |
| Yazarlar | |
| Yayımlanma Tarihi | 9 Haziran 2015 |
| Gönderilme Tarihi | 5 Haziran 2015 |
| Yayımlandığı Sayı | Yıl 2015 Cilt: 2 Sayı: 3 |