PREPARATION of BLACK COLORANTS for STONEWARE GLAZES with USING Ni-Co COMPOSITE, CHROMITE and IRON OXIDE MIXTURES

Abstract

Black ceramic colorants were prepared from mixing Ni-Co composite, chromite and magnetite mineral as raw materials. The colorant mixture prepared for this purpose was added to stoneware ceramic glazes at 10%,15% and 20% respectively. The prepared colorant added glazes were ground in the jet mill for 15 minutes and sieves. Glazes applied to the stoneware bodies and then fired at 1200 °C in an industrial ceramic kiln. Color values of colorants and colored glazes were measured L*a*b* with a spectrophotometer device. It has been observed that this prepared colorant has similar properties with the color values of the black colorants used in the sector. As a result, it has been shown that the black colorant obtained can be used as a colorant in Stoneware glaze recipes without causing any problems or defects in the final product.

Keywords

• Stoneware
• Glaze
• Materials
• Characterization
• Colorant

Supporting Institution

KÜTAHYA DUMLUPINAR ÜNİVERİSTESİ

Project Number

2017 – 69

Thanks

This study was financially supported by Kütahya Dumlupınar University Scientific Research Projects Co-operative Center with project no. 2017 – 69. We would like to thank our Scientific Research Projects Co-operator Ship Center, which provided financial support to the project.

References

1. [1] Arcasoy, A., (1983)., Seramik Teknolojisi. M.Ü.G.S.F. Seramik İstanbul., ASD Yay., No:2, 13-14.
2. [2] Yıldızay H., Taşçı E., (2019). Lateritik Nikel Cevherinden Elde Edilen Nikel-Kobalt Oksit Kompozitinin Stoneware Sırındaki Renk Etkileri. Akü Femübid, Özel Sayı (204-211).
3. [3] Costa, G., Della, V.P., Ribeiro, M.J., Oliveria, A.P.N., Monros, G., and Labrincha, J.A. (2008). Synthesis of black ceramic pigments from secondary raw materials. Dyes and Pigments, Vol.77, pp.137–144.
4. [4] Escribano, P., Carda, J.B., Cordoncillo, E., (2001). Esmaltes y pigmentos cerámicos, Faenza Editrice Iberica, Castellon,
5. [5] Italian Ceramic Society, (2003). Colour, Pigments and Colouring in Ceramics, SALA, Modena,
6. [6] Eppler, R.A., (1987). Selecting ceramic pigments. Am. Ceram. Soc. Bull. 66 1600-1604.
7. [7] Ozel, E., and Turan, S., (2003), Production and characterisation of iron-chromium pigments and their interactions with transparent glazes. J. Eur. Ceram. Soc. 23, 2097–2104.
8. [8] Eppler, R.A., (1998). “Colorants for Ceramics”; pp. 877–92 in Encyclopedia of Chemical Technology, Vol. 8, Edited by R.E. Kirk, and D.F. Othmer. Wiley, New York,

9. [9] Maslennikova, G.N., (2001). Pigments of the spinel type, Glass Ceram. 58 5-6.
10. [10] Tanisan, B., and Turan, S. (2011). Black ceramic pigments for porcelain tile bodies produced with chromite ores and iron oxide waste. Journal of Ceramic Processing Research, Vol.12, 462-467.
11. [11] Tanisan, B., and Turan, S. (2012). Synthesis of Fe-Mn black pigments by using hematite waste and manganese ore mixtures. Trans. Indian Ceram. Soc. Vol.71(1),17-22.
12. [12] Ozel, E., Turan, S., Çoruh S., and Ergun, O.N., (2006). Production of brown and black pigments by using flotation waste from copper slag. Waste Manage. Res., Vol. 24, pp.125–133.
13. [13] Costa, G., Della, V.P., Ribeiro, M.J., and Labrincha, J.A., (2008). Forming black spinel pigment from industrial sludge. Am. Ceram. Soc. Bull., Vol.87, No.7, 9101–9107.
14. [14] Yang, Y.G., Xu, J.H., Cai, B., Wang, Q.C., Xiu, D.P., Zhao, Z.B., Sun, Q. Z., and Cao, S. L. (2013). Synthesis and applications of black ceramic from recycled industrial wastes. Advances in Applied Ceramics, 112, 146-148.
15. [15] Ozturk, Z.B., Dal, S. (2022). “Characterization of industrial ceramic glazes containing chromite processing waste: Experimental factorial design effects on color parameters”, Materials Chemistry and Physics, 282, 125928.
16. [16] Ozturk, Z.B., Ay, N., (2010). “The effect of ferrochromium fly ash as a pigment on wall tile glaze”, Advances in Science and Technology, 88,213-218.
17. [17] http://www.metanikel.com.tr /mhp-uretiyoruz