THE INVESTIGATION SURFACE COATING USING FeTi+STELLITE 6 ALLOY OF AISI 304 AUSTENITIC STAINLESS STEEL SURFACE

Yıl 2011, Cilt: 6 Sayı: 4, 48 - 59, 01.05.2011

Öz

In this study, FeTi with Stellite 6 alloy on the 304 austenitic stainless steel surface by using Tungsten Inert Gas (TIG) processing. Alloyed layer and interface were examined with optical microscope (OM), scanning electron microscope (SEM), and X-Ray diffraction (XRD) and energy dispersive spectograph. Macro and microhardness values of samples were measured. OM and SEM observations have been shown that the obtained coating had a smooth and uniform surface, as well as a metallurgical combination with the AISI 304 stainless steel substrate without cracks and pores at the interface. As a result of experimental study; hardness values of samples increased and the grain boundaries were occurred dendritic structures has been determined

AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY

Yıl 2011, Cilt: 6 Sayı: 4, 48 - 59, 01.05.2011

Öz

Bu çaly?mada, AISI 304 ostenitik paslanmaz çelik yüzeyine FeTi +Stellite 6 ala?ymy Tungsten Inert Gas (TIG) kaynak yöntemi kullanylarak ala?ymlandyrylmy?tyr. Kaplama tabakasy; optik mikroskop (OM), taramaly elektron mikroskobu (SEM), X-y?yn difraktogramy (XRD) ve X y?yny enerji da?ylym spektrometresinden (EDS) faydalanylarak incelenmi?tir. Ayryca numunelerin sertlik da?ylymlary mikro ve makro sertlik ölçümleri ile de?erlendirildi. Optik mikroskop ve mikroyapy incelemeleri neticesinde, kaplama tabakasy ile alt tabakanyn birbirlerine metalurjik olarak ba?landy?y, numunelerde, FeTi tozu ilavesine ba?ly olarak sertlik de?erlerinin artty?y ve tane synyrlarynda ince taneli dentritik yapylaryn meydana geldi?i tespit edilmi?tir.

Toplam 0 adet kaynakça vardır.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Elektrik Makinaları
Yazarlar

Mahmut Karataş Bu kişi benim

Hüseyin Turhan Bu kişi benim

Yayımlanma Tarihi 1 Mayıs 2011
Yayımlandığı Sayı Yıl 2011 Cilt: 6 Sayı: 4

Kaynak Göster

APA Karataş, M., & Turhan, H. (2011). AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY. Technological Applied Sciences, 6(4), 48-59. https://doi.org/10.12739/10.12739
AMA Karataş M, Turhan H. AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY. NWSA. Mayıs 2011;6(4):48-59. doi:10.12739/10.12739
Chicago Karataş, Mahmut, ve Hüseyin Turhan. “AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY”. Technological Applied Sciences 6, sy. 4 (Mayıs 2011): 48-59. https://doi.org/10.12739/10.12739.
EndNote Karataş M, Turhan H (01 Mayıs 2011) AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY. Technological Applied Sciences 6 4 48–59.
IEEE M. Karataş ve H. Turhan, “AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY”, NWSA, c. 6, sy. 4, ss. 48–59, 2011, doi: 10.12739/10.12739.
ISNAD Karataş, Mahmut - Turhan, Hüseyin. “AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY”. Technological Applied Sciences 6/4 (Mayıs 2011), 48-59. https://doi.org/10.12739/10.12739.
JAMA Karataş M, Turhan H. AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY. NWSA. 2011;6:48–59.
MLA Karataş, Mahmut ve Hüseyin Turhan. “AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY”. Technological Applied Sciences, c. 6, sy. 4, 2011, ss. 48-59, doi:10.12739/10.12739.
Vancouver Karataş M, Turhan H. AISI 304 OSTENYTYK PASLANMAZ ÇELYK YÜZEYYNYN FeTi+STELLYTE 6 ALA?IMI KULLANILARAK YÜZEY MODYFYKASYONUNUN YNCELENMESY. NWSA. 2011;6(4):48-59.