MICROSTRUCTURE AND ABRASIVE WEAR BEHAVIOUR OF GAS TUNGSTEN ARC SYNTHESIZED Fe-Cr-C-Ti COATTING ON AISI 304 STAINLESSS STEEL

Yıl 2007, Cilt 2, Sayı 4, 340 - 349, 01.05.2007

Öz

AISI 304 stainless steel was coated by using Fe-Cr-C-Ti alloy powders and gas tungsten arc processing method. The microstructure and microhardness values of the coating surfaces were investigated. Gas tungsten arc processing parameters to be committed dentritic structure was seen. In the coating ground plates primary MxCy carbides and secondary phases that is largely with Ti elements was determined. The result of rise 660 Hv. This increase is parallel powder amount. When the look at wear performance of coating samples, which has high powder amount.

TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI

Yıl 2007, Cilt 2, Sayı 4, 340 - 349, 01.05.2007

Öz

AISI 304 paslanmaz çelik yüzeyinde, gaz tungsten ark kaynak yöntemiyle Fe-Cr-C-Ti tozları ergitilerek kaplama tabakası oluşturuldu. Oluşan kaplama tabakalarının mikroyapı görüntüleri ve mikrosertlik değerleri incelendi. Kaplama derinlik parametrelerine bağlı olarak, dendritik yapıların oluştuğu izlendi. Ayrıca kaplama alt tabaka arayüzeyine yakın bölgelerde birincil MxCy karbürleri ve Ti ağırlıklı ikincil fazların oluştuğu tespit edildi. Kaplama tabakalarının mikrosertlik değerleri bakıldığında 660 Hv'ye kadar çıktığı gözlendi. Bu artış toz miktarının artışıyla paraleldir. Kaplama numunelerinin aşınma performansına bakıldığında ise; ençok toz miktarına sahip kaplama numunesinin en iyi aşınma direncini gösterdiği izlendi.

Ayrıntılar

Birincil Dil Türkçe
Bölüm Elektrik Makinaları
Yazarlar

Ayhan ORHAN Bu kişi benim

Yayımlanma Tarihi 1 Mayıs 2007
Yayınlandığı Sayı Yıl 2007, Cilt 2, Sayı 4

Kaynak Göster

Bibtex @ { nwsatecapsci213995, journal = {Technological Applied Sciences}, eissn = {1308-7223}, address = {}, publisher = {E-Journal of New World Sciences Academy}, year = {2007}, volume = {2}, number = {4}, pages = {340 - 349}, doi = {10.12739/10.12739}, title = {TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI}, key = {cite}, author = {Orhan, Ayhan} }
APA Orhan, A. (2007). TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI . Technological Applied Sciences , 2 (4) , 340-349 . Retrieved from https://dergipark.org.tr/tr/pub/nwsatecapsci/issue/20190/213995
MLA Orhan, A. "TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI" . Technological Applied Sciences 2 (2007 ): 340-349 <https://dergipark.org.tr/tr/pub/nwsatecapsci/issue/20190/213995>
Chicago Orhan, A. "TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI". Technological Applied Sciences 2 (2007 ): 340-349
RIS TY - JOUR T1 - TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI AU - Ayhan Orhan Y1 - 2007 PY - 2007 N1 - DO - T2 - Technological Applied Sciences JF - Journal JO - JOR SP - 340 EP - 349 VL - 2 IS - 4 SN - -1308-7223 M3 - UR - Y2 - 2022 ER -
EndNote %0 Technological Applied Sciences TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI %A Ayhan Orhan %T TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI %D 2007 %J Technological Applied Sciences %P -1308-7223 %V 2 %N 4 %R %U
ISNAD Orhan, Ayhan . "TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI". Technological Applied Sciences 2 / 4 (Mayıs 2007): 340-349 .
AMA Orhan A. TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI. NWSA. 2007; 2(4): 340-349.
Vancouver Orhan A. TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI. Technological Applied Sciences. 2007; 2(4): 340-349.
IEEE A. Orhan , "TUNGTEN ASAL GAZ KAYNAK YÖNTEMİYLE AISI 304 PASLANMAZ ÇELİK YÜZEYİNDE ÜRETİLEN Fe-Cr-C-Ti KAPLAMALARININ MİKROYAPISI VE AŞINMA DAVRANIŞI", Technological Applied Sciences, c. 2, sayı. 4, ss. 340-349, May. 2007, doi:10.12739/10.12739