Sintering-Driven Evolution of Phase, Microstructure, and Microstrain in Perlite-Containing Ceramics

Öz

In this study, ceramic samples with perlite additions in the range of 0–50% were sintered at 1050, 1150, and 1250 °C to investigate their effects on phase stability, microstructural evolution, and microstrain. The XRD patterns revealed that the quartz-dominant phase environment was preserved, and the broad amorphous hump at 2θ ≈ 8–16° persisted in all groups. Scherrer analysis indicated that crystallite size reached its maximum (11–12 nm) in samples containing 10–20% perlite at 1150 °C, whereas it decreased to as low as 2–3 nm at ≥40% perlite additions at 1250 °C. The Williamson–Hall method demonstrated a pronounced increase in microstrain at 1250 °C, peaking particularly around 40% perlite. SEM-based dark-field (%) analysis showed more compact and homogeneous structures at medium additions (20–40%), while higher additions tended to cause structural heterogeneity. Furthermore, microhardness measurements supported the observed structural trends. Overall, the findings suggest that the optimum microstructural features (10–20% perlite at 1150 °C) were achieved through low microstrain, high crystallinity, and balanced crystallite size, while excessive perlite additions under advanced sintering conditions disrupted the morphology. These results contribute to defining the optimum perlite ratio in ceramic body design.

Anahtar Kelimeler

• Crystallinity index
• Crystallite size
• Microstrain
• Perlite-containing ceramics
• Sintering

Destekleyen Kurum

This research did not receive any specific grant from funding agencies in the public, commercial, or not-for-profit sectors.

Etik Beyan

The authors declare that no studies involving human participants or animals were conducted by the authors for this article.

Teşekkür

This article is derived from the Master’s thesis entitled “Investigation of the Usability of Pumice and Perlite from the Erzurum Region in the Ceramic Industry” conducted at the Department of Metallurgical and Materials Engineering, Atatürk University (Student: Author 1; Supervisor: Author 2). • B. T. Ceylan (MSc thesis student): Experimental work, XRD and SEM analyses, visualization, writing – original draft. • Y. E. Benkli (Thesis supervisor): Conceptualization, methodology, data interpretation, writing – review and editing, validation. All authors have read and approved the final version of the manuscript.

Perlit Katkılı Seramiklerde Sinterleme Tabanlı Faz, Mikroyapı ve Mikrogerinim Evrimi

Öz

Bu çalışmada, %0–50 aralığında perlit katkılı seramik numuneler 1050, 1150 ve 1250 °C’de sinterlenerek faz kararlılığı, mikroyapısal evrim ve mikrogerinim üzerindeki etkileri incelenmiştir. XRD desenleri, kuvars baskın faz ortamının korunduğunu ve 2θ ≈ 8–16° aralığındaki geniş amorf kubbenin tüm gruplarda sürdüğünü göstermiştir. Scherrer analizi, 1150 °C’de %10–20 perlit katkılı numunelerde kristalit boyutunun 11–12 nm ile maksimuma ulaştığını; 1250 °C’de ≥%40 perlit katkılarında ise 2–3 nm’ye kadar gerilediğini ortaya koymuştur. Williamson–Hall yöntemi, 1250 °C’de mikrogerinimin belirgin şekilde arttığını ve özellikle %40 perlit civarında maksimuma ulaştığını göstermiştir. SEM tabanlı koyu-alan (%) analizi, orta katkılarda (20–40%) daha kompakt ve homojen yapılar, yüksek katkılarda ise heterojenleşme eğilimi olduğunu ortaya koymuştur. Ek olarak, mikrosertlik ölçümleri de yapısal eğilimleri desteklemiştir. Bulgular birlikte değerlendirildiğinde, optimum mikroyapısal özelliklerin (%10–20 perlit, 1150 °C) düşük mikrogerinim, yüksek kristalinlik ve dengeli kristalit boyutu ile elde edildiği; yüksek perlit katkılarının ise ileri sinterleme altında morfolojiyi bozduğu sonucuna varılmıştır. Bu sonuçlar, seramik gövde tasarımında optimum perlit oranının belirlenmesine katkı sağlamaktadır.

Anahtar Kelimeler

• Kristalinlik indeksi
• Kristalit boyutu
• Mikrogerinim
• Perlit katkılı seramikler
• Sinterleme

Destekleyen Kurum

Bu araştırma, kamu, ticari veya kâr amacı gütmeyen fon sağlayıcılarından herhangi bir özel destek almamıştır.

Etik Beyan

Yazarlar, bu makale kapsamında insan katılımcılar veya hayvanlar üzerinde herhangi bir çalışma yapılmadığını beyan ederler.

Teşekkür

Bu makale, Atatürk Üniversitesi Metalürji ve Malzeme Mühendisliği Bölümü’nde yürütülen “Erzurum Yöresinden Elde Edilen Pomza ve Perlitin Seramik Endüstrisinde Kullanılabilirliğinin İncelenmesi” başlıklı Yüksek Lisans tezinden türetilmiştir (Öğrenci: Yazar 1; Danışman: Yazar 2). B. T. Ceylan (Yüksek Lisans öğrencisi): Deneysel çalışmalar, XRD ve SEM analizleri, görselleştirme, yazım – ilk taslak. Y. E. Benkli (Tez danışmanı): Kavramsallaştırma, metodoloji, veri yorumlama, yazım – gözden geçirme ve düzenleme, doğrulama. Tüm yazarlar makalenin son halini okumuş ve onaylamıştır.

Kaynakça

1. Abbasi, N., Hamlet, S., Love, R. M., & Nguyen, N.-T. (2020). Porous scaffolds for bone regeneration. Journal of Science: Advanced Materials and Devices, 5(1), 1–9. https://doi.org/10.1016/j.jsamd.2020.01.007
2. Allen, W.B., Kenneth, O., Thomas, R., Ignatius, Y.C. (2009). On the estimation of average crystallite size of zeolites from the Scherrer equation: A critical evaluation of its application to zeolites with one-dimensional pore systems. Microporous and Mesoporous Materials, 117(1–2), 75-90. https://doi.org/10.1016/j.micromeso.2008.06.010
3. Barsoum, M., Barsoum, M.W. (2002). Fundamentals of Ceramics (1st ed.). CRC Press, 9780429194924, Boca Raton, 624. https://doi.org/10.1201/b21299
4. Basar, F.S. (2023). Investigation of the Contribution of Perlite in Ceramic Mud and its Applications. Thesis (M.Sc.), Sakarya University, Institute of Social Sciences, Türkiye.
5. Benkli, Y.E., Koca, K. (2024). Suitability and characterization of pumice, bauxite, and ferrochrome slag as alternative raw materials in vitrified ceramic industry. Physicochemical Problems of Mineral Processing, 60(2), 187967. https://doi.org/10.37190/ppmp/187967
6. Binici, H. (2007). Effect of crushed ceramic and basaltic pumice as fine aggregates on concrete mortars properties. Construction and Building Materials, 21(6), 1191-1197. https://doi.org/10.1016/j.conbuildmat.2006.06.002
7. Bozkurt, N. (2013). The effect of high temperature on concrete containing perlite powder. SDU International Technologic Science, 5(1), 87-93.
8. Carty, W., Senapati, U. (2005). Porcelain-raw materials, processing, phase evolution, and mechanical behavior. Journal of the American Ceramic Society. 81(1), 3-20. https://doi.org/10.1111/j.1151-2916.1998.tb02290.x.

9. Ceylan, B.T. (2019). Investigation of Pumice and Perlite Extracted in Erzurum Region for the Usability in Ceramics Industry. Thesis (M.Sc.), Atatürk University, Institute of Science and Technology, Türkiye.
10. Chen, A., Li, L., Ren, W., Wang, C., & Wang, Q. (2023). Enhancing thermal insulation and mechanical strength of porous ceramic through size-graded MA hollow spheres. Ceramics International, 49(20), 33247–33254. https://doi.org/10.1016/j.ceramint.2023.08.033
11. Civan, L. (2011). Uses of Pumice as a Glaze Composition and Investigations. Thesis (M.Sc.), Anadolu University, Institute of Science and Technology, Türkiye.
12. Durgut, E. (2025). Evaluation of the use of microwave energy on green floor/wall tile drying process. Drying Technology, 43(5), 937–948. https://doi.org/10.1080/07373937.2025.2474156
13. Durgut, E., Çavdar, Y.E., Çınar, M., Yavuz, O., Özdemir, O. (2025). Fine-size separation of halloysite, kaolinite, and quartz minerals as binary systems using dispersion and sedimentation methods. Physicochemical Problems of Mineral Processing, 61(3), 203-225. https://doi.org/10.37190/ppmp/203225
14. Elmastas, N. (2012). A mine becoming increasingly important for economy of Turkey: pumice. The Journal of International Social Research, 5(23), 197–206.
15. Fatimah, S., Ragadhita, R., Husaeni, D.F., Nandiyanto, A.B.D. (2022). How to calculate crystallite size from X-Ray Diffraction (XRD) using Scherrer Method. ASEAN Journal of Science and Engineering, 2(1), 65-76. https://doi.org/10.17509/ajse.v2i1.37647
16. Gencel, O. (2015). Characteristics of fired clay bricks with pumice additive. Energy and Buildings, 102, 217–224. https://doi.org/10.1016/j.enbuild.2015.05.031
17. Gesing, T.M., Robben, L. (2024). Determination of the average crystallite size and the crystallite size distribution: the envelope function approach EnvACS. Journal of Applied Crystallography, 57(5), 1466-1476. https://doi.org/10.1107/S1600576724007362
18. Hossain, K.M.A. (2004). Properties of volcanic pumice based cement and lightweight concrete. Cement and Concrete Research, 34(2), 283–291. https://doi.org/10.1016/j.cemconres.2003.08.004
19. Idrissi, D.E.M., Elidrissi, Z.C., Achiou, B., Ouammou, M., Younssi, S.A. (2023). Fabrication of low-cost kaolinite/perlite membrane for microfiltration of dairy and textile wastewaters. Journal of Environmental Chemical Engineering, 11(2), 109281. https://doi.org/10.1016/j.jece.2023.109281
20. Ismail, A.I.M., Souaya, E.R., Fathy, M., Abd El-Hakeem A. (2018). Production of lightweight concretes from pumice/bentonite mix. Geotechnical and Geological Engineering, 36, 581-588. https://doi.org/10.1007/s10706-017-0348-z
21. Kai, H., Nuofu, C., Congjie, W., Lishuai, W., Jikun, C. (2018). Method for determining crystal grain size by X-ray diffraction. Crystal Research-Technology, 53(2), 1700157. https://doi.org/10.1002/crat.201700157
22. Kayacı, K. (2020). The use of perlite as flux in the production of porcelain stoneware tiles. Boletín de la Sociedad Española de Cerámica y Vidrio, 60(5), 283-290. https://doi.org/10.1016/j.bsecv.2020.03.003
23. Kawsar, Md., Sahadat, H.Md., Newaz, M.B., Samina, A. (2024). Synthesis of nano-crystallite hydroxyapatites in different media and a comparative study for estimation of crystallite size using Scherrer method, Halder-Wagner method size-strain plot, and Williamson-Hall model. Heliyon, 10(3), e25347. https://doi.org/10.1016/j.heliyon.2024.e25347
24. Kingery, W.D., Bowen, H.K., Uhlmann, D.R. (1976). Introduction to Ceramics (2nd edition). Wiley, 978-0-471-47860-7, 1056.
25. Koca, K. (2019). Investigation of Vitrified Ceramic Production Supplies from Combinations of Pumice and Industrial Wastes. Thesis (M.Sc.), Atatürk University, Institute of Science and Technology, Türkiye.
26. Koca, K., Benkli, Y.E. (2025). Microstructural and elemental characterization of pumice–bauxite–clay ceramics: effects of sintering temperature and Scherrer-based analysis. Journal of the Australian Ceramic Society. https://doi.org/10.1007/s41779-025-01242-8
27. Kuzugudenli, O.E. (2004). Use of pumice stone as a ceramic raw material. Key Engineering Materials, 264–268, 1427–1430. https://doi.org/10.4028/www.scientific.net/kem.264-268.1427
28. Kuzugudenli, O.E., Zengin, G. (2004). Production of low-density ceramics using pumice stone. Key Engineering Materials, 264–268, 2527–2530. https://doi.org/10.4028/www.scientific.net/kem.264-268.2527
29. Liu, K., Shi, Y., Li, C., Hao, L., Liu, J., Wei, Q. (2014). Indirect selective laser sintering of epoxy resin-Al2O3 ceramic powders combined with cold isostatic pressing. Ceramics International, 40(5), 7099–7106. https://doi.org/10.1016/j.ceramint.2013.12.043
30. Liu, K., Sun, H., Shi, Y., Liu, J., Zhang, S., Huang, S., Wang, M. (2016). Research on selective laser sintering of Kaolin–epoxy resin ceramic powders combined with cold isostatic pressing and sintering. Ceramics International, 42(9), 10711–10718. https://doi.org/10.1016/j.ceramint.2016.03.190
31. Lu, T. J., & Fleck, N. A. (1998). The thermal shock resistance of solids. Acta Materialia, 46(13), 4755–4768. https://doi.org/10.1016/S1359-6454(98)00127-X
32. Lukianova, O. (2015). Mechanical and elastic properties of new silicon nitride ceramics produced by cold isostatic pressing and free sintering. Ceramics International, 41(10A), 13716–13720. https://doi.org/10.1016/j.ceramint.2015.08.026
33. Mercan, E. (2021). Production of Aerogel-Modified Expanded Perlite Aggregate and Clay (AEP/C) Board and Investigation of Physical and Mechanical Properties. Thesis (M.Sc.), Ihsan Doğramacı Bilkent University, Institute of Economics and Social Sciences, Türkiye.
34. Monshi, A., Foroughi, M.R., Monshi, M.R. (2012). Modified Scherrer equation to estimate more accurately nano-crystallite size using XRD. World Journal of Nano Science and Engineering, 2(3), 154-160. https://doi.org/10.4236/wjnse.2012.23020
35. Nusrat, J.T., Sahadat, H.Md., Newaz, M.B., Samina, A. (2024). Green synthesis of Ag2O - facile synthesis of ZnO and characterization using FTIR, bandgap energy - XRD (Scherrer equation, Williamson-Hall, size-train plot, Monshi-Scherrer model). Results in Chemistry, 7, 101313. https://doi.org/10.1016/j.rechem.2024.101313
36. Oztürk, B.Z., Can, A. (2023). Sürdürülebilir endüstriyel özellikleri taşıyan seramik sağlık gereci sırları üretiminde mikronize pomzanın kullanımı. Gazi Üniversitesi Mühendislik Mimarlık Fakültesi Dergisi, 38(3), 1967-1978. https://doi.org/10.17341/gazimmfd.1121723
37. Poyraz, H.B., Erginel, N., Ay, N. (2006). The use of pumice (pumicite) in transparent roof tile glaze composition. Journal of the European Ceramic Society, 26(4-5), 741–746. https://doi.org/10.1016/j.jeurceramsoc.2005.06.032 Rahaman, M.N. (2003). Ceramic Processing and Sintering (2nd Edition), CRC Press, 9781315274126, Boca Raton, 875. https://doi.org/10.1201/9781315274126
38. Reka, A., Pavlovski, B., Lisichkov, K., Jashari, A., Boev, B., Boev, I., Lazarova, M., Eskizeybek, V., Oral, A., Jovanovski, G., Makreski, P. (2019). Chemical, mineralogical and structural features of native and expanded perlite from Macedonia. Geologia Croatica, 72(3), 215–221. https://doi.org/10.4154/gc.2019.18
39. Rzepa, K., Wons, W., Reben, M. (2016). Building ceramics with improved thermal insulation parameters. E3S Web of Conferences, 10, 00082. https://doi.org/10.1051/e3sconf/20161000082
40. Tarhan, M., Tarhan, B. (2018). The Effect of Perlite Use on Ceramic Wall Tile Technical Properties. International Journal of Engineering Research and Development, 10(1), 94–100. https://doi.org/10.29137/umagd.364552
41. Tarhan, B., Tarhan, M. (2022). Utilization of perlite as an alternative raw material in the production of ceramic sanitaryware. Journal of Thermal Analysis and Calorimetry, 147, 3509–3518. https://doi.org/10.1007/s10973-021-10784-5
42. Wang, Q., Sui, J., Li, L., Tuo, Y., Zhang, W., Zhong, G., Zhou, H., & Feng, X. (2024). Recent advances in regulating ceramic monolithic catalyst structure for preferential oxidation of CO in H₂. Molecules, 29(15), 3481. https://doi.org/10.3390/molecules29153481
43. Zhang, S.S. (2006). The effect of the charging protocol on the cycle life of a Li-ion battery. Journal of Power Sources, 161(2), 1385–1391. https://doi.org/10.1016/j.jpowsour.2006.06.040