Tekstil ve Mühendis 1300-7599 2147-0510 TMMOB Tekstil Mühendisleri Odası 10.7216/130075992012198503 Engineering Mühendislik Knot- and Loop Tensile Tests of Ultra High-Modulus Pitch-Based Carbon Fibers Ultra Yüksek Modüllü Zift-Esaslı Karbon Liflerin Düğüm ve Halka Çekme Testleri Glowanıa Michael Schneıders Sven Hesselbach Johanne Sımonıs Kristina Grıes Thomas 03 01 2012 19 85 9 14 12 13 2013 Copyright © 1987, Tekstil ve Mühendis 1987 Tekstil ve Mühendis

Increasingly Fibre Reinforced Plastics (FRP) replace metal materials e.g. because of their lightweight. Besides FRP have a low thermal conductivity (TC). Thus, applications like are limited because heat cannot conduct through FRP and causes damage to electrical components.The TC of FRP can be increased one order and more using pitch-based carbon fibres. Unfortunately the processing of these fibres is still a huge challenge because of the high fibre brittleness. The Institut für Textiltechnik of RWTH Aachen University, Germany, has developed technologies to process these fibres to enable the manufacturing of 3D preforms for new ways of lightweight engineering.

Hafif olmalarý gibi sebeplerle elyaf takviyeli plastikler (FRP) hýzlý bir þekilde metallerin yerini almaktadýr. Dahasý FRPmalzemelerin termal geçirgenlikleri (TC) de düþüktür. Bu sebeple, benzer uygulamalarý sýnýrlýdýr çünkü ýsý FRPler ile iletilemez ve elektronik parçalara zarar verir. FRPlerin TC deðerleri zift esaslý karbon elyaf kullanýmý ile arttýrýlabilir. Ancak yüksek elyaf kýrýlganlýklarý sebebiyle bu liflerin üretimi hala çok zordur. Almanya RWTH Aachen Teknik Tekstiller Ensititüsü, hafif mühendislik uygulamalarý için 3D ön þekillerin üretiminde kullanýlmak üzere bu liflerin iþlenmesi için teknolojiler geliþtirmiþtir.

 Fibre Reinforced Plastics Carbon fibre Glass fibre Pitch based Thermal Conductivity Elyaf takviyeli plastikler karbon elyaf cam elyaf zift esaslý termal iletkenlik