Investigation of the Effect of Raising and Finishing Process on the Physical Performance of 3-Thread Fleece Fabric
Year 2022,
Volume: 32 Issue: 3, 183 - 192, 30.09.2022
Ğassan Asker
,
Onur Balcı
Abstract
Within the scope of the study, pre-softening, raising and final softening processes were applied to 2 selected fabrics under different conditions. The raising fastness, air permeability and bursting strength tests were performed on the samples obtained after the processes, and the effect of the process conditions on the researched performance values was examined. This paper is also detailed by statistical analysis. When the results were examined, it was seen that the best result in terms of raising fastness was the fabric with 50% waste + 50% PES back yarn. As a process, it was determined that the best result was obtained after a single passage with micro silicon pre-softening and raising at a speed of 15m / min, and then a low concentration softening process with a polyvinyl acetate-based binder and softener mixture.
Supporting Institution
TÜBİTAK
Thanks
This study was supported by The Scientific and Technological Research Council of Turkey (TÜBİTAK) with Project No: 3161066.
References
- 1. Marmaralı A.B., (2004). Atkı Örmeciliğine Giriş. Ege Üniversitesi Tekstil ve Konfeksiyon Araştırma-Uygulama Merkezi Yayını, İzmir.
- 2. Sarker M., Rahman T., Rahman M., (2012). Study on Fleece Knit Fabric. Daffodil International University, Dhaka.
3. Pailthorpe M., (2009). Dry Finishing of Wool Fabrics. The Australian Wool Education Trust Licensee for Educational Activities University of New England.
- 4. SchindlerW.D, Hauser P. J., (2004). Chemical Finishing of Textile. Woodhead Publishing Ltd. Cambridge, England.
- 5. Candan C, Önal L., (2002). Dimensional, Pilling, and Abrasion Properties of Weft Knits Made from Open-End and Ring Spun Yarns. Textile Research Journal. 72(2), 164-169.
- 6. Çoruh E.H., (2004). İnvestigation of Dimensional Stability of Knitted Fabric. (Master’s. Thesis). Textile Engineering University of Gaziantep, Gaziantep.
- 7. Gülsevin N., (2005). Spor Giysilerin Konfor Özellikleri Üzerine Bir Araştırma. (Yüksek Lisans Tezi). Ege Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, İzmir
- 8. Meriç B., Demirhan F., (2005). Örme Kumaş ve Giysilerde Yıkama ve Kurutma Sonrası Boyut Değişimlerinin İncelenmesi. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi, 3, 381-390.
- 9. Güneşoğlu C., (2006) Spor Giysilik Kumaşların Performans Özelliklerinin Nanoteknolojik Ürünler Kullanılarak Geliştirilmesi ve Aplikasyon Tekniklerinin Araştırılması. (Doktora Tezi). Uludağ Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Bursa.
- 10. Erkoç S., (2006). Yuvarlak Örme Makinalarında Üretilen Örme Kumaş Özelliklerini Etkileyen Parametrelerin İncelenmesi. (Yüksek Lisans Tezi). Çukurova Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Adana.
- 11. Emirhanova N., Kavuşturan Y., (2008). Effects of Knit Structure on the Dimensional and Physical Properties of Winter Outerwear Knitted Fabrics, Fibres&Textiles in Eastern Europe, (16)2, 69-74.
- 12. Baçan V., (2010). Endüstriyel Örme Giyim Ürünlerinin Teknolojik Özelliklerinin Belirlenmesi. (Doktora Tezi). Ankara Üniversitesi, Fen Bilimleri Enstitüsü, Ev Ekonomisi (El Sanatları) Ana Bilim Dalı, Ankara.
- 13. Mezarcıöz S., (2010). Farklı Üretim Teknikleriyle Eğrilmiş İpliklerden Örülen Kumaşların Belirli Özelliklerinin İncelenmesi ve İstatistiksel Modellenmesi. (Doktora Tezi). Çukurova Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Adana.
- 14. Özyazgan V., (2010). Çift Plakalı Örgü Kumaşlarda Bitim İşlemlerine Bağlı Boyutsal Değişimler. (Doktora Tezi). Marmara Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Eğitimi Ana Bilim Dalı, İstanbul
- 15. Ertekin G., Marmaralı A., (2011). Askı ve Atlamanın Düz Örgü Kumaşların Isıl Konfor Özelliklerine Etkileri. Tekstil ve Mühendis Dergisi, (18) 83, 22-26.
- 16. Taştan E.Ö., (2013). Aktif Spor Giyimde Kullanılan Bazı Örme Kumaş Yapılarının Isı ve Nem Transferi Özelliklerinin İncelenmesi. (Yüksek Lisans Tezi). Uludağ Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Bursa.
- 17. Yurdakul B., Özçelik E., Sakin S., (2014). Kimyasal İşlem ve Membran YapılarınKombinasyonu ile Su İtici Spor Giyim Ürünlerinin Geliştirilmesi. XIII. Uluslararası İzmir Tekstil ve Hazır Giyim Sempozyumu, İzmir, Türkiye.
- 18. Güneşoğlu S., Meriç B., Güneşoğlu C., (2005). Thermal Contact Properties of 2-Yarn Fleece Knitted Fabrics. Fibres&Textiles in Eastern Europe, 13, 2(50), 46-50.
- 19. Güneşoğlu S., (2005). Sportif Amaçlı Giysilerin Konfor Özelliklerinin Araştırılması. (Doktora Tezi). Uludağ Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Bursa.
- 20. Tatlı N.Ö., (2007). Üç İplik Kumaş Yapısının ve Geçirdiği Terbiye İşlemlerinin Yanma Davranışı Üzerine Etkileri. (Yüksek Lisans Tezi). İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, İstanbul.
- 21.Balcı O., Asker Ğ., Yolaçan G., Örtlek H.G., C., (2011). İki İplik Örme Kumaşların Kullanım ve Üretim Performansına Etkisi Olan Parametrelerin Tespit Edilmesi. Tekstil&Teknik Dergisi, 27 (323), 86-92.
- 22. Badr A. A., El-nahrawy A., (2016). Moisture Properties of Raised 3-Thread Fleece Fabric Knitted with Different Face and Fleecy Yarns. Alexandria Engineering Journal 55, 2881–2892
- 23. Asker Ğ., Akkuş E., Arslan İ., Sevilmiş M., Pektaş K. and Balcı O., (2019). Investigation of The Fibre Loss Effect of Raised 3-Thread Fleecy Fabric. Tekstil ve Mühendis, 26(116), 346-352.
Year 2022,
Volume: 32 Issue: 3, 183 - 192, 30.09.2022
Ğassan Asker
,
Onur Balcı
References
- 1. Marmaralı A.B., (2004). Atkı Örmeciliğine Giriş. Ege Üniversitesi Tekstil ve Konfeksiyon Araştırma-Uygulama Merkezi Yayını, İzmir.
- 2. Sarker M., Rahman T., Rahman M., (2012). Study on Fleece Knit Fabric. Daffodil International University, Dhaka.
3. Pailthorpe M., (2009). Dry Finishing of Wool Fabrics. The Australian Wool Education Trust Licensee for Educational Activities University of New England.
- 4. SchindlerW.D, Hauser P. J., (2004). Chemical Finishing of Textile. Woodhead Publishing Ltd. Cambridge, England.
- 5. Candan C, Önal L., (2002). Dimensional, Pilling, and Abrasion Properties of Weft Knits Made from Open-End and Ring Spun Yarns. Textile Research Journal. 72(2), 164-169.
- 6. Çoruh E.H., (2004). İnvestigation of Dimensional Stability of Knitted Fabric. (Master’s. Thesis). Textile Engineering University of Gaziantep, Gaziantep.
- 7. Gülsevin N., (2005). Spor Giysilerin Konfor Özellikleri Üzerine Bir Araştırma. (Yüksek Lisans Tezi). Ege Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, İzmir
- 8. Meriç B., Demirhan F., (2005). Örme Kumaş ve Giysilerde Yıkama ve Kurutma Sonrası Boyut Değişimlerinin İncelenmesi. Pamukkale Üniversitesi Mühendislik Bilimleri Dergisi, 3, 381-390.
- 9. Güneşoğlu C., (2006) Spor Giysilik Kumaşların Performans Özelliklerinin Nanoteknolojik Ürünler Kullanılarak Geliştirilmesi ve Aplikasyon Tekniklerinin Araştırılması. (Doktora Tezi). Uludağ Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Bursa.
- 10. Erkoç S., (2006). Yuvarlak Örme Makinalarında Üretilen Örme Kumaş Özelliklerini Etkileyen Parametrelerin İncelenmesi. (Yüksek Lisans Tezi). Çukurova Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Adana.
- 11. Emirhanova N., Kavuşturan Y., (2008). Effects of Knit Structure on the Dimensional and Physical Properties of Winter Outerwear Knitted Fabrics, Fibres&Textiles in Eastern Europe, (16)2, 69-74.
- 12. Baçan V., (2010). Endüstriyel Örme Giyim Ürünlerinin Teknolojik Özelliklerinin Belirlenmesi. (Doktora Tezi). Ankara Üniversitesi, Fen Bilimleri Enstitüsü, Ev Ekonomisi (El Sanatları) Ana Bilim Dalı, Ankara.
- 13. Mezarcıöz S., (2010). Farklı Üretim Teknikleriyle Eğrilmiş İpliklerden Örülen Kumaşların Belirli Özelliklerinin İncelenmesi ve İstatistiksel Modellenmesi. (Doktora Tezi). Çukurova Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Adana.
- 14. Özyazgan V., (2010). Çift Plakalı Örgü Kumaşlarda Bitim İşlemlerine Bağlı Boyutsal Değişimler. (Doktora Tezi). Marmara Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Eğitimi Ana Bilim Dalı, İstanbul
- 15. Ertekin G., Marmaralı A., (2011). Askı ve Atlamanın Düz Örgü Kumaşların Isıl Konfor Özelliklerine Etkileri. Tekstil ve Mühendis Dergisi, (18) 83, 22-26.
- 16. Taştan E.Ö., (2013). Aktif Spor Giyimde Kullanılan Bazı Örme Kumaş Yapılarının Isı ve Nem Transferi Özelliklerinin İncelenmesi. (Yüksek Lisans Tezi). Uludağ Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Bursa.
- 17. Yurdakul B., Özçelik E., Sakin S., (2014). Kimyasal İşlem ve Membran YapılarınKombinasyonu ile Su İtici Spor Giyim Ürünlerinin Geliştirilmesi. XIII. Uluslararası İzmir Tekstil ve Hazır Giyim Sempozyumu, İzmir, Türkiye.
- 18. Güneşoğlu S., Meriç B., Güneşoğlu C., (2005). Thermal Contact Properties of 2-Yarn Fleece Knitted Fabrics. Fibres&Textiles in Eastern Europe, 13, 2(50), 46-50.
- 19. Güneşoğlu S., (2005). Sportif Amaçlı Giysilerin Konfor Özelliklerinin Araştırılması. (Doktora Tezi). Uludağ Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, Bursa.
- 20. Tatlı N.Ö., (2007). Üç İplik Kumaş Yapısının ve Geçirdiği Terbiye İşlemlerinin Yanma Davranışı Üzerine Etkileri. (Yüksek Lisans Tezi). İstanbul Teknik Üniversitesi, Fen Bilimleri Enstitüsü, Tekstil Mühendisliği Ana Bilim Dalı, İstanbul.
- 21.Balcı O., Asker Ğ., Yolaçan G., Örtlek H.G., C., (2011). İki İplik Örme Kumaşların Kullanım ve Üretim Performansına Etkisi Olan Parametrelerin Tespit Edilmesi. Tekstil&Teknik Dergisi, 27 (323), 86-92.
- 22. Badr A. A., El-nahrawy A., (2016). Moisture Properties of Raised 3-Thread Fleece Fabric Knitted with Different Face and Fleecy Yarns. Alexandria Engineering Journal 55, 2881–2892
- 23. Asker Ğ., Akkuş E., Arslan İ., Sevilmiş M., Pektaş K. and Balcı O., (2019). Investigation of The Fibre Loss Effect of Raised 3-Thread Fleecy Fabric. Tekstil ve Mühendis, 26(116), 346-352.