ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V

Mahmut Furkan Kalkan; Murat Artan; Hasan Mithat Delibaş; Abdulcabbar Yavuz; Necip Fazıl Yılmaz

EN

ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V

Abstract

Energy storage systems have received increasing attention in recent years because of the requirements of energy supply with respect to the growing population and technology. Among the technologies of energy storage devices, supercapacitors become popular due to their superior characteristics such as high power density, extremely fast charge-discharge capability and long life cycle. A wide variety of materials are already in use to fabricate supercapacitors. Carbon and its derivatives are common materials among the electrode materials of supercapacitors. In this study, electrochemical behaviour of flexible graphite yarns are investigated in different media in order to elucidate the performance of graphite as a supercapacitor material. Electrochemical experiments of graphite electrode are carried out in sodium sulphate (Na2SO4), hydrochloric acid (HCl), potassium hydroxide (KOH) and Ethaline deep eutectic solvent as electrolyte media. Graphite yarn is cycled at wide potential window (from -1 V to 1 V) at various scan rates in the range of 5 to 100 mV s−1 in order to observe the associated electrochemical behaviour and performance. Graphite yarn electrodes without any treatment can be used in Ethaline and aqueous Na2SO4 electrolytes. However, these electrodes cannot be used in acidic or alkaline media with high potential window of 2 V.

Keywords

energy storage, flexible, capacitance, graphite

Supporting Institution

Gaziantep Üniversitesi BAP Birimi

Project Number

(MF.ALT.19.18).

Thanks

The authors thank the Scientific Research Unit of Gaziantep University

References

[1] X. Wang, S. Han, Y. Wu, X. Wang, Coverage and energy consumption control in mobile heterogeneous wireless sensor networks, IEEE Trans. Automat. Contr. 58 (2012) 975–988.
[2] Z.S. Iro, C. Subramani, S.S. Dash, A brief review on electrode materials for supercapacitor, Int. J. Electrochem. Sci. 11 (2016) 10628–10643. https://doi.org/10.20964/2016.12.50.
[3] W. Zuo, R. Li, C. Zhou, Y. Li, J. Xia, J. Liu, Battery‐supercapacitor hybrid devices: recent progress and future prospects, Adv. Sci. 4 (2017) 1600539.
[4] A. Borenstein, O. Hanna, R. Attias, S. Luski, T. Brousse, D. Aurbach, Carbon-based composite materials for supercapacitor electrodes: a review, J. Mater. Chem. A. 5 (2017) 12653–12672.
[5] M. Vangari, T. Pryor, L. Jiang, Supercapacitors: review of materials and fabrication methods, J. Energy Eng. 139 (2013) 72–79.
[6] B. Xie, C. Yang, Z. Zhang, P. Zou, Z. Lin, G. Shi, Q. Yang, F. Kang, C.-P. Wong, Shape-tailorable graphene-based ultra-high-rate supercapacitor for wearable electronics, ACS Nano. 9 (2015) 5636–5645.
[7] D.P. Dubal, Advances in flexible supercapacitors for portable and wearable smart gadgets, in: Emerg. Mater. Energy Convers. Storage, Elsevier, 2018: pp. 209–246.
[8] H. Li, Z. Tang, Z. Liu, C. Zhi, Evaluating flexibility and wearability of flexible energy storage devices, Joule. 3 (2019) 613–619.
[9] W.-J. Song, S. Lee, G. Song, H. Bin Son, D.-Y. Han, I. Jeong, Y. Bang, S. Park, Recent progress in aqueous based flexible energy storage devices, Energy Storage Mater. 30 (2020) 260–286.
[10] Y. Li, Z. Kang, X. Yan, S. Cao, M. Li, Y. Liu, S. Liu, Y. Sun, X. Zheng, Y. Zhang, A facile method for the preparation of three-dimensional CNT sponge and a nanoscale engineering design for high performance fiber-shaped asymmetric supercapacitors, J. Mater. Chem. A. 5 (2017) 22559–22567.

[11] X. Cheng, X. Gui, Z. Lin, Y. Zheng, M. Liu, R. Zhan, Y. Zhu, Z. Tang, Three-dimensional α-Fe 2 O 3/carbon nanotube sponges as flexible supercapacitor electrodes, J. Mater. Chem. A. 3 (2015) 20927–20934.
[12] J. Li, W. Lu, Y. Yan, T.-W. Chou, High performance solid-state flexible supercapacitor based on Fe 3 O 4/carbon nanotube/polyaniline ternary films, J. Mater. Chem. A. 5 (2017) 11271–11277.
[13] Y.-Y. Horng, Y.-C. Lu, Y.-K. Hsu, C.-C. Chen, L.-C. Chen, K.-H. Chen, Flexible supercapacitor based on polyaniline nanowires/carbon cloth with both high gravimetric and area-normalized capacitance, J. Power Sources. 195 (2010) 4418–4422.
[14] I. Shown, A. Ganguly, L. Chen, K. Chen, Conducting polymer‐based flexible supercapacitor, Energy Sci. Eng. 3 (2015) 2–26.
[15] Z. Wang, D.O. Carlsson, P. Tammela, K. Hua, P. Zhang, L. Nyholm, M. Strømme, Surface modified nanocellulose fibers yield conducting polymer-based flexible supercapacitors with enhanced capacitances, ACS Nano. 9 (2015) 7563–7571.
[16] C. Meng, C. Liu, L. Chen, C. Hu, S. Fan, Highly flexible and all-solid-state paperlike polymer supercapacitors, Nano Lett. 10 (2010) 4025–4031.
[17] S.W. Ali, S. Bairagi, Conductive Polymer Based Flexible Supercapacitor, in: Self-Standing Substrates, Springer, 2020: pp. 211–233.
[18] M. Miao, Electrical conductivity of pure carbon nanotube yarns, Carbon N. Y. 49 (2011) 3755–3761. https://doi.org/https://doi.org/10.1016/j.carbon.2011.05.008.
[19] Z. Zhang, P. Zhang, D. Zhang, H. Lin, Y. Chen, A new strategy for the preparation of flexible macroscopic graphene fibers as supercapacitor electrodes, Mater. Des. 157 (2018) 170–178.
[20] N. He, W. Shan, J. Wang, Q. Pan, J. Qu, G. Wang, W. Gao, Mordant inspired wet-spinning of graphene fibers for high performance flexible supercapacitors, J. Mater. Chem. A. 7 (2019) 6869–6876.
[21] Z. Yang, Y. Jia, Y. Niu, Y. Zhang, C. Zhang, P. Li, M. Zhu, Q. Li, One-step wet-spinning assembly of twisting-structured graphene/carbon nanotube fiber supercapacitor, J. Energy Chem. 51 (2020) 434–441.
[22] L. Kou, T. Huang, B. Zheng, Y. Han, X. Zhao, K. Gopalsamy, H. Sun, C. Gao, Coaxial wet-spun yarn supercapacitors for high-energy density and safe wearable electronics, Nat. Commun. 5 (2014) 1–10.
[23] S. Cai, T. Huang, H. Chen, M. Salman, K. Gopalsamy, C. Gao, Wet-spinning of ternary synergistic coaxial fibers for high performance yarn supercapacitors, J. Mater. Chem. A. 5 (2017) 22489–22494.
[24] W.K. Chee, H.N. Lim, N.M. Huang, Electrochemical properties of free‐standing polypyrrole/graphene oxide/zinc oxide flexible supercapacitor, Int. J. Energy Res. 39 (2015) 111–119.
[25] Z. Dou, Z. Qin, Y. Shen, S. Hu, N. Liu, Y. Zhang, High–performance flexible supercapacitor based on carbon cloth through in–situ electrochemical exfoliation and re–deposition in neutral electrolyte, Carbon N. Y. 153 (2019) 617–624.
[26] F. Hekmat, Y. Tutel, H.E. Unalan, Wearable supercapacitors based on nickel tungstate decorated commercial cotton fabrics, Int. J. Energy Res. 44 (2020) 7603–7616.
[27] A.P. Bond, H.H. Uhlig, Corrosion behavior and passivity of nickel‐chromium and cobalt‐chromium alloys, J. Electrochem. Soc. 107 (1960) 488.
[28] T.G. Yun, B. Il Hwang, D. Kim, S. Hyun, S.M. Han, Polypyrrole–MnO2-coated textile-based flexible-stretchable supercapacitor with high electrochemical and mechanical reliability, ACS Appl. Mater. Interfaces. 7 (2015) 9228–9234.
[29] X. Pu, L. Li, M. Liu, C. Jiang, C. Du, Z. Zhao, W. Hu, Z.L. Wang, Wearable self‐charging power textile based on flexible yarn supercapacitors and fabric nanogenerators, Adv. Mater. 28 (2016) 98–105.
[30] Y. Wen, B. Wang, C. Huang, L. Wang, D. Hulicova‐Jurcakova, Synthesis of phosphorus‐doped graphene and its wide potential window in aqueous supercapacitors, Chem. Eur. J. 21 (2015) 80–85.
[31] Y.-J. Gu, W. Wen, J.-M. Wu, Wide potential window TiO2@carbon cloth and high capacitance MnO2@carbon cloth for the construction of a 2.6 V high-performance aqueous asymmetric supercapacitor, J. Power Sources. 469 (2020) 228425. https://doi.org/https://doi.org/10.1016/j.jpowsour.2020.228425.
[32] L. Demarconnay, E. Raymundo-Piñero, F. Béguin, Adjustment of electrodes potential window in an asymmetric carbon/MnO2 supercapacitor, J. Power Sources. 196 (2011) 580–586. https://doi.org/https://doi.org/10.1016/j.jpowsour.2010.06.013.
[33] A.A. Bojang, H.S. Wu, Characterization of electrode performance in enzymatic biofuel cells using cyclic voltammetry and electrochemical impedance spectroscopy, Catalysts. 10 (2020) 782.
[34] S. Vinayaraj, K. Brijesh, P.C. Dhanush, H.S. Nagaraja, ZnWO4/SnO2 composite for supercapacitor applications, Phys. B Condens. Matter. 596 (2020) 412369.

Details

Primary Language

English

Subjects

Material Production Technologies

Journal Section

Research Article

Authors

Mahmut Furkan Kalkan ^*
0000-0002-1903-5583
Türkiye

Murat Artan
0000-0002-0629-5626
Türkiye

Hasan Mithat Delibaş
0000-0003-3353-8600
Türkiye

Abdulcabbar Yavuz
0000-0002-7216-0586
Türkiye

Necip Fazıl Yılmaz
0000-0002-0166-9799
Türkiye

Publication Date

June 30, 2022

Submission Date

November 17, 2021

Acceptance Date

June 2, 2022

Published in Issue

Year 2022 Volume: 5 Number: 1

IZ

https://izlik.org/JA85YE55RY

APA

Kalkan, M. F., Artan, M., Delibaş, H. M., Yavuz, A., & Yılmaz, N. F. (2022). ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V. The International Journal of Materials and Engineering Technology, 5(1), 48-52. https://izlik.org/JA85YE55RY

AMA

1.Kalkan MF, Artan M, Delibaş HM, Yavuz A, Yılmaz NF. ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V. TIJMET. 2022;5(1):48-52. https://izlik.org/JA85YE55RY

Chicago

Kalkan, Mahmut Furkan, Murat Artan, Hasan Mithat Delibaş, Abdulcabbar Yavuz, and Necip Fazıl Yılmaz. 2022. “ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V”. The International Journal of Materials and Engineering Technology 5 (1): 48-52. https://izlik.org/JA85YE55RY.

EndNote

Kalkan MF, Artan M, Delibaş HM, Yavuz A, Yılmaz NF (June 1, 2022) ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V. The International Journal of Materials and Engineering Technology 5 1 48–52.

IEEE

[1]M. F. Kalkan, M. Artan, H. M. Delibaş, A. Yavuz, and N. F. Yılmaz, “ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V”, TIJMET, vol. 5, no. 1, pp. 48–52, June 2022, [Online]. Available: https://izlik.org/JA85YE55RY

ISNAD

Kalkan, Mahmut Furkan - Artan, Murat - Delibaş, Hasan Mithat - Yavuz, Abdulcabbar - Yılmaz, Necip Fazıl. “ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V”. The International Journal of Materials and Engineering Technology 5/1 (June 1, 2022): 48-52. https://izlik.org/JA85YE55RY.

JAMA

1.Kalkan MF, Artan M, Delibaş HM, Yavuz A, Yılmaz NF. ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V. TIJMET. 2022;5:48–52.

MLA

Kalkan, Mahmut Furkan, et al. “ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V”. The International Journal of Materials and Engineering Technology, vol. 5, no. 1, June 2022, pp. 48-52, https://izlik.org/JA85YE55RY.

Vancouver

1.Mahmut Furkan Kalkan, Murat Artan, Hasan Mithat Delibaş, Abdulcabbar Yavuz, Necip Fazıl Yılmaz. ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V. TIJMET [Internet]. 2022 Jun. 1;5(1):48-52. Available from: https://izlik.org/JA85YE55RY

Bu eser Creative Commons Atıf-GayriTicari 4.0 Uluslararası Lisansı ile lisanslanmıştır.

Abstract

ELECTROCHEMICAL BEHAVIOUR AND PERFORMANCE OF FLEXIBLE GRAPHITE YARNS IN DIFFERENT ELECTROLYTES WITH WIDE POTENTIAL WINDOW OF 2 V

Abstract

Keywords

Supporting Institution

Project Number

Thanks

References

Details

Primary Language

Subjects

Journal Section

Authors

Publication Date

Submission Date

Acceptance Date

Published in Issue

IZ

Cite