INVESTIGATION OF COMPATIBILITY OF AL5182 SERIES SHEETS WITH DP800 SERIES SHEETS BY CMT METHOD

Yıl 2023, Cilt: 6 Sayı: 2, 59 - 65, 31.12.2023

Öz

In this study, 1 mm thick DP800 (Double Phase) galvanized coated steel sheets used in the production of automotive body and chassis parts were combined with 1.5 mm thick Al 5182 series sheets. These connections were made using the cold metal transfer (CMT) method of gas arc welding. The applied welding position is determined as the overlap. This application was carried out in a fully automatic robotic system using 1 mm diameter aluminum-based ER4043 (AlSi5) filling wire. After joining processes with the cold metal transfer (CMT) method, tensile strength (MPa), bending test, hardness values (HV), macro and micro tests in the joining areas were examined. In conclusion, the maximum breaking strength was reached at 90 amps (Fm: 4.28 kN). It was observed that heat input affected the intermetallic (IMC) phase formation and thickness. In bending tests, the highest breaking force (295 N) was reached at 85 amperes. Negative effects of evaporative galvanization (incomplete melting, pore formation) were observed in Al-DP steel joints. It was observed that the melting of aluminum positively affected the wetting angle in galvanization.

Destekleyen Kurum

Ak-Pres Otomotiv A.Ş.

Proje Numarası

AP.22.005

Teşekkür

Ak-Pres Otomotiv A.Ş.

Kaynakça

  • Schierl, A., The CMT process a revolution in welding technology, Weld. World. 2005
  • Shi, Y., Zhang, G., Huang, Y., Lu, L., Huang, J., Shao, Y., Pulsed double electrode GMAW brazing for joining of aluminum to steel, Weld. J. 2014
  • Shao, L., Shi, Y., Huang, J., Wu, S., Effect of joining parameters on microstructure of dissimilar metal joints between aluminum and galvanized steel, Mater. Des. 2015, 66, 453–458
  • Peyre, P., Sierra, G., Deschaux-Beaume, F., Stuart, D., Fras, G., Generation of aluminium–steel joints with laser-induced reactive wetting, Mater. Sci. Eng. 2007, 444(1-2): 327–338
  • Park, H.J., Rhee, S., Kang, M.J., Kim, D.C., Joining of steel to aluminum alloy by AC pulse MIG welding, Mater. Trans. 2009, 50(9):2314–2317
  • Boumerzoug Z., et al. Fabrication and welding of aluminum composite, The International Journal of Materials and Engineering Technology, 2022, 5(2):71-74
  • Iwase, T., et al., Dissimilar metal joining between aluminum alloy and hot-dip aluminized steel sheet, Kobelco Technol. Rev. 2008:29–34
  • Türkoğlu, R., Aydın, L., & Gültürk, E., Modelıng and Optımum Parameters of CO2 Laser Mıg Hybrıd Weldıng Proces. The International Journal of Materials and Engineering Technology, 2021, 4(2), 91-100
  • Babu, S., Panigrahi, S.K., Ram, G.J., Venkitakrishnan, P.V., Kumar, R.S., Cold metal transfer welding of aluminium alloy AA 2219 to austenitic stainless steel AISI 321. Journal of Materials Processing Technology, 2019, 266:155-164
  • Madhavan, S., Kamaraj M., Vijayaraghavan, L., Microstructure and mechanical properties of cold metal transfer welded aluminium/dual phase steel, Science and Technology of Welding and Joining, 2016, 21(3):194-200
  • Singh, J., Arora, K. S., & Shukla, D. K., Lap weld-brazing of aluminium to steel using novel cold metal transfer process, Journal of Materials Processing Technology, 2020, 283, 116728
  • <https://www.fronius.com/tr-tr/turkey > Dated 11.06.2023
  • Zhang, H., T., Feng, J., C., He, P., Zhang, B.B., Chen, J.M., Wang, L., The Arc Characteristics and Metal Transfer Behaviour of Cold Metal Transfer and Its Use in Joining Aluminium to Zinc-Coated Steel, Materials Science and Engineering. 2009, 499, 111-113
  • Yagati, K.P., Bathe, R.N., Rajulapati, K.V., Rao, K.B.S., Padmanabham, G., Fluxless arc weld-brazing of aluminium alloy to steel. Journal of Materials Processing Technology, 2014, 214(12):2949-2959
  • Medgyesi, T., Popescu, M., Opris, C., Difficulties Encountered in Performing Dissimilar Joints On Sheets, Proceedings of The 22nd International DAAAM Symposium, Vienna, Austria, 2011
  • Gullino, A, Matteis, P, D’Aiuto, F., Review of Aluminum-To-Steel Welding Technologies for Car-Body Applications. Metals; 2019, 9(3): 315.
  • Dong, H., Hu, W., Duan, Y., Wang, X., Dong, C., Dissimilar metal joining of aluminum alloy to galvanized steel with Al–Si, Al–Cu, Al–Si–Cu and Zn–Al filler wires. J. Mater. Process. Technol. 2012, 212, 458–464
  • Su, Y., Hua, X., Wu, Y., Influence of alloy elements on microstructure and mechanical property of aluminum–steel lap joint made by gas metal arc welding, J. Mater. Process. Technol, 2014, 214, 750–755
  • Kobayashi, S., Yakou, T., Control of intermetallic compound layers at interface between steel and aluminum by diffusion-treatment [J]. Materials Science & Engineering A, 2002, 338(1-2):44-53
Yıl 2023, Cilt: 6 Sayı: 2, 59 - 65, 31.12.2023

Öz

Proje Numarası

AP.22.005

Kaynakça

  • Schierl, A., The CMT process a revolution in welding technology, Weld. World. 2005
  • Shi, Y., Zhang, G., Huang, Y., Lu, L., Huang, J., Shao, Y., Pulsed double electrode GMAW brazing for joining of aluminum to steel, Weld. J. 2014
  • Shao, L., Shi, Y., Huang, J., Wu, S., Effect of joining parameters on microstructure of dissimilar metal joints between aluminum and galvanized steel, Mater. Des. 2015, 66, 453–458
  • Peyre, P., Sierra, G., Deschaux-Beaume, F., Stuart, D., Fras, G., Generation of aluminium–steel joints with laser-induced reactive wetting, Mater. Sci. Eng. 2007, 444(1-2): 327–338
  • Park, H.J., Rhee, S., Kang, M.J., Kim, D.C., Joining of steel to aluminum alloy by AC pulse MIG welding, Mater. Trans. 2009, 50(9):2314–2317
  • Boumerzoug Z., et al. Fabrication and welding of aluminum composite, The International Journal of Materials and Engineering Technology, 2022, 5(2):71-74
  • Iwase, T., et al., Dissimilar metal joining between aluminum alloy and hot-dip aluminized steel sheet, Kobelco Technol. Rev. 2008:29–34
  • Türkoğlu, R., Aydın, L., & Gültürk, E., Modelıng and Optımum Parameters of CO2 Laser Mıg Hybrıd Weldıng Proces. The International Journal of Materials and Engineering Technology, 2021, 4(2), 91-100
  • Babu, S., Panigrahi, S.K., Ram, G.J., Venkitakrishnan, P.V., Kumar, R.S., Cold metal transfer welding of aluminium alloy AA 2219 to austenitic stainless steel AISI 321. Journal of Materials Processing Technology, 2019, 266:155-164
  • Madhavan, S., Kamaraj M., Vijayaraghavan, L., Microstructure and mechanical properties of cold metal transfer welded aluminium/dual phase steel, Science and Technology of Welding and Joining, 2016, 21(3):194-200
  • Singh, J., Arora, K. S., & Shukla, D. K., Lap weld-brazing of aluminium to steel using novel cold metal transfer process, Journal of Materials Processing Technology, 2020, 283, 116728
  • <https://www.fronius.com/tr-tr/turkey > Dated 11.06.2023
  • Zhang, H., T., Feng, J., C., He, P., Zhang, B.B., Chen, J.M., Wang, L., The Arc Characteristics and Metal Transfer Behaviour of Cold Metal Transfer and Its Use in Joining Aluminium to Zinc-Coated Steel, Materials Science and Engineering. 2009, 499, 111-113
  • Yagati, K.P., Bathe, R.N., Rajulapati, K.V., Rao, K.B.S., Padmanabham, G., Fluxless arc weld-brazing of aluminium alloy to steel. Journal of Materials Processing Technology, 2014, 214(12):2949-2959
  • Medgyesi, T., Popescu, M., Opris, C., Difficulties Encountered in Performing Dissimilar Joints On Sheets, Proceedings of The 22nd International DAAAM Symposium, Vienna, Austria, 2011
  • Gullino, A, Matteis, P, D’Aiuto, F., Review of Aluminum-To-Steel Welding Technologies for Car-Body Applications. Metals; 2019, 9(3): 315.
  • Dong, H., Hu, W., Duan, Y., Wang, X., Dong, C., Dissimilar metal joining of aluminum alloy to galvanized steel with Al–Si, Al–Cu, Al–Si–Cu and Zn–Al filler wires. J. Mater. Process. Technol. 2012, 212, 458–464
  • Su, Y., Hua, X., Wu, Y., Influence of alloy elements on microstructure and mechanical property of aluminum–steel lap joint made by gas metal arc welding, J. Mater. Process. Technol, 2014, 214, 750–755
  • Kobayashi, S., Yakou, T., Control of intermetallic compound layers at interface between steel and aluminum by diffusion-treatment [J]. Materials Science & Engineering A, 2002, 338(1-2):44-53
Toplam 19 adet kaynakça vardır.

Ayrıntılar

Birincil Dil İngilizce
Konular Kaynak Teknolojileri
Bölüm Articles
Yazarlar

Cihan Yakupoğlu 0000-0003-3596-9623

Ufuk Öztürk 0000-0002-1281-5931

İbrahim Acar 0000-0001-9248-2972

Faruk Varol 0000-0003-2952-2251

Proje Numarası AP.22.005
Erken Görünüm Tarihi 31 Aralık 2023
Yayımlanma Tarihi 31 Aralık 2023
Gönderilme Tarihi 9 Aralık 2023
Kabul Tarihi 26 Aralık 2023
Yayımlandığı Sayı Yıl 2023 Cilt: 6 Sayı: 2

Kaynak Göster

APA Yakupoğlu, C., Öztürk, U., Acar, İ., Varol, F. (2023). INVESTIGATION OF COMPATIBILITY OF AL5182 SERIES SHEETS WITH DP800 SERIES SHEETS BY CMT METHOD. The International Journal of Materials and Engineering Technology, 6(2), 59-65.