The Effect of Aggregate Size and Cure Conditions On The Engineering Properties of Concrete

Abstract

In this study, the effect of curing conditions and aggregate size on the engineering properties of concrete was investigated. Aggregates in the range of 0-8 mm and 0-16 mm were used in concrete production and then cubic samples of 100x100x100 mm were prepared. In the study, slump value of fresh concrete was determined as S3. Three samples were used for each experiment. Compressive strength, abrasion, porosity and carbonation tests were performed on 28-day concrete samples subjected to water and air curing. According to the results obtained, it is determined that concrete samples under the effect of water curing give better results. In addition, better results were obtained for compressive strength, abrasion, porosity and carbonation properties of concrete by increase in aggregate size. It has also been observed that there is an increase in compressive strength of concrete, a positively decrease for abrasion, porosity and carbonation properties.

Keywords

• Concrete
• air cure
• water cure
• slump

References

1. Referans1 Şimşek O. Beton ve beton teknolojisi. Seçkin Yayınları, 5. Baskı. Ankara, 2015.
2. Referans2 Güçlüer K, Günaydın O, Tekin ÖF ve Şahan MF. Farklı tipte agrega kullanımının betonun mekanik özelliklerine etkisinin araştırılması. NÖHÜ Müh. Bilim. Derg. 2017; 6(1), 107-114.
3. Referans3 Özel C. ve Kaplan AN. Kendiliğinden yerleşen beton özellikleri üzerinde agrega özelliklerinin etkisi. USMTD 2017; 1(1), 1-6.
4. Referans4 Usta, S. Agrega Granülometrisinin Beton Bileşimindeki Teorik Malzeme Miktarları ile Betonun Kompasite ve Porozite Değerleri Üzerindeki Etkilerinin İncelenmesi. Yapı teknol. elektron. Derg. 2012; 8(1), 1-15.
5. Referans5 Neville AM. Properties of concrete. London: Longman, 1995.
6. Referans6 Özalp F, Şengül Ö, Taşdemir MA. Kür Koşulları ve Tecrit Malzemesinin Betonun Geçirimlilik ve Mekanik Özeliklerine Etkisi. THBB Derg. 2015; 69-74.
7. Referans7 Özcan F, Atiş CD, Karahan O ve Bilim C. Silis Dumanının ve Kür Şartlarının Harç Basınç Dayanımına Etkisi. 2014; Tam metin bildiri: http://www.imo.org.tr/resimler/ekutuphane/pdf/11143.pdf.
8. Referans8 TS EN 12390-3. Beton - Sertleşmiş beton deneyleri - Bölüm 3: Deney numunelerinin basınç dayanımının tayini. Türk Standartları Enstitüsü, Ankara, 2010.

9. Referans9 ASTM C944/C944M-12 Standard Test Method for Abrasion Resistance of Concrete or Mortar Surfaces by the Rotating-Cutter Method. West Conshohocken, PA; ASTM International, 2012.
10. Referans10 TS EN 12390-6. Beton - Sertleşmiş beton deneyleri - Bölüm 6: Deney numunelerinin yarmada çekme dayanımının tayini. Türk Standartları Enstitüsü, Ankara, 2010.
11. Referans11 Yazıcıoğlu S, Demirel B, Gönen T ve Özer Ş. Farklı tip çimentoların betonun karbonatlaşmasına etkisi. UTBD 2012; 4(3), 112-120.
12. Referans12 Kara C ve Yazicioglu S. Mermer tozu atığı ve silis dumanının betonun karbonatlaşma özelliğine etkisi. Bitlis Eren Univ J Sci 2016; 5(2), 191-202.
13. Referans13 Baradan B ve Aydın S. Betonun Durabilitesi (Dayanıklılık, Kalıcılık). Beton 2013 Hazır Beton Kongresi; 2013; pp. 265-288.