The Properties of Fe3Nb5B12 Based Intermetallic Composites

Yıl 2014, Cilt: 14 Sayı: 3, 381 - 386, 01.12.2014

A. Şükran Demirkıran Yasin Yılmaz Özkan Özdemir Şenol Yılmaz Şaduman Şen Uğur Şen

Öz

In the present study, Fe-Nb-B based intermetallic materials were produced by using as atomical 15% B, 25% Nb and 60% Fe powders. The powders mixed in the attritor for 20 hours were mechanically alloyed, and shaped by uniaxial dry pressing at pressing pressure of 60 MPa. After shaping and drying, these samples were sintered at 1350°C for 120 minutes in controlled atmosphere. Some general properties of intermetallic materials produced by this way were determined by various characterization techniques. Then, these samples were exposed to corrosion test in 0,5 M NaCl. Thus, the corrosion behavior of samples was determined and the corroded surfaces were characterized by SEM. © Afyon Kocatepe Üniversitesi 1. Giriş Klasik öğütme süreçleri ile mümkün olmayan katı halde alaşımlama işlemi yüksek enerjili öğütme ortamı sağlayan atritör ve bazı titreşimli değirmenler ile laboratuar ölçekli değirmenlerde mekanik alaşımlama (MA) ile gerçekleştirilir. Mekanik alaşımlandırılmış tozlardan, alaşım, intermetalik bileşik ve amorf malzemelerin üretilebileceği alternatif bir katı hal tekniğidir. Bu yöntemde, başlangıç tozları defalarca şiddetli bir şekilde deformasyona uğrar, kırılır, parçalanır ve bu parçacıklar başka parçacıklarla birleşir (Sunol et al. 2004)

Anahtar Kelimeler

-

Fe3-Nb5-B12 Esaslı İntermetalik Kompozitlerin Özellikleri

Öz

Bu çalışmada, atomik olarak %15 B, %25 Nb ve %60 Fe tozları kullanılarak Fe-Nb-B esaslı intermetalik malzemeler üretilmiştir. 20 saat süreyle atritörde karıştırılarak mekanik alaşımlama işlemine tabi tutulan toz karışımı, 60 MPa basınç altında tek yönlü olarak preslenip şekillendirilmiştir. Şekillendirme ve kurutma sonrası, 1350°C sıcaklıkta 120 dakika süreyle kontrollü atmosferde sinterleme işlemi ile Fe-NbB esaslı intermetalik malzemelerin üretimi gerçekleştirilmiştir. Daha sonra çeşitli karakterizasyon yöntemleriyle genel özellikleri belirlenen numuneler 0.5 M NaCl ortamında korozyona tabi tutularak korozyon davranışı incelenmiş ve SEM ile korozyon yüzeyleri karakterize edilmiştir.

Anahtar Kelimeler

“Toz Metalurjisi”, “Fe-Nb-B”, “İntermetalik”, “Korozyon”

Kaynakça

• Gloriant, T., Surinach, S. and Baro, M.D., 2004. Stability and crystallization of Fe–Co–Nb–B amorphous alloys, Journal of Non-Crystalline Solids, 333 320–326.
• Hawk, J.A. and Alman, D.E., 1997. Abrasive wear of intermetallic-based alloys and composites, Materials Science and Engineering A, 239–240, 899–906.
• Johnson, D.R, 1999. Intermetallic-based composites, Current Opinion in Solid State and Materials Science, 4, 249–253.
• Park, J.M., Park, J.S., Na, J.H., Kim, D.H. and Kim, D.H., 2006. Effect of Y addition on thermal stability and the glass forming ability in Fe–Nb–B–Si bulk glassy alloy, Materials Science and Engineering A, 435–436, 425– 428.
• Proff, C., Abolhassani, S. and Lemaignan, C., 2011. Oxidation behaviour of binary zirconium alloys containing intermetallic precipitates, Journal of Nuclear Materials, 416 125-134.
• Sunol, J.J., Gonzalez, A., Saurina, J., Escoda, L. And Bruna, P., 2004. Thermal and structural characterization of Fe–Nb–B alloys prepared by mechanical alloying, Materials Science and Engineering A, 375–377, 874–880.
• Yeh, C.L., 2006. Preparation of niobium borides NbB and
• NbB2 by self-propagating combustion synthesis,
• Journal of Alloys and Compounds, 420 (1-2), 111- 116.
• Yoshitomi, K., Nakama, Y., Ohtani, H. and Hasebe, M., 2008. Thermodynamic analysis of the Fe-Nb-B ternary system, ISIJ International, 48 (6) 835-844.