THE EFFECT OF CCA ON THE MECHANICAL PROPERTIES OF ALDER WOOD

Abstract

In this study, it was aimed to determine mechanical properties of alder wood treated with CCA (1, 3 and 10%) and fixed at different temperatures (60  °C, 88°C and 100  °C). Compression strength
parallel to grain and Modulus of Elasticity (MOE) of CCA treated (according to ASTM D 1413) and untreated (control) alder wood samples were investigated according to TS 2474 and TS 2595, respectively. Results shows that compression strength parallel to grain and modulus of elasticity of treated wood samples increased generally while concentration and fixation temperature were increasing

Keywords

• -

CCA’NIN KIZILAĞAÇ ODUNUNUN MEKANİK ÖZELLİKLERİ ÜZERİNE ETKİSİ

Abstract

Bu çalışmada; CCA ile (Bakır/krom/arsenik) %1, %3 ve %10 konsatrasyonlarında  emprenye edilen ve değişen sıcaklıklarda (60  °C, 88  °C ve 100  °C) fiksasyona bırakılan  kızılağaç odunlarının mekanik
özellikleri belirlenmiştir. ASTM D 1413 standardına göre emprenye edilen odun örneklerinde liflere paralel basınç ve statik eğilme direnci TS 2474 ve TS 2595 standartlarında öngörülen şekilde belirlenmiştir. Elde edilen bulgulara göre sıcaklık ve konsantrasyon artışı ile liflere paralel basınç ve statik eğilme dirençlerinde genel bir artış söz konusu olmaktadır. 