NANO-SIZED PIGMENT APPLICATIONS IN İZNİK TILES

Abstract

Traditional İznik tiles are known as “unproducable” due to its high quartz content. İznik tiles contain four different layers as “body, engobe (slip), decors and glaze” and each one has some different starting materials. Recent studies have showed that the production techniques and the particle size of pigments are important parameters in development of colours. TUBITAK MRC and İznik Foundation carried out an experimental work to improve and understand the effects of nanotechnology application to İznik tiles. High quartz content was kept as it is and pigments were applied in decoration as nano-sized pigments. İznik tiles were produced and comparison was carried out between traditional and modern İznik tiles in colour and brightness. Characterization techniques were used in order to understand and compare the results and also the effects of nano-sized pigments to İznik tiles

Keywords

• -

İZNİK ÇİNİLERİNDE NANOMETRE BOYUTLU PİGMENT UYGULAMALARI

Abstract

Geleneksel İznik çinileri, bileşimlerinde bulunan yüksek kuvarstan dolayı “üretilmesi imkansız seramik” olarak bilinmektedir. İznik çinileri; “masse, astar, dekor ve sır” olarak adlandırılan ve her biri ayrı başlangıç malzemelerine ve hazırlanma tekniklerine sahip 4 farklı tabakadan oluşmaktadır. Son çalışmalar, seramiklerin renklerinde, üretim tekniklerinin ve pigment tane boyutlarının önemli parametreler olduğunu göstermiştir. TÜBİTAK MAM ve İznik Vakfı, İznik çinilerine nanoteknoloji uygulamalarının etkisini anlayabilmek için deneysel çalışmalar gerçekleştirmiştir. Yüksek kuvars içeriği değiştirilmeden, dekor aşamasındaki pigmentlerin boyutu nano boyuta indirgenmiştir. Geleneksel ve modern İznik çinileri üretilmiş, renk ve parlaklık özellikleri açısından karşılaştırılmıştır. Nanometre boyutlu pigmentlerin İznik çinilerine etkisinin anlaşılması ve karşılaştırma için karakterizasyon teknikleri kullanılmıştır.

Keywords

• İznik çinileri, Nanoboyutlu pigment, Geleneksel pigment

References

1. Antonic, S.E., Kostic-Gvozdenovic, L., Dimitrijevic, R., Despotovic, S. and Filipovic-Petrovic, L. (1997). Sol-gel method used for synthesis of ceramic pigments, Key Engineering Materials 132-136, 30-33.
2. Arcasoy, A. (1983). Ceramic Technology, Marmara University, Fine Arts Faculty, Ceramics Department Publication 277, (in Turkish).
3. Balogh, A. (1997). High stability ceramic pigments, Key Engineering Materials 132-136, 97-100.
4. Biswas, S.K., Dhak, D.D., Patnak, A. and Pramanik, P. (2008). Chemical synthesis of environment-friendly nanosized yellow titanate pigments, Materials Research Bulletin 43, 665-675.
5. Cavalcante, P.M.T., Dondi, M., Guarini, G., Raimondo, M. and Baldi, G. (2009). Colour performance of ceramic nano- pigments, Dyes and Pigments 80, 226- 232.
6. Ishbel, G., Jones, R. and Airey, T. (1997). CERAM.