CHEMICAL DURABİLİTY OF SOME GLASSES IN HYDROCYLORIC ACID SOLUTİON
Abstract
Chemical durability of some sodium silîcate and sodium boro-silicate glasses in 0.1 N hydrochloric acid solution was studied. The raw materials used were ali of cheınicaliy püre grade and were fincly pulverised. AH nıelts were made in Pt- 2% Rh crucibles in gas furnaces. The temperature of melting ranged from 1400 to 1600°C for four hours. After çomplete melting, the molten glass was annealed at the appropriate temperature; and then the glass was ground usirg agate mortar. AH the measurements of the Chemical durability of the glass powder for each glass sample, was carried out in the usual way using 0.1 N HC1 solution as the immersion solution. The experimental results obtained revealed that the change in the weight loss with the gradual inc- rease of the soda content was attributed to the corrosion rate.
Keywords
References
- CHEMICAL DURABİLİTY OF SOME GLASSES IN HYDROCYLORIC ACID SOLUTİON
Details
Primary Language
English
Subjects
Chemical Engineering
Journal Section
Research Article
Authors
Z.a. El-hadı
This is me
Türkiye
Publication Date
January 1, 1991
Submission Date
January 1, 1990
Acceptance Date
-
Published in Issue
Year 1970 Volume: 37