Bonding Characteristics of Low-Fusing Porcelain Bonded to different Dental Alloys

Abstract

The aim of this study was to investigate the bond compatibility between porcelain-titanium and base metal alloys-porcelain, by using three point bending test. The ceramometal bond strength was evaluated according to DIN draft 13927 with three point bending test. Fractured surfaces of the metal and porcelain were examined macroscopically. The 60 cast plates 25 mmX5 mmX0.4 mm of each group were prepared. A uniform thickness of 1 mm of porcelain was applied along an 8 mm length in the central portion of the metal specimens. The firing schedules followed the recommendations given by the manufacturers. Testing the bond strengths of specimens was performed with a t hree point flexural device on Instron universal testing machine with a span distance of 20 mm. and the load of bond failure was recorded and statically analyzed Instron Corp., Canton, Mass . The bond strength of Base metal alloy/Vita Omega porcelain was significantly greater than low fusing porcelain groups. The bending strength of all groups was found to be within the acceptable standard levels 25N/mm2 . There was no significant difference in the bond strength of low fusing porcelain to different metal alloys.

Keywords

• Low-fusing porcelain, dentalalloys, ceramometal bonding

FARKLI DENTAL ALAŞIMLARI ÜZERİNE HAZIRLANAN DÜŞÜK ISI PORSELENLERİNİN BAĞLANTI KARAKTERİZASYONU

Abstract

Bu çalışmanın amacı, öncelikle titanyum ilekullanım amacı ile geliştirilmiş olan düşük ısıporselenlerinin farklı metal ve alaşımları ile olanbağlantı karakterizasyonunun incelenmesidir.Bunun için, DIN 13927 no’lu standartlara uygunolarak 25mm x 5mm x 0.4 mm boyutlarındaki özelbir kalıp yardımıyla toplam 60 adet metal alt yapıhazırlanmıştır. Hazırlanan metal alt yapılardan 12tanesi altın alaşımı, 36 tanesi temel metal alaşımı,kalan 12 tanesi de titanyum olacak şekilde düzenlenmiştir.Daha sonra bu alt yapıların merkezine 8 mmuzunluğunda, 5 mm genişliğinde ve 1 mmkalınlığında porselen yığılmasını temin edecekşekilde iki parçalı metal bir kalıp sayesinde metalalt yapıların üzerine uygun porselen tozları kondanse edilerek hazırlanan örnekler fırınlama işlemine tabi tutulmuştur. Hazırlanan örnekler Lloyduniversal test cihazında üç nokta yükleme testinetabii tutulmuş ve porselen kısım ortada ve alttakalacak şekilde örnek iki destek arasına yerleştirilmiştir. Daha sonra metal üzerinden, porselenin tamorta noktasına gelecek şekilde sabit bir hızla yükleme yapılmıştır. Sonuç olarak; temel metalalaşımı-Vita porseleni, diğer dört gruba göre düşük ısı porselenleri anlamlı derecede yüksekbağlantı direncine sahiptir. Düşük ısı porselenleriarasında ise bağlantı direnci açsından istatistikselolarak belirgin bir fark saptanmamıştır

Keywords

• Düşük ısı porselenleri, Dental alaşımlar, Metal-porselen bağlantı dayanıklılığı

References

1. Kimura H, Horng C, Okazaki M, Takahashi J. Thermal compatibility of titanyum-porcelain sys- tem. J. Osaka Univ. Dent. Sch. 1990; 30: 43-52.
2. Mclean JW, Hughes H. The reinforcement of dental porcelain with ceramic oxides. Br. Dent. J. 1965; 119: 251-67.
3. O’brien WJ. Dental materials: Properties and selection. Chicago, Quintessence Pub. Co. Inc. 1989; p: 413-546.
4. Derand T, Hero H. Bond strength of porce- lain on cast vs. wrought titanium. Scand. J. Dent. Res. 1992; 100: 184-8.
5. Hautaniemi JA, Hero H. Effect of crystalline leucite on porcelain bonding on titanium. J. Am. Ceram. So. 1991; 74: 1449-51.
6. Hautaniemi JA, Hero H. On the bonding of porcelain on titanyum. J. Material. Science. 1992; 3: 186-91.
7. Luthy H. Titanium: Material science aspects. 1stinformation meeting on titanium in d entistry. Geneva, Conference abstracts, 1994: p: 31-45.
8. Bagby M, Marshall SJ, Marshall GW. Metal ceramic compatibility: A review of the literature. J. Prosthet. Dent. 1990; 63: 21-5.

9. International Standart/ISO 9693. Metal- ceramic bond charecterization. 1999; p. 1-11.
10. Deutsches Institut Fur Normung. DIN 13927. Metall-keramik Systeme. Beuth Verlag. Berlin, 1990; p: 1-10.
11. Gilbert JL, Covey DA, Lautenschlager EP. Bond characteristics of porcelain fused to milled tita- nium. Dent Mater. 1994; 10: 134-40.
12. Boenineg KW, Walter MH, Repel PD. Non- cast titanium restorations in fixed prosthodontics, J Oral. Rehabil. 1992; 19: 281-7.
13. Hegehbarth EA. Ceramic veneering of titanyum-Procedures and esthetic considerations 1st Information Meeting on Titanyum in Dentistry. Geneva. Conference Abstracts. 1984; p: 103-6.
14. Pang IC, Gilbert JL, Chai J, Lautenschlager EP. Bonding characteristics of low-fusing porcelain bonded to pure titanyum and palladium-copper alloy. J. Prosthet. Dent. 1995; 73: 17-25.
15. Edwards MR, Jacobsen PH. Williams GJ. The three-point beam test for the evaluation of den- tal porcelain. J. Dent. Res. 1983; 60: 815-9
16. Pröbster L, Maiwald U, Weber H. Three- point bending strength of ceramics fused to cast titanyum. Eur J. Oral. Sci. 1996; 104: 313-9.
17. Yılmaz H, Dinçer C. Comparison of the bond compatibility of titanium and an NiCr alloy t o dental porcelain. Journal of dentistry. 1999; 27: 21 5- 22.
18. Aschl I, Rammelsberg P, Pospiech P, Gernet W. Bond strength of low-fusing ceramic to casted titanium. J. Dent. Res. 1998; (IADR Abstracts) 77: 941.
19. Baez R, Blackman R, Serrano C. Strength of low-firinge porcelains using three test modes. J. Dent. Res. 1997; (IADR Abstract) 76: 62.
20. Mutawa NJA, Sato T, Shğiozawa I, Hasegawa S, Miura H. A study of bond strength and color of ultralow-fusing porcelain. Int J. Prosthodont. 2000; 13: 519-25.