Investigation on the corrosion resistances of bronze-waste tire-concrete composites

Year 2019, Volume: 3 Issue: 3, 189 - 194, 15.12.2019

Tuba Bahtlı , Nesibe Sevde Ozbay

https://doi.org/10.35860/iarej.630895

Abstract

In this study, finely ground
CuAl10Ni bronze sawdust and waste tire additives were incorporated into C30
concrete at different amounts and then their corrosion resistances were
investigated. SEM/EDX analyses were performed. It was observed that after acids
attacks, as the waiting time in the acid solutions increased, electrical
surface resistance values increased due to further corrosion. Also, more losses
in the weight were observed in the pure concrete than the concretes including
bronze sawdust and waste tire grains, then those refractories showed higher
corrosion resistances than that of pure concrete.

Keywords

Bronze sawdust, Composite, Concrete, Corrosion, Waste tire

Project Number

171351001

References

• 1. Liu, T., Weyers, W., Modeling the Dynamic Corrosion Process in Chloride Contaminated Concrete Structures. Cement and Concrete Research, 1998. 28(3): p. 365-379.
• 2. Fang, C., Lundgrenb, K., Chena, L., Zhua, C., Corrosion Influence on Bond in Reinforced Concrete. Cement and Concrete Research, 2004. 34: p. 2159–2167.
• 3. Cabrera, J. G., Deterioration of Concrete Due to Reinforcement Steel Corrosion. Cement & Concrete Composites, 1996. 18: p. 47-59.
• 4. Guerrero, A. M. A., Robayo-Salazar, R. A., Mejía de Gutiérrez, R., A Novel Geopolymer Application: Coatings to Protect Reinforced Concrete Against Corrosion. Applied Clay Science, 2017. 135: p. 437–446.
• 5. Elsener, B., Büchler, M., Stalder, F., Böhni H., Migrating Corrosion Inhibitor Blend for Reinforced Concrete: Part 1—Prevention of Corrosion. Corrosion,1999. 55(12): p. 1155-1169.
• 6. Song, H.W., Saraswathy, V., Corrosion Monitoring of Reinforced Concrete Structures – A Review. International Journal of Electrochemical Science, 2007. 2: p. 1- 28.
• 7. Thomas, B. S., Gupta, R. C., Panicker, V. J., Recycling of waste tire rubber as aggregate in concrete:durability-related performance. Journal of Cleaner Production, 2016. 112(1): p. 504-513.
• 8. Oikonomou, N., Mavridou, S., Improvement of chloride ion penetration resistance in cement mortars modifiedwith rubber from worn automobile tires. Cement & Concrete Composites, 2009. 31: p. 403–407.
• 9. Yung, W. H., Yung, L. C., Hua L. H., A study of the durability properties of waste tire rubber appliedto self-compacting concrete. Construction and Building Materials, 2013. 41: p. 665-672.
• 10. Dermaj, A., Hajjaji, N., Joiret, S. ,. Rahmouni, K., Srhiri, A., Takenouti, H., Vivier, V., Electrochemical and spectroscopic evidences of corrosioninhibition of bronze by a triazole derivative. Electrochimica Acta, 2007. 52: p. 4654–4662.
• 11. Goffer, Z., Archaeological Chemistry, 2007, A John Wiley & Sons, Inc Publication, , p. 193-197.