Investigation of mechanical properties of AL5083 plates joined by MIG and TIG welding at different amperage values

Abstract

One of the most commonly used metals in the industrial industry is aluminum. After the production of aluminum metal, it is important to combine them with each other for industrial use. Aluminum metals can be combined with each other with different welding methods. In this study, AL5083 plate was combined with different welding parameters using MIG and TIG welding methods. Tensile test and bending test were applied to the materials joined by welding. As a result of the study, when the tensile test results for 5083 series aluminum alloy were examined, the maximum tensile strength was obtained at 90 amperes for MIG welding and 100 amperes for TIG welding. After the tensile test, rupture in butt joints occurred in the region under the influence of heat or in the weld region. According to the bending test results, we see that many test pieces broke from the weld region. As a result, the optimum welding parameters were determined in the joining of AL5083 plate with MIG and TIG welding with this study.

Keywords

• Al5083
• Tensile, bend test
• MIG
• TIG
• Welding

Farklı amper değerlerinde MIG ve TIG kaynağı ile birleştirilen AL5083 plakaların mekanik özelliklerinin incelenmesi

Abstract

Sanayi endüstrisinde en çok kullanılan metallerden biri de alüminyumdur. Alüminyum metalinin üretiminden sonra endüstriyel olarak kullanımı için birbirleriyle birleştirmeleri önem arz etmektedir. Alüminyum metalleri birbirleriyle farklı kaynak yöntemleriyle birleştirilebilmektedir. Bu çalışmada, AL5083 plaka MIG ve TIG kaynak yöntemleri kullanılarak farklı kaynak parametrelerinde birleştirilmiştir. Kaynakla birleştirilen malzemelere çekme deneyi, eğme deneyi uygulanmıştır. Çalışma sonucunda, 5083 serisi alüminyum alaşımı için çekme deneyi sonuçları incelendiğinde MIG kaynağı için 90 amperde, TIG kaynağı için 100 amper değerinde maksimum çekme dayanımı elde edilmiştir. Çekme testi sonrası alın birleştirmelerinde kopma, ısı tesiri altında kalan bölge veya kaynak bölgesinde meydana gelmiştir. Eğme deneyi sonuçlarına göre ise birçok deney parçasının kaynak bölgesinden kırıldığını görmekteyiz. Sonuç olarak bu çalışma ile AL5083 plakanın MIG ve TIG kaynağı ile birleştirilmesinde optimum kaynak parametreleri belirlenmiştir.

Keywords

• Al5083
• Çekme, eğme testi
• MIG
• TIG
• Kaynak

References

1. Ertürk, İ. (1994). MIG-MAG kaynak yönteminde kaynak parametrelerinin sıçrama kayıplarına etkilerinin incelenmesi. Doktora tezi, Gazi Üniversitesi, Ankara.
2. Ertemiz, M. (2005). Östenitik paslanmaz çeliklerin TIG kaynak yöntemi ile birleştirilmesi ve mekanik özelliklerinin incelenmesi. Yüksek lisans tezi, Sakarya Üniversitesi.
3. Eryürek, İ. (2007). Çelikler için elektrod seçimi. İstanbul: As Kaynak. Katnam, K.B., Da Silva, L., and Young, T. (2013) Bonded repair of composite aircraft structures: A review of scientific challenges and opportunities, Progress in Aerospace Sciences, 61: 26-42.
4. Eryürek, İ. B. (2007). Gazaltı ark kaynağı. İstanbul: Askaynak Yayınları.
5. Madavi, K. R., Jogi, B. F., & Lohar, G. S. (2022). Metal inert gas (MIG) welding process: A study of effect of welding parameters. Materials Today: Proceedings, 51, 690-698.
6. Anık, S. ve Tülbentçi, K. (1991). Örtülü elektrot ile ark kaynağı. İstanbul: Gedik Holding Yayınları
7. Anık, S. ( 1991). Kaynak tekniği el kitabı. İstanbul: Gedik Eğitim Vakfı.
8. Jeyaprakash, N., Haile, A., & Arunprasath, M. (2015). The parameters and equipments used in TIG welding: A review. The International Journal of Engineering and Science (IJES), 4(2), 11-20.

9. Kilerci, İ. (2011). Titanyum alaşımlarının farklı kaynak yöntemleriyle kaynağının incelenmesi. Y. Lisans Tezi), Celal Bayar Üniversitesi Fen Bilimleri Enstitüsü, Manisa.
10. Gunay, A., Fank, S., Gulmez, T., & Durakbasa, N. M. (2013). Calculation of measurement uncertainty for plastic (ABS) material in flexural testing. International Journal of Metrology and Quality Engineering, 4(1), 29-33.
11. Sachin, L.S., Mayur, S., Pavan, K.M., Chandrashekar, A. & Ajaykumar, B.S. (2014). Evaluation of Structural and Mechanical Properties of TIG Welded Aluminium Alloy AA5083 Subjected to Post Cryogenic Treatment. The Research Pubblications, 3(2),14–18.
12. Fauzi, E.R.I., Jamil, M.S., Samad, Z. & Muangjunburee, P. (2017). Microstructure analysis and mechanical characteristics of tungsten inert gas and metal inert gas welded AA6082-T6 tubular joint: A comparative study. Transactions of Nonferrous Metals Society of China, 27, 17–24. https://doi.org/10.1016/S1003-6326(17)60003-7