Optimization of Process Prarameters for Porous Artificial Bone

Abstract

In this study, porous artificial bone from hydroxyapatite was fabricated usind garbonyl diamide space fille. In porous bioceramics applications has low mechanical properties, therefore new developments are required on production of porous ceramics. İn this study, calcium-phosphate in hydroxyapatite from (Nanotech Co. in Eskişehir) and carbonyl diamide balls in 50% rati were used to prepare the powder. To optimize the fabrication, sintering temperatures (950 ℃, 1050 ℃, 1150 ℃) and time (1-5h) wereoptimse to enhance the mechnical properties of porou ceramics. Afte sintering, pore size and microstructure of the samples were analyzed with scanning microsopy. Porous samples  were tested with compression test. From the results compressive strenght were changged between 1.2 MPa to 11 MPa depends on the process parameters.

Keyword- artificial bone, hydroxyapatite, sintering, porous, comprerssion

Keywords

• artificial bone,hydroxyapatite,sintering,porous

References

1. [1] Şevki Yılmaz GÜVEN, ''Biyouyumluluk ve biyomalzemelerin seçimi'', Süleyman Demirel Üniversitesi Mühendislik Bölümü ÖS: BiyoMekanik, 303-311, 2014 ISSN: 1308-6693, 2014
2. [2] Övül Kümbüloğlu ''Biyomateryaller''. Ege Üniversitesi Diş Hekimliği Fakültesi, Derg 2013; 34 (1): 27-33, 2013
3. [3] Feza Korkusuz, Pelek Korkusuz: ''Kalsiyum hidroksiapatit seramiklerin ortopedide kullanımı'', Acta Ortop Traumatol Turc 31 : 63-67, 1997
4. [4] Zafer Evis. ''Çeşitli İyonlar Eklenmiş Nano-Hidroksiapatitler: Üretim Yöntemleri, İç Yapı, Mekanik ve Biyouyumluluk Özellikleri Yönlerinden İncelenmesi''. Engineering Sciences Department, Middle East Technical University, Ankara, 06531, Turkey
5. [5] Pasinli, A.,'' Biyomedikal Uygulamalarda Kullanılan Biyomalzemeler'', Ege Üniversitesi Ege Meslek Yüksekokulu, Makine Programı 35100 Bornova / İZMİR, Makine Teknolojileri Elektronik Dergisi, (4) 25-34, 2004.
6. [6] Kaya GÜR, Mustafa TAŞKIN,'' Metalik Biyomalzemeler ve Biyouyum'' Fırat Üniversitesi, Teknik Eğitim Fakültesi, Metal Bölümü-ELAZIĞ. 2004.
7. [7] Ahmet PASINLI, R. Sami AKSOY, ''Yapay Kemik Uygulamaları İçin Hidroksiapatit'', Ege Universitesi, Ege Meslek Yuksekokulu, Makine Programı, 35100, Bornova, İzmir, 2010.
8. [8] Soner ÇAKMAK, ''Kemik Doku Onarimi için Hidroksiapatit/Peptit Amfifil Bazli Nanokompozit Doku İskelelerinin Geliştirilmesi'', Hacettepe Üniversitesi. Doktora Tezi, 2015

9. [9] Yıldız ÖZALP, Nurten ÖZDEMİR. ''Biyomateryaller ve biyouyumluluk''. Ankara Üniversitesi. Eczacılık Fakültesi, Farmasötik Teknoloji Anabilim Dalı 06100 - Tandoğan / Ankara Yayın Tarihi: 1996 Sayı: 2 Cilt: 25 Yayınlandığı Sayfalar: 057-072Yayın Niteleme Bilgileri: 1015-3918
10. [11] Feza Korkusuz, Emre Tomin, Duran N. Yetkinler, Muharrem Timuçin, Abdullah Öztürk,Petek Korkusuz, ''Yapay kemik dokusu''. Orta Doğu Teknik Üniversitesi, TOTBİD Dergisi 2011;10(2):134-142, 2011.
11. [12] Pang, Y.X., Bao, X. ''Influence of temperature, ripening time and calcination on the morphology and crystallinity of hydroxyapatite nanoparticles,'' Journal of the European Ceramic Society, 23, 1697-704. 2003.