EFFECT OF EPOXY RESIN BASED ROOT CANAL SEALER CONTAMINATED IN THE BONDING OF COMPOSITE RESIN TO DENTIN-Epoksi Reçine Bazlı Kök Kanal Patı Kontaminasyonunun Kompozit Reçinenin Dentine Bağlanması Üzerine Etkisi

Abstract

ABSTRACT

Purpose: The effect of precleansing procedures for epoxy resin-based root canal sealer contaminated dentin surfaces for the evaluation of bond strength of a composite resin to dentin.

Material and Methods: Twenty-five extracted intact human molar crowns were prepared longitudinally on 4 sides (mesial, distal, buccal, and lingual) to produce flat dentin surfaces (25 teeth x 4 surfaces = 100 specimens) for bonding. Group A, B, C, and D were contaminated with sealer for 15 minutes; Group E was not contaminated. After contamination, Group A was cleaned with a dry cotton pellet, Group B was cleaned with 25% ethanol, Group C was cleaned with a dry cotton pellet and left for 3 days (to allow the sealer remnant polymerization), and Group D was cleaned with ethanol and left for 3 days. Composite resin specimens bonded to all the dentine specimens and loaded for shear bond strength.

Results: There were no significant difference among the groups (p=0.368).

Conclusion: Use of ethanol cleansing on epoxy-resin sealer contaminated surfaces before Clearfill SE Bond use had no positive effect on bonding strength of adhesive restoration.

Keywords: Adhesive, epoxy resin root canal sealer, contamination, bond strength

ÖZ

Amaç: Epoksi reçine bazlı kök kanal patı kontaminasyonunun kompozit reçinenin dentine bağlanması üzerine etkisinin değerlendirilmesi.

Gereç ve Yöntem: Yirmi beş adet çekilmiş çürüksüz insan molar dişi düzgün bağlama yüzeyleri elde etmek için dört tarafından (meziyal, distal, bukkal ve lingual) kesildi (25 diş x 4 yüzey = 100 örnek). Grup A, B, C ve D pat ile kontamine edildi; Grup E kontamine edilmedi. Kontaminasyon sonrasında Grup A kuru pamuk pelet ile temizlendi, Grup B %25'lik etanol ile temizlendi, Grup C kuru pamuk pelet ile temizlenip 3 gün bekletildi (pat kalıntılarının polimerizasyonu için) ve Grup D %25'lik etanol ile temizlenip 3 gün bekletildi. Kompozit reçine örnekleri dentin örnekleri üzerine uygulandı ve üniversal bir test cihazı ile yüke tabi tutuldu.

Bulgular: Gruplar arasında anlamlı fark yoktu (p=0.368).

Sonuç: Epoksi reçine bazlı kök kanal patı kontaminasyonunun kompozit reçinenin dentine bağlanma dayanımını azaltmadığı belirlendi.

Anahtar kelimeler: Adezif, epoksi reçine kök kanal patı, kontaminasyon, bağlanma dayanımı

Keywords

• Adhesive, epoxy resin root canal sealer, contamination, bond strength

Epoksi Reçine Bazlı Kök Kanal Patı Kontaminasyonunun Kompozit Reçinenin Dentine Bağlanması Üzerine Etkisi

Abstract

Amaç: Epoksi reçine bazlı kök kanal patı kontaminasyonunun kompozit reçinenin dentine bağlanması üzerine etkisinin değerlendirilmesi.Gereç ve Yöntem: Yirmi beş adet çekilmiş çürüksüz insan molar dişi düzgün bağlama yüzeyleri elde etmek için dört tarafından (meziyal, distal, bukkal ve lingual) kesildi (25 diş x 4 yüzey = 100 örnek). Grup A, B, C ve D pat ile kontamine edildi; Grup E kontamine edilmedi. Kontaminasyon sonrasında Grup A kuru pamuk pelet ile temizlendi, Grup B %25’lik etanol ile temizlendi, Grup C kuru pamuk pelet ile temizlenip 3 gün bekletildi (pat kalıntılarının polimerizasyonu için) ve Grup D %25’lik etanol ile temizlenip 3 gün bekletildi. Kompozit reçine örnekleri dentin örnekleri üzerine uygulandı ve üniversal bir test cihazı ile yüke tabi tutuldu. Bulgular: Gruplar arasında anlamlı fark yoktu (p=0.368).Sonuç: Epoksi reçine bazlı kök kanal patı kontaminasyonunun kompozit reçinenin dentine bağlanma dayanımını azaltmadığı belirlendi.

Keywords

• Adezif, epoksi reçine kök kanal patı, kontaminasyon, bağlanma dayanımı

References

1. Vire DE. Failure of endodontically treated teeth: classification and evaluation. J Endod 1991;17(7):338-42.
2. Trope M, Elfenbein L, Tronstad L. Mandibular premolars with more than one root canal in different race groups. J Endod 1986;12(8):343-5.
3. Trope M, Maltz DO, Tronstad L. Resistance to fracture of restored endodontically treated teeth. Endod Dent Traumatol 1985;1(3):108-11.
4. Inoue S, Pereira PN, Kawamoto C, Nakajima M, Koshiro K, Tagami J, Carvalho RM, Pashley DH, Sano H. Effect of depth and tubule direction on ultimate tensile strength of human coronal dentin. Dent Mater J 2003;22(1):39-47.
5. Sattabanasuk V, Shimada Y, Tagami J. The bond of resin to different dentin surface characteristics. Oper Dent 2004;29(3):333-41.
6. Korkmaz Y, Baseren M. Effect of antibacterial varnishes applied to root dentin on shear bond strength of toothcolored restorative materials. Oper Dent 2008;33(1):65-71. de Castro FL, de Andrade MF, Duarte Junior SL, Vaz LG, Ahid FJ. Effect of 2% chlorhexidine on microtensile bond strength of composite to dentin. J Adhes Dent 2003;5(2):129-38.
7. Hansen EK, Asmussen E. Influence of temporary filling materials on effect of dentin-bonding agents. Scand J Dent Res 1987;95(6):516-20.
8. Altintas SH, Tak O, Secilmis A, Usumez A. Effect of provisional cements on shear bond strength of porcelain laminate veneers. Eur J Dent 2011;5(4):373-9.

9. Macchi RL, Capurro MA, Herrera CL, Cebada FR, Kohen S. Influence of endodontic materials on the bonding of composite resin to dentin. Endod Dent Traumatol 1992;8(1):26-9.
10. Saraç D, Bulucu B, Saraç YS, Kulunk S. The effect of dentin-cleaning agents on resin cement bond strength to dentin. J Am Dent Assoc 2008;139(6):751-8.
11. Kuphasuk W, Harnirattisai C, Senawongse P, Tagami J. Bond strengths of two adhesive systems to dentin contaminated with a hemostatic agent. Oper Dent 2007;32(4):399-405.
12. Arslan S, Ertaş H, Zorba YO. Influence of Ankaferd Blood Stopper on shear bond strength of bonding systems. Dent Mater J 2012;31(2):226-31.
13. Itoh T, Fukushima T, Inoue Y, Arita S, Miyazaki K. Effect of water, saliva and blood contamination on bonding of metal brackets with a 4-META/MMA/ TBB resin to etched enamel. Am J Dent 1999;12(6):299-304.
14. Raffaini MS, Gomes-Silva JM, TorresMantovani CP, Palma-Dibb RG, Borsatto MC. Effect of blood contamination on the shear bond strength at resin/dentin interface in primary teeth. Am J Dent 2008;21(3):159-62.
15. Abdalla AI, Davidson CL. Bonding efficiency and interfacial morphology of onebottle adhesives to contaminated dentin surfaces. Am J Dent 1998;11(6):281-5. de Carvalho Mendonça EC, Vieira SN, Kawaguchi FA, Powers J, Matos AB. Influence of blood contamination on bond strength of a self-etching system. Eur J Dent 2010;4(3):280-6. Corresponding Author: Hüseyin ERTAŞ Department of Endodontics, Faculty of Dentistry, Izmir Katip Celebi University, Izmir, Turkey. Tel: [phone] e-mail: [e-mail]