The Effects of Exposed to Sea Water Steam on Thermal Conductivity of Varnished Fir Wood

Year 2012, Volume: 12 Issue: 3 , 217 - 220 , 01.09.2012

Raşit Esen Cemal Özcan Erkan Likos Osman Emre Özkan

https://izlik.org/JA34WL64NU

Abstract

Keywords

-

The Effects of Exposed to Sea Water Steam on Thermal Conductivity of Varnished Fir Wood

https://izlik.org/JA34WL64NU

Abstract

In this study, the thermal conductivity of varnished fir wood exposed to sea water steam was investigated. For this purpose, test samples were coated by using varnishing goldspar (polyurethane varnish), original (synthetic varnish), perfection (polyurethane varnish), and schooner varnishes (synthetic varnish). After applying furnished process, samples were exposed to sea water steam during 6, 24, 60, and 96 hours. It was found that the vapour application has decreased the chemical and physical structure of test material. The thermal conductivity test was performed based on the ASTM C 1113-99 hot-wire method

Keywords

-

References

• Simpson, W., TenWolde, A. 1999. Physical Properties and Moisture Relations of Wood, Wood handbook, chapter 3, Madison.
• Desch, H.E. and J.M. Dinwoodie. 1996. Timber: structure, properties, conversion and use. MacMillan Press Ltd., London.
• Williams, R.S., Feist, C.W. 1993. Durability of Paint or Solid–Color Stain Applied to Preweathered Wood, Forest Product Journal, Vol. 43, No: 1.
• Grantham, J.B. Black, J.M. Heebink, T.B. Mraz, E.A. 1976. Natural Exterior Finishes for Wood in the Pacific Northwest, Forest Product Journal, Vol. 26, No: 8.
• Akza Nobel International. 2011. 35730 Kemalpaşa, İzmir, Turkey.
• TS 2471. 1976. Wood, Determination of Moisture Content for Physical and Mechanical Tests, TSE Standards, Turkey.
• TS 2472. 1976. Wood - Determination of Density for Physical and Mechanical Tests, TSE Standards, Turkey.
• ASTM D-3024, 1998. Standard Practice for Determination of Resistance of Factory Applied Coatings on Wood Products of Stain and Reagents.
• ASTM C1113-99. 2004. Standard Test Method for Thermal Conductivity of Refractories by Hot Wire (Platinum Resistance Thermometer Technique).
• ASTM C 177/C 518. 2004. Methods of Measuring Thermal Conductivity, Absolute and Reference Method.