Mechanical and microstructural characterization of rubber particle reinforced thermoplastic for automobile bumper application
Abstract
Thermoplastic elastomer composite produced from low-density polyethylene (LD-PE) mixed with 150μm pulverised rubber particles in varied proportions (5%, 10%, 15%, 20% and 25%) using stir casting technique was characterized for mechanical properties in relation to the base polyethylene. Tensile, impact, flexural, and hardness tests were conducted to investigate the mechanical properties of the elastomer. The results obtained showed that the reinforcement with up to 20%wt of pulverised rubber particle generated a composite with a higher modulus of elasticity of 374MPa and hardness of 14.06BHN relative to those of the base material which are 227MPa and 11.48BHN respectively. However, the bending strength and the impact energy of the generated composite are 40MPa and 19.5J, which are lower than those of the base material, which are 57MPa and 20J. This may be due to insufficient adhesion between the phases of the matrix and reinforcement.
Keywords
References
- [1]. Egodage SM, Harper JF, Walpalage S. "The development of rubber-thermoplastic blends from ground tyre rubber and waste polypropylene", J Natl Sci Found Sri Lanka (2009), 37.
- [2].Hrdlicka Z, Kuta A, Hajek J. "Thermoplastic elastomer blends based on waste rubber and low-density polyethylene", Polimery, 55, (2010), 832–8.
- [3]. Michael H, Scholz H, Mennig G. "Blends from recycled rubber and thermoplastics", Kautschuk Gummi Kunststoffe, 52, (1999), 510–3.
- [4]. Mennig G, Michael H, Rzymski WM, Scholz H. "Thermoplastic elastomers from polypropylene-powdered rubber scrap blends", Polimery, 42, (1997), 491–3.
- [5]. Zhang ZX, Zhang SL, Kim JK. "Evaluation of mechanical, morphological and thermal properties of waste rubber tire powder/LLDPE blends", E-Polymers (2008), 8.
- [6]. Guo B, Cao Y, Jia D, Qiu Q. "Thermoplastic Elastomers .Derived from Scrap Rubber Powder/LLDPE Blend with LLDPE‐graft‐(Epoxidized Natural Rubber) Dual Compatibilizer", Macromol Mater Eng, 7, (2004), 289-360.
- [7]. Tolstov A, Grigoryeva O, Fainleib A, Danilenko I, Spanoudaki A, Pissis P, et al. Reactive Compatibilization of Polyethylene/Ground Tire Rubber Inhomogeneous Blends via Interactions of Pre‐Functionalized Polymers in Interface. Macromol. Symp., vol. 254, Wiley Online Library; (2007), 226–32.
- [8]. Li Y, Zhang Y, Zhang Y. "Mechanical properties of high‐density polyethylene/scrap rubber powder composites modified with ethylene–propylene–diene terpolymer, dicumyl peroxide, and silicone oil", J Appl Polym Sci, 88, (2003), 2020–7.
- [9]. Naskar AK, De SK, Bhowmick AK. "Thermoplastic elastomeric composition based on maleic anhydride–grafted ground rubber tire", J Appl Polym Sci, 84, (2002), 370–8.
- [10]. Kumar CR, Fuhrmann I, Karger-Kocsis J. "LDPE-based thermoplastic elastomers containing ground tire rubber with and without dynamic curing", Polym Degrad Stab, 76, (2002), 137–44.