THE INVESTIGATION OF ULTRASONIC AND DEPTH OF PENETRATION OF WATER ON ADDITION CONCRETES

Abstract

In this study, the effect of fly ash and silica fume on the permeability and compressive of C20 and C30 concretes was imvestigation. The cement proportion in concrete samples was reduced %10 and was it replaced with fly ash and silica fume. Depth of penetration of water and ultrasonic tests were performed on 24 cube samples having 150x150x150 mm dimension at 28 th and 90 th days respectively; these results were compared with reference samples. As a result, sample of silica fume additive showed best performance for both C20 and C30 classes.

Keywords

• Permeability, Portland cement, Silica fume, Fly Ash, Ultrasonic,

MİNERAL KATKILI BETONLARDA ULTRASES GEÇİŞ HIZI İLE SU İŞLEME DERİNLİĞİNİN DEĞERLENDİRİLMESİ

Abstract

Bu çalışmada, uçuçu kül ve silis dumanı katkılı C20 ve C30 betonlarında ultrases geçiş hızının geçirimlilik üzerine etkileri araştırılmıştır. Beton örnekleri çimento miktarının ağırlıkça %10'ar oranında uçucu kül ve silis dumanı ikame edilerek üretilmiştir. 150x150x150 mm boyutlarında üretilen 24 adet küp örnek üzerinde 28. ve 90. günlerde su işleme derinliği deneyi ve ultrases deneyleri gerçekleştirilerek referans örneklerle karşılaştırılmıştır. Sonuçta C20 ve C30 sınıflarında, ultrases geçiş hızı ve su işleme derinliği bakımından en iyi sonuç, SD katkılı numunelerde görülmüştür.

Keywords

• Geçirgenlik, Portland çimentosu, Silis Dumanı,, Uçucu Kül, Ultrases,