THE EFFECT OF TEMPERATURES ON THE TLP DIFFUSION BONDING OF Ni-Ti-Cu COMPOSITES MANUFACTURED BY COLD PRESSING METHOD

Year 2008, Volume: 3 Issue: 4, 558 - 570, 01.05.2008

Abstract

ABSTRACT In this study, the effect of welding temperatures on the TLP diffusion bonding of Ni-Ti-Cu composites manufactured by cold pressing method was investigated. Composite materials have been produced with proportions by mixing 44±5µm Ni-Ti-Cu powders. Diffusion bonding experiments were carried out in argon atmosphere at 910-940 and 970 ºC and 5 MPa under a dynamic load for at 60 constant durations. The microstructure of the join was examined by optic analysis, SEM and X-Ray. The strength of the joint tested by shear-lap and microhardness tests. The result of all observations, tests and measurements indicated that the quality of the coalescence at interfaces a homogenous Ni-Ti-Cu distribution and high interlayer diffusion. The result of all observations, tests and measurements indicated that the quality of the coalescence at interfaces at elevated temperatures.

SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ

Year 2008, Volume: 3 Issue: 4, 558 - 570, 01.05.2008

Abstract

ÖZET Bu çalışmada, soğuk presleme yöntemiyle üretilen, Ni-Ti-Cu kompozitlerin, TLP difüzyon kaynak yöntemiyle birleştirilmesinde kaynak sıcaklığının birleşme üzerindeki etkisi araştırılmıştır. Kompozit malzemeler ortalama 44±5µm boyutlarında toz malzemelerden üretildi. Üretilen numunelerin difüzyon kaynakları, argon koruyucu gaz atmosferinde, 5 MPa'lık dinamik yükleme ile 60 dk'lık sabit süre, 910, 940 ve 970 ºC'lik sıcaklıklarda Ni ve Cu folyo kullanılarak yapıldı. Deneyler sonucunda mikro yapı özellikleri optik mikroskop, SEM ve X-Ray analizleri ile incelendi. Kaynaklı numunelere bindirme kayma ve mikrosertlik testleri uygulandı. Yapılan incelemeler sonucunda homojen Ni-Ti-Cu dağılımı ve yüksek folyo difüzyonu gözlendi. Bütün birleştirmelerde, artan sıcaklığa paralel olarak kaynağın mekanik özelliklerinin iyileştiği tespit edilmiştir.

There are 0 citations in total.

Details

Primary Language Turkish
Journal Section Computer Engineering
Authors

Uğur Çalıgülü This is me

Mustafa Taşkın This is me

Haluk Kejanlı This is me

Publication Date May 1, 2008
Published in Issue Year 2008 Volume: 3 Issue: 4

Cite

APA Çalıgülü, U., Taşkın, M., & Kejanlı, H. (2008). SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ. Engineering Sciences, 3(4), 558-570. https://doi.org/10.12739/nwsaes.v3i4.5000067174
AMA Çalıgülü U, Taşkın M, Kejanlı H. SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ. Engineering Sciences. May 2008;3(4):558-570. doi:10.12739/nwsaes.v3i4.5000067174
Chicago Çalıgülü, Uğur, Mustafa Taşkın, and Haluk Kejanlı. “SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ”. Engineering Sciences 3, no. 4 (May 2008): 558-70. https://doi.org/10.12739/nwsaes.v3i4.5000067174.
EndNote Çalıgülü U, Taşkın M, Kejanlı H (May 1, 2008) SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ. Engineering Sciences 3 4 558–570.
IEEE U. Çalıgülü, M. Taşkın, and H. Kejanlı, “SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ”, Engineering Sciences, vol. 3, no. 4, pp. 558–570, 2008, doi: 10.12739/nwsaes.v3i4.5000067174.
ISNAD Çalıgülü, Uğur et al. “SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ”. Engineering Sciences 3/4 (May 2008), 558-570. https://doi.org/10.12739/nwsaes.v3i4.5000067174.
JAMA Çalıgülü U, Taşkın M, Kejanlı H. SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ. Engineering Sciences. 2008;3:558–570.
MLA Çalıgülü, Uğur et al. “SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ”. Engineering Sciences, vol. 3, no. 4, 2008, pp. 558-70, doi:10.12739/nwsaes.v3i4.5000067174.
Vancouver Çalıgülü U, Taşkın M, Kejanlı H. SOĞUK PRESLEME YÖNTEMİYLE ÜRETİLMİŞ Ni-Ti-Cu KOMPOZİTLERİN TLP DİFÜZYON KAYNAĞINDA SICAKLIĞIN BİRLEŞME ÜZERİNDEKİ ETKİSİNİN İNCELENMESİ. Engineering Sciences. 2008;3(4):558-70.