Novel Lightweight Artificial Aggregate Production: 3D-Printed Aggregate in Lightweight Concrete

Abstract

This study introduces a novel lightweight artificial aggregate manufactured using fused deposition modeling (FDM) 3D‑printing and evaluates its influence on the fresh, mechanical, physical, and durability performance of lightweight aggregate concrete (LWAC). Three aggregate geometries, spherical, edged, and irregular were fabricated from polylactic acid (PLA), and the optimal printing infill density was determined through a multi-criteria decision-making approach using TOPSIS, considering particle crushing strength (PCS), density, and production cost. The optimized 100% infill density configuration was subsequently employed in LWAC mixtures, in which 3D‑printed aggregates fully replaced natural pumice aggregate. The results demonstrate substantial performance improvements across all mixtures incorporating 3D-printed aggregates (3DPA). The 28-day compressive strength of concrete increased by 15-34% relative to pumice-based LWAC, while all mixtures achieved a density lower than 2000 kg/m3. The water absorption and open porosity decreased by up to 32% and 27%, respectively, owing to the impermeable polymeric shell of the 3DPA. Capillary sorptivity significantly reduced for spherical and edged geometries, while irregular shapes induced slightly higher sorptivity due to geometry-related ITZ heterogeneities. The abrasion resistance improved by as much as 23%, and chloride migration resistance exhibited remarkable enhancement, with spherical and edged aggregate concretes yielding “very low” Dnssm values (<5×10-12 m2/s). Overall, the findings highlight the potential of additive‑manufactured artificial aggregates as a tunable, high‑performance alternative to natural lightweight aggregates like pumice, enabling durability‑enhanced LWAC production with superior mechanical and physical performance.

Keywords

• Fused Deposition Modeling (FDM)
• lightweight artifical aggregate
• pumice
• 3D-printing
• TOPSIS

Ethical Statement

Bu çalışmanın özgün olduğunu, daha önce hiçbir yerde yayımlanmadığını ve eşzamanlı olarak başka bir dergiye değerlendirme için gönderilmediğini beyan ederim. Çalışmada herhangi bir çıkar çatışması bulunmamaktadır.

References

1. N. Singh, J. Raza, F. Colangelo, I. Farina, Advancements in lightweight artificial aggregates: typologies, compositions, applications, and prospects for the future, Sustainability 16 (2024) 9329.
2. G.B. Bekkeri, K.K. Shetty, G. Nayak, Synthesis of artificial aggregates and their impact on performance of concrete: a review, J. Mater. Cycles Waste Manag. 25 (2023) 1988–2011.
3. Z. Duan, W. Yang, S. Zou, H. Liu, W. Zhao, W. Chen, A critical review on cold-bonded artificial aggregate developed from solid wastes: From granulation analysis to performance evaluation, Journal of Building Engineering 99 (2025) 111588.
4. S. Islam, G. Ara, U.S. Akhtar, M.G. Mostafa, I. Haque, Z.M. Shuva, A. Samad, Development of lightweight structural concrete with artificial aggregate manufactured from local clay and solid waste materials, Heliyon 10 (2024).
5. B. Vakhshouri, S. Nejadi, Review on the mixture design and mechanical properties of the lightweight concrete containing expanded polystyrene beads, Australian Journal of Structural Engineering 19 (2018) 1–23.
6. X. Shang, J. Chang, J. Yang, X. Ke, Z. Duan, Life cycle sustainable assessment of natural vs artificial lightweight aggregates, J. Clean. Prod. 367 (2022) 133064.
7. A.T. Abdulrasool, S.S. Mohammed, N.R. Kadhim, W.A. Mohammad Hussain, Sustainable materials used as lightweight aggregate:(an overview), in: IOP Conf. Ser. Earth Environ. Sci., IOP Publishing, 2022: p. 012027.
8. N.A. Conzelmann, M.N. Partl, F.J. Clemens, C.R. Müller, L.D. Poulikakos, Effect of artificial aggregate shapes on the porosity, tortuosity and permeability of their packings, Powder Technol. 397 (2022) 117019.

9. M. Zhao, M. Zhao, M. Chen, J. Li, D. Law, An experimental study on strength and toughness of steel fiber reinforced expanded-shale lightweight concrete, Constr. Build. Mater. 183 (2018) 493–501.
10. Y.O. Özkılıç, A.N. Beskopylny, S.A. Stel’makh, E.M. Shcherban, L.R. Mailyan, B. Meskhi, A. Chernil’nik, O. Ananova, C. Aksoylu, E. Madenci, Lightweight expanded-clay fiber concrete with improved characteristics reinforced with short natural fibers, Case Studies in Construction Materials 19 (2023) e02367.
11. A. Terzić, L. Pezo, V. Mitić, Z. Radojević, Artificial fly ash based aggregates properties influence on lightweight concrete performances, Ceram. Int. 41 (2015) 2714–2726.
12. Y. Liang, B. Guan, T. Cao, G. Liu, P. Tang, M. He, M.F. Cheira, A.M. Rashad, Study on the properties of an excess-sulphate phosphogypsum slag cement stabilized base-course mixture containing phosphogypsum-based artificial aggregate, Constr. Build. Mater. 409 (2023) 134095.
13. N. Kabay, A.B. Kızılkanat, B. Akturk, Y. Kahraman, Lightweight cement-based composites incorporating hollow glass microspheres: Fresh and hardened state properties, Teknik Dergi 33 (2022) 11543–11567.
14. J. Liu, C. Shi, N. Farzadnia, X. Ma, Effects of pretreated fine lightweight aggregate on shrinkage and pore structure of ultra-high strength concrete, Constr. Build. Mater. 204 (2019) 276–287.
15. .K. Yew, M.C. Yew, J.H. Beh, F.W. Lee, S.K. Lim, Y.L. Lee, J.H. Lim, K.I.S.A. Kabeer, Effect of pre-soaking treatment method of plant-based aggregate on the properties of lightweight concrete—preliminary study, Coatings 13 (2023) 864.
16. W. Li, D. Wang, B. Chen, K. Hua, Z. Huang, C. Xiong, H. Yu, Preparation of artificial pavement coarse aggregate using 3D printing technology, Materials 15 (2022) 1575.
17. Z. Chen, J. Li, C. Luo, H. Cui, W. Li, Research and application of high-performance artificial aggregates based on 3D printing, Front. Mater. 13 (2026) 1797017.
18. Y. Chen, Y. Zhang, B. Pang, Z. Liu, G. Liu, Extrusion-based 3D printing concrete with coarse aggregate: Printability and direction-dependent mechanical performance, Constr. Build. Mater. 296 (2021) 123624.
19. M. Hematibahar, A. Hasanzadeh, M. Kharun, A.N. Beskopylny, S.A. Stel’makh, E.M. Shcherban’, The Influence of Three-Dimensionally Printed Polymer Materials as Trusses and Shell Structures on the Mechanical Properties and Load-Bearing Capacity of Reinforced Concrete, Materials 17 (2024). https://doi.org/10.3390/ma17143413.
20. Turkish Standards Institution, Tests for mechanical and physical properties of aggregates - Part 6: Determination of particle density and water absorption, Ankara, 2022.
21. M. Rizwee, D. Kumar, Contribution of geometrical infill pattern on mechanical behaviour of 3D manufactured polylactic acid specimen: experimental and numerical analysis, Progress in Rubber, Plastics and Recycling Technology 41 (2025) 331–351.
22. B. Pernet, J.K. Nagel, H. Zhang, Compressive strength assessment of 3D printing infill patterns, Procedia CIRP 105 (2022) 682–687.
23. H. Özkan, N. Kabay, N. Miyan, Properties of cold-bonded and sintered aggregate using washing aggregate sludge and their incorporation in concrete: A promising material, Sustainability 14 (2022) 4205.
24. D. Diakoulaki, G. Mavrotas, L. Papayannakis, Determining objective weights in multiple criteria problems: The critic method, Comput. Oper. Res. 22 (1995) 763–770.
25. H. Taherdoost, M. Madanchian, VIKOR method—an effective compromising ranking technique for decision making, Taherdoost, H., Madanchian, M (2023) 27–33.
26. ASTM International, Standard Test Method for Flow of Hydraulic Cement Mortar, West Conshohocken, PA, 2020.
27. European Committee for Standardization, Testing hardened concrete - Part 1: Shape, dimensions and other requirements for specimens and moulds, Brussels, 2021.
28. N. Miyan, T. Omur, N. Kabay, B. Birol, The potential usage of waste ferrochrome slag in alkali-activated mixes, Journal of Building Engineering 75 (2023) 107026. https://doi.org/10.1016/j.jobe.2023.107026.
29. S. Farah, D.G. Anderson, R. Langer, Physical and mechanical properties of PLA, and their functions in widespread applications — A comprehensive review, Adv. Drug Deliv. Rev. 107 (2016) 367–392. https://doi.org/10.1016/j.addr.2016.06.012.
30. ASTM International, Standard Test Method for Measurement of Rate of Absorption of Water by Hydraulic-Cement Concretes, West Conshohocken, PA, 2020.
31. European Committee for Standardization, Concrete paving blocks - Requirements and test methods, Brussels, 2003.
32. Nordtest, Concrete, mortar and cement-based repair materials: Chloride migration coefficient from non-steady-state migration experiments, Espoo, 1999.
33. P. Ren, T.-C. Ling, K.H. Mo, Recent advances in artificial aggregate production, J. Clean. Prod. 291 (2021) 125215.
34. G. Cao, Y. Liu, S. Long, D. Deng, S. Jiang, H. Su, T. Tan, Influence of aggregate shape on the flow properties of fresh concrete, Powder Technol. 415 (2023) 118186. https://doi.org/10.1016/j.powtec.2022.118186.
35. S.J. Lee, C.H. Lee, M. Shin, S. Bhattacharya, Y.F. Su, Influence of coarse aggregate angularity on the mechanical performance of cement-based materials, Constr. Build. Mater. 204 (2019) 184–192.
36. Q. Liu, A. Cheng, C. Sun, K. Chen, Y. Wang, W. Li, Effects of aggregate’s type and orientation on stress concentration and crack propagation of modeled concrete applied a shear force, Journal of Building Engineering 95 (2024) 110340.
37. P. Deng, K. Xu, S. Guo, Effects of coarse aggregate morphology on concrete mechanical properties, Journal of Building Engineering 63 (2023) 105408.
38. J. Castro, L. Keiser, M. Golias, J. Weiss, Absorption and desorption properties of fine lightweight aggregate for application to internally cured concrete mixtures, Cem. Concr. Compos. 33 (2011) 1001–1008.
39. J. Zhou, Y. Dong, T. Qiu, J. Lv, P. Guo, X. Liu, The microstructure and modification of the interfacial transition zone in lightweight aggregate concrete: a review, Buildings 15 (2025) 2784.
40. Turkish Standards Institution, Concrete - Specification, performance, production and conformity, Ankara, 2021.
41. L. Gu, T. Ozbakkaloglu, Use of recycled plastics in concrete: A critical review, Waste Management 51 (2016) 19–42.
42. W. Ye, S. Li, T. Qiu, X. Cong, Y. Tan, Effects of plastic coating on the physical and mechanical properties of the artificial aggregate made by fly ash, J. Clean. Prod. 360 (2022) 132187.
43. C.S. Thunuguntla, T.D.G. Rao, Effect of mix design parameters on mechanical and durability properties of alkali activated slag concrete, Constr. Build. Mater. 193 (2018) 173–188.
44. S. Papatzani, K. Paıne, Nanomontmorillonite Reinforced Fibre Cements and Nanomontmorillonite-Nanosilica Reinforced Mortars, Turkish Journal of Civil Engineering 34 (2023) 43–60.
45. A. Kılıç, C.D. Atiş, A. Teymen, O. Karahan, F. Özcan, C. Bilim, M. Özdemir, The influence of aggregate type on the strength and abrasion resistance of high strength concrete, Cem. Concr. Compos. 30 (2008) 290–296.
46. İ.A. Al-akhaly, Engineering properties of basalt coarse aggregates in Hamdan Area, NW Sana’a, Yemen, Jeoloji Mühendisliği Dergisi 42 (2018) 159–174.
47. T. Omur, A.K. Akpunar, A.B. Bingöl, B. Oktay, C.B. Üstündağ, N. Kabay, The influence of phase change material filled three-dimensional printed artificial aggregates on the properties of blast furnace slag based alkali-activated concrete, Frontiers of Structural and Civil Engineering 19 (2025) 445–457.
48. N. Kabay, Abrasion resistance and fracture energy of concretes with basalt fiber, Constr. Build. Mater. 50 (2014) 95–101.
49. E.T. Tunc, A Preliminary Experimental Study on the Comparison of Concrete Strength Tests and Bohme Abrasion Test for Basalt Aggregate Concrete, Bitlis Eren Üniversitesi Fen Bilimleri Dergisi 14 (n.d.) 225–242.
50. F. Eren, M. Keskinateş, B. Felekoğlu, K.T. Felekoğlu, Mineral Katkı İkamesinin Kalsiyum Alümina Çimentolu Harçların Taze Hal ve Zamana Bağlı Sertleşmiş Hal Özelliklerine Etkileri, Turkish Journal of Civil Engineering 34 (2023) 139–162.
51. J. Liu, X. Chen, H. Rong, A. Yu, Y. Ming, K. Li, Effect of interface transition zone and coarse aggregate on microscopic diffusion behavior of chloride ion, Materials 15 (2022) 4171.
52. Q. Liu, G. Feng, J. Xia, J. Yang, L. Li, Ionic transport features in concrete composites containing various shaped aggregates: a numerical study, Compos. Struct. 183 (2018) 371–380.
53. L. Nilsson, M.H. Ngo, O.E. Gjørv, High-performance repair materials for concrete structures in the port of Gothenburg, in: Second International Conference on Concrete under Severe Conditions: Environment and Loading, 1998: pp. 1193–1198.
54. U. Geological Survey, Mineral Commodity Summaries 2025, 2025.
55. A. Sarabèr, R. Overhof, T. Green, J. Pels, Artificial lightweight aggregates as utilization for future ashes–A case study, Waste Management 32 (2012) 144–152.
56. J. Go, S.N. Schiffres, A.G. Stevens, A.J. Hart, Rate limits of additive manufacturing by fused filament fabrication and guidelines for high-throughput system design, Addit. Manuf. 16 (2017) 1–11.
57. G.D. Goh, K.K. Wong, N. Tan, H.L. Seet, M.L.S. Nai, Large-format additive manufacturing of polymers: a review of fabrication processes, materials, and design, Virtual Phys. Prototyp. 19 (2024) e2336160.
58. D. Moreno Nieto, D. Moreno Sánchez, Design for Additive Manufacturing: Tool Review and a Case Study, Applied Sciences 11 (2021). https://doi.org/10.3390/app11041571.
59. C.E. Duty, V. Kunc, B. Compton, B. Post, D. Erdman, R. Smith, R. Lind, P. Lloyd, L. Love, Structure and mechanical behavior of Big Area Additive Manufacturing (BAAM) materials, Rapid Prototyp. J. 23 (2017) 181–189. https://doi.org/10.1108/RPJ-12-2015-0183.
60. P. Wu, J. Wang, X. Wang, A critical review of the use of 3-D printing in the construction industry, Autom. Constr. 68 (2016) 21–31.