Investigation of Calcium Oxide (CaO) Effects in Crackle Stoneware Glazes

Yıl 2018, Cilt: 4 Sayı: 1, 25 - 38, 29.04.2018

Selvin Yeşilay Münevver Çakı Aslı Çakır Arianpour

Öz

Crackle
glazes for use on ceramic bodies are well-known in the ceramic art and may be
defined as glazes whose tendency to craze is used for decorative effect. One of
the important steps to understanding glazes and glazing is to have a good grasp
of the properties the materials you are using and how they affect the glaze
properties.  The final properties of the
glaze can be managed and evaluated by focusing on the oxide effects of the
fired glaze. Calcium Oxide (CaO) is the principle flux in medium and high temperature
glazes, beginning its action (within the glaze) around 1100 ◦C. In this work
the effect of CaO on the properties of crackle glazes was investigated. 5
different crackle glaze recipes containing different amounts of calcium oxide
were prepared and fired at 1160 ◦C degrees. Manganese (II) oxide (MnO) and Iron
Oxide (Fe₂O₃) were used as coloring oxide.

 

All
the samples were characterized by X-ray fluorescence (XRF), X-ray diffraction
(XRD), scanning electron microscopy (SEM) and color/gloss measurements.  It has been observed that calcite addition
affects the transparency, color and surface texture of the standard seal. It
has been observed that as the amount of calcite increases in the glaze
formulation, some new phases are formed. From the analysis of these newly
formed peaks, it was found that the new phases are the Ca-silicate phase
varieties and especially the wollastonite (CaSiO₃). Addition of
calcite in the ratio of 40 % increased the sintering temperature by 210 °C. 

Anahtar Kelimeler

Crackle glaze, ceramic, characterization, calcuim oxide, production

Kalsiyum Oksitin (CaO) Çatlaklı Sır Bileşimlerindeki Etkilerinin Araştırılması

Öz

Seramik
ürünlerde kullanılan sırlar arasında güçlü görsel etkiye sahip çatlaklı sırlar
seramik sanatında yaygın kullanılırlar ve çatlak oluşturma eğilimi olan ve
dekoratif etki için kullanılan sırlar olarak tanımlanabilirler. Sırların ve
camların anlaşılmasına yönelik önemli adımlardan biri, kullandığınız
malzemeleri ve sır özelliklerini nasıl etkilediğini iyi kavramaktır. Sırların
nihai özellikleri, sır bileşiminde kullanılan oksitlerin pişmiş sırın özelliklerine
olan etkileri incelenerek kontrol edilebilir. Kalsiyum Oksit (CaO) etkisi 1100
⁰C’nin üzerinde başlayan orta ve yüksek sıcaklık sırlarında kullanılan temel
bir akışkanlaştırıcıdır.

 

Yapılan
çalışmada CaO’in çatlaklı sırın özelliklerine etkisi incelenmiştir. Farklı
oranlarda CaO içeren 5 farklı çatlaklı sır reçetesi hazırlanarak 1160 ⁰C’de
pişirilmiştir. Üretilen sırlarda renklendirici olarak Mangan oksit (MnO) ve
demir oksit (Fe₂O₃) kullanılmıştır. Tüm numunelere XRF
(X-Işınları Floresansı), XRD (X-Işınları Difraksiyonu), SEM (Taramalı elektron
mikroskobu) ve renk/parlaklık ölçüm testleri uygulanmıştır. Kalsit ilavesinin
standart sırın şeffaflık, renk ve yüzey dokuları üzerinde etkili olduğu
gözlenmiştir. sır formülasyonunda kalsit miktarının artmasıyla sonucunda bazı
yeni fazların oluştuğu gözlemlenmiştir. Bu yeni oluşan piklerin analizine
bakıldığında,  yeni fazların Ca-silikat
fazının çeşitleri olduğu ve özellikle vollastonit (CaSiO₃) 'ten
oluştuğu tespit edilmiştir. % 40 oranında kalsit ilavesi sırın sinterleme
sıcaklığını yaklaşık 210 °C arttırmıştır.

Anahtar Kelimeler

Çatlaklı sır, seramik, karakterizasyon, kalsiyum oksit, üretim

Kaynakça

• [1] A. Sariisik, G. Sariisik, A. Sentürk, Applications of glaze and décor on dimensioned andesites used in construction sector, Constr. Build. Mater., 25 (2011), pp. 3694-3702.
• [2] Gajek, M., Partyka, J., Rapacz-Kmita, A., Gasek, K. Development of anorthite based white porcelain glaze without ZrSiO4 content (2017) Ceramics International, 43 (2), pp. 1703-1709, doi: 10.1016/j.ceramint.2016.08.140. [3] M. Sheikhattar, H. Attar, S. Sharafi, W.M. Carty, Influence of surface crystallinity on the surface roughness of different ceramic glazes, Mater. Charact., 118 (2016), pp. 570-574.
• [4] R. Casasola, J.Ma. Rincón, M. Romero. Glass-ceramics glazes for ceramic tiles-a review, Journal of Material Science, 47 (2012) 553-582; doi: 10.1007/s10853-011-5981-y.
• [5] M. Reben, M. Kosmal, N. Pałczyńska and P. Pichniarczyk, Waste immobilization and environmental sustainability in glass-ceramics glazes development, E3S Web of Conferences 10, 00071 (2016), SEED 2016, DOI: 10.1051/ e3sconf/20161000071.
• [6] Jiyuan Li, Jinsheng Liang, Lijuan Wang, Fei Wang, Effect of particle-size distribution on the surface appearance of glazed surface, J. Therm. Anal. Calorim. (2014) 115:1127–1131,.
• [7] Richard Zakin, Ceramics, Mastering the Craft, Chilton Book Company/Radnor, Pennsylvania, s.80, 1990.
• [8] Daniel Rhodes, Clay and Glazes for the Potter, Ravenio Books, 22 Eki 2015 - 248 sayfa.
• [9] David Scott, Clays and Glazes in Studio Ceramics, The Crowood Press, s.112, 1998.
• [10] Sophia Lahlil, Weidong Li and Ji Ming Xu, Crack Patterns Morphology of Ancient Chinese Wares, The Old Potter’s Almanack, Volume Eighten, number One: June 2013. ISSN 0965-7479.
• [11] L.M. Schabbacha, F. Bondioli, M.C. Fredel, Colouring of opaque ceramic glaze with zircon pigments: Formulation with simplified Kubelka–Munk model, Journal of the European Ceramic Society, Volume 31, Issue 5, May 2011, Pages 659–664.
• [12] Notes on glazes, La Meridiana International School of Ceramic Art In Tuscany, http://www.lameridiana.fi.it/pdf/EN%20Notes%20on%20glazes.pdf.
• [13] Suna Çetin, Çukurova Üniversitesi, Sosyal Bilimler Enstitüsü, Seramik Anasanat Dalı, Bazalt Tüfü Kullanılarak Yapılan Firitlerin Endüstriyel ve Sanatsal Sırlarda Kullanımı, Fiziksel ve Kimyasal Özelliklerinin Araştırılması, Yüksek Lisans Tezi, Adana 2005.
• [14] J.R. Taylor ve A.C. Bull, Ceramics Glaze Technology, The Institute of Ceramics, Pergamon Press, 1986.
• [15] Wood, N., Chinese Glazes: Their Origins, Chemistry, and Recreation, University of Pennsylvania Press, s.12, 1999.