The structural, electronic, mechanical and
dynamic properties of Rh3Sc compound in the L12 phase
have been investigated. The calculated lattice constants, bulk modulus and
elastic constants for this compound are in good agreement with the available
theoretical and experimental data. The elastic constants (C11,
C12 and C44) in L12 phase for
Rh3Sc compound are calculated using the energy-strain method. These
calculated elastic constants satisfy the mechanical stability criterion of Rh3Sc
is predicted. The electronic structure and phonon frequency curves of Rh3Sc
are obtained and analyzed. The high-frequency region of Rh3Sc is
mainly due to the vibrations of Sc atoms. The specific heat capacity at
constant volume and different temperature is calculated, and this aspect is
discussed using quasi-harmonic approximation.
Rh3Sc bileşiğinin L12 fazındaki yapısal,
elektronik, mekanik ve dinamik özellikleri araştırılmıştır. Bu bileşik için
hesaplanan örgü sabitleri, Bulk modülü ve elastik sabitler mevcut teorik ve
deneysel verilerle iyi bir şekilde uyumludur. L12 fazda incelenen Rh3Sc
bileşiğinin elastik sabitleri (C11, C12 ve C44)
enerji-strain metodu kullanılarak hesaplandı. Rh3Sc’nin hesaplanan elastik
sabitleri mekanik kararlılık şartlarını karşılamaktadır. Rh3Sc'nin
elektronik yapısı ve fonon özellikleri hesaplanmış ve analiz edilmiştir. Rh3Sc'nin
yüksek frekans bölgesi, esas olarak Sc atomlarının titreşimlerinden
kaynaklanmaktadır. Farklı sıcaklık ve sabit hacimde ısı sığası quasi-harmonik
yaklaşım kullanılarak hesaplandı ve bu çerçevede tartışıldı.
Konular | Malzeme Üretim Teknolojileri |
---|---|
Bölüm | Araştırma Makalesi |
Yazarlar | |
Yayımlanma Tarihi | 1 Haziran 2017 |
Gönderilme Tarihi | 22 Aralık 2016 |
Kabul Tarihi | 21 Mart 2017 |
Yayımlandığı Sayı | Yıl 2017 |
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.