Cadmium sulphide films have been deposited onto glass
substrate by chemical bath deposition method. The CdS films have been annealed
in the temperature range of 200-400 oC at one hour in nitrogen gas.
The crystal structures of the films were determined by x-ray diffraction (XRD)
patterns. XRD data showed that the transition from CdS (FCC) to α-CdS (Hawleyite) form by annealing effect.
The optical band gaps of the films have been obtained from the optical
absorbance spectrum found to be 2.33 and 2.39 eV. The bands bending in the
films were calculated to be between 120-350 meV. The optical transmissions of
the films have been determined to be between 45-92 % in the visible region.
CdS Chemical bath deposition Thermal annealing Optical properties
Kadmiyum sülfür filmleri kimyasal banyo depolama yöntemi ile
cam tabanlar üzerine biriktirildi. Elde edilen filmler azot gazında 1 saat
boyunca 200-400 oC sıcaklık aralığında tavlandı. Filmlerin kristal
yapısı x-ışını kırınım (XRD) desenlerinden belirlendi. XRD verileri, tavlama
etkisiyle CdS (FCC) yapısından α-CdS
(Hawleyite) formuna geçiş olduğunu gösterdi. Elde edilen CdS filmlerinin
optiksel bant aralığı değerleri optiksel absorbans spetrumlarından
yararlanılarak 2,33 ve 2,39 eV olarak belirlendi. Bant sarkmaları değerleri
120-350 meV arasında olduğu hesaplandı. Filmlerin görünür bölgede %45-92
arasında geçirgenlik değerlerine sahip olduğu belirlendi.
Konular | Metroloji,Uygulamalı ve Endüstriyel Fizik |
---|---|
Bölüm | Araştırma Makalesi |
Yazarlar | |
Yayımlanma Tarihi | 1 Aralık 2017 |
Gönderilme Tarihi | 5 Ocak 2017 |
Kabul Tarihi | 1 Haziran 2017 |
Yayımlandığı Sayı | Yıl 2017 |
This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.