Effect of Process Parameters on the Metallurgical Properties of a Boron-Added Cast Austenitic Steel Designed for Special Purposes
Abstract
A new kind of boron-added cast austenitic steel which also contained chromium, molybdenum and manganese was manufactured via vacuum induction melting followed by casting procedure. Solution annealing heat treatment was performed at three different temperatures for three different times to dissolve eutectic M2C carbides in austenitic matrix. All of the samples were rapid-cooled in oil medium after the solution annealing heat treatment. Aging treatments were carried out after solution annealing heat treatment performed at 1250 °C for 24 hours. Hardness value was decreased after solution annealing performed at 1250 °C for 24 hours. Transformation of M2C carbide with a hexagonal lattice into Fe-rich M6C carbide with a face-centered cubic lattice and formation of precipitates occurred as a result of aging performed at 700 and 800 °C. Sub-micron sized Cr23C6 carbides and Mo2BC precipitates were formed and hardness value was increased after aging performed at 700 °C. Nano-sized Cr23C6 carbides, Mo2B borides and Cr7BC4 precipitates were formed and hardness value was higher after aging performed at 800 °C. An optical light microscope was utilized to characterize solution annealing treatments and to perform grain size measurements. A scanning electron microscope was used to identify carbide types and carbide transformation during aging.
Keywords
Vacuum induction melting, Cast austenitic steel, Heat treatment, Precipitation hardening, Carbide and boride precipitate, Carbide transformation
Supporting Institution
This work was financially supported by Scientific Research and Project Unit of Istanbul Technical University.
Ethical Statement
This manuscript has been originated from the MSc thesis of the first author.
References
- Asahi, H. (2002). Effects of Mo addition and austenitizing temperature on hardenability of low alloy B-added steels. ISIJ International, 42(10), 1150-1155.
- ASTM (2021). E112-13, Standard test methods for determining average grain size.
- ASTM (2023). E92-23, Standard test methods for Vickers hardness and Knoop hardness of metallic materials.
- Balluffi, R. W. & Mehl, R. F. (1982). Grain boundary diffusion mechanisms in metals. Metallurgical Transactions A, 13(12), 2069-2095.
- Banerji, S. K. & Morral, J. E. (1980). Boron in austenitic stainless steels. Warrendale: The Metallurgical Society of AIME.
- Bhadeshia, H. K. D. H. & Honeycombe, R. W. K. (2006). Steels: Microstructure and Properties (Third Edition). Elsevier.
- Bialobrzeska, B. (2021). Effect of alloying additives and microadditives on hardenability increase caused by action of boron. Metals, 11, 589.
- Bin, Z., Yu, S., Jun, C. & Zhen-shan, C. (2011). Breakdown behavior of eutectic carbide in high speed steel during hot compression. Journal of Iron and Steel Research International, 18(1), 41-48.
- British Standard (2000). BS EN 10020:2000, Definition and classification grades of steel.
- Chaus, A. S., Chovanec, J. & Legerska, M. (2006). Development of high-speed steels for cast metal-cutting tools. Solid State Phenomena, 113, 559-564.