GAZ ATOMİZASYON YÖNTEMİ İLE AM60 MAGNEZYUM ALAŞIM TOZU ÜRETİMİ VE KARAKTERİZASYONU

Öz

In this study, the production of AM60 magnesium alloy powder by gas atomization method was experimentally investigated. Experiments were carried out at a constant temperature of 770 °C, 35 bar atomizing gas pressure and 4 different nozzle diameters (2, 3, 4, 5 mm). Argon gas was used to atomize the melt. Scanning electron microscopy (SEM) was used to determine the shape of the AM60 powders produced, XRD and XRF analyzes were used to determine the internal phases of the produced powders and percentage of these phases, and laser measurement devices were used for powder size analysis. The overall appearance of the AM60 magnesium alloy powders produced is complex, ligament, rod, droplet, flake and spherical but the shape of the powder is mostly dripping and spherical depending on the reduction of the nozzle diameter. The finest powder obtained was found to have a gas pressure of 35 bar at a temperature of 770 °C, a diameter of 2 mm, and the overall shape of the powder was found to be complex.

Anahtar Kelimeler

• Gaz atomizasyonu,AM60 alaşım tozu,nozul çapı,toz karakterizasyonu.

AM60 MAGNESIUM ALLOY POWDER PRODUCTION AND CHARACTERIZATION BY GAS ATOMIZATION METHOD

Öz

Anahtar Kelimeler

• Gas atomization,AM60 alloy powder,nozzle diameter,powder characterization.

Kaynakça

1. 1. Oğuz, Ş., Öztürk, Z., Uzun, E., Kurt, A. ve Boz, M., “Gaz atomizasyonu yöntemi ile kalay tozu üretiminde gaz basıncının toz boyutu ve şekline etkisi”, 6th International Advanced Technologies Symposium (IATS’11), Elâzığ, 565-568 (2011).
2. 2. Boz, M. ve Kurt, A., "Toz metal fren balata malzemelerinin sürtünme-aşınma performansı üzerine çinkonun etkisi." Gazi Üniversitesi MühendislikMimarlık Fakültesi Dergisi, 21.1 (2006).
3. 3. Sarıtaş, S., Türker, M. ve Durlu, N., “Toz Metalurjisi ve Parçacıklı Malzeme İşlemleri”, Türk Toz Metalurjisi Derneği Yayınları, Ankara, (2007).
4. 4. Sarıtaş, S., and Doğan, C., Metal powder production by centrifugal atomization, Int. J. Powder Metallurgy, 30, 419 – 427 (1994).
5. 5. Yıldız, E.S., “Gaz Atomizasyonu İle Metal Tozu Üretiminde Nozul Geometrisinin Toz Boyutuna Etkisinin Araştırılması”, Yüksek Lisans Tezi, Dumlupınar Üniversitesi Fen Bilimleri Enstitüsü, Kütahya, 5-14 (2007)
6. 6. Öztürk, F. ve Kaçar, İ., “Magnezyum alaşımları ve kullanım alanlarının incelenmesi”, Niğde Üniversitesi Mühendislik Bilimleri Dergisi, Cilt 1 Sayı 1: 12-20 (2012).
7. 7. Öztürk, Z., Aslan H., Uzun E. ve Boz, M., “Gaz Atomizasyon Yöntemi ile Al 2024 Tozu Üretimi ve Karakterizasyonu”, 7. th International Powder Metallurgy Conference, 24-28 Haziran, (2014).
8. 8. Mordike B.L., and Ebert T., “Magnesium Properties—Applications—Potential”, Mat. Sci. Eng. A, 302, p: 37-45, (2001).

9. 9. Benedyk J.J., “Magnesium Challenges Aluminum Dominance as the Light Metal of Choice in Automotive Markets”, Light Metal Age-The International Magazine of Light Metal Industry, October 2004.
10. 10. American Society for Testing and Materials-ASM, Metal Handbook, Forming and Forging, 14, p: 791-804, 9th Edition, 1988.
11. 11. Derin, C. B., “Kendiliğinden İlerleyen Yüksek Sıcaklık Sentezi Yöntemi İle Tunsgten Borür Tozu Üretimi” (Doctoral dissertation, Fen Bilimleri Enstitüsü) (2009).
12. 12. Uslan, İ., ve Küçükarslan, S., “Kalay tozu üretimine gaz atomizasyonu parametrelerinin etkisinin incelenmesi”. Gazi Üniversitesi Mühendislik-Mimarlık Fakültesi Dergisi, 25(1) (2010).
13. 13. Kayalı, Y.E. ve Ünal R., “Gaz Atomizasyonu İle Metal Tozu Üretiminde Toz Boyutunun Sayısal Çözümleme İle Belirlenmesi”, Gazi Üniversitesi MühendislikMimarlık Fakültesi Dergisi, (2018).
14. 14. Grant, N.J., "Recent trends and developments with rapidly solidified materials." Metallurgical and Materials Transactions A 23.4, 1083-1093 (1992).
15. 15. Daloz, D., and Michot, G., “Influence of the consolidation step on the mechanical properties of rapidly solidified Mg-Al-Zn alloys”, Int. J. Rapid Solidif., 9, 289e304 (1996).
16. 16. Rajan, T. P. D., Jayakumar, E. and Pai. B.C., "Developments in solidification processing of functionally graded aluminium alloys and composites by centrifugal casting technique." Transactions of the Indian Institute of Metals 65.6, 531-537 (2012).
17. 17. Pai, B. C., Pillai, U. T. S., Manikandan, P., and Srinivasan, A., “Modification of AZ91 Mg alloys for high temperature applications.” Transactions of the Indian Institute of Metals, 65(6), 601-606 (2012).
18. 18. Zhang, J. M., Jiang, B. L., Wang, Z. H., Yuan, S., Nan, H. Q., and Luo, H. B., “Influence of aging modes on microstructure and mechanical properties of AZ80 magnesium alloy.” Research & Development (2007).
19. 19. Boby, A., Pillai, U. T. S., and Pai, B. C., “Effect of Pb Addition on the Discontinuous and Continuous Mg17Al12-β Precipitate During Solidification of AZ91 Magnesium Alloy.” Transactions of the Indian Institute of Metals, 66(2), 105-108 (2013).