Sn-Zn based lead free alloys are considered for replacing lead containing alloy systems for soldering. In this paper, In, Ag, Al doped Sn-Zn based systems were produced and investigated for mechanical and microstructural properties to obtain the most suitable system. Microstructures were observed by using an optic microscope. The samples' existing phases were investigated by using Energy Dispersive X-Ray analysis (EDX). Melting temperatures, the enthalpy of fusion and the specific heat change between the liquid and solid phases in the systems were determined with Differential Scanning Calorimetry (DSC). Also, microhardness values were measured at room temperature.
Lead-free solder systems Mechanical properties Microstructure Differential Scanning Calorimetry Microhardness
Sn-Zn bazlı kurşunsuz alaşımlar, lehimleme için kurşun içeren alaşım sistemlerinin yerine kullanılmak üzere düşünülmektedir. Bu çalışmada, In, Ag, Al katkılı Sn-Zn esaslı sistemler üretilmiş ve en uygun sistemin elde edilmesi için mekanik ve mikro yapısal özellikler incelenmiştir. Mikro yapılar bir optik mikroskop kullanılarak gözlemlenmiştir. Numunelerin mevcut fazları Enerji Dağılım X-Işını Spektrometresi (EDX) kullanılarak araştırılmıştır. Sistemlerdeki erime sıcaklıkları, füzyon entalpisi ve sıvı ve katı fazlar arasındaki özgül ısı değişimi Diferansiyel Taramalı Kalorimetre (DSC) ile belirlenmiştir. Ayrıca oda sıcaklığında mikrosertlik değerleri de ölçülmüştür.
Kurşunsuz Lehim Sistemleri Mekanik Özellikler Mikroyapı Diferansiyel Taramalı Kalorimetre Mikrosertlik
Primary Language | English |
---|---|
Subjects | Metrology, Applied and Industrial Physics |
Journal Section | Articles |
Authors | |
Publication Date | June 30, 2022 |
Submission Date | February 18, 2022 |
Published in Issue | Year 2022 |
Bu eser Creative Commons Atıf-GayriTicari 4.0 Uluslararası Lisansı ile lisanslanmıştır.