Development and Characterization of Parian Bodies Using Feldspar from Two Selected Deposits in Nigeria

Year 2016, Volume: 4 Issue: 1, 0 - 0, 01.01.2016

Toluwalope Ogundare

https://doi.org/10.21541/apjes.08877

Cited By: 1

Abstract

Self glazed bodies also called Parian Bodies are chiefly composed of Feldspar which majorly acts as flux in reducing the melting temperature of the particular ceramic body thereby reducing the stress of double firing a ceramic product. In this present research work, Okpella and Ijero-Ekiti feldspar deposits in Nigeria together with other raw materials were utilized to develop parian bodies which are very suitable for making ceramic tiles, dolls and figurines. Chemical analyses were carried out on the raw materials using X-ray fluorescence (XRF) in order to ascertain their suitability for developing parian bodies. Six compositions were made from these two deposits using a standard parian body composition of 70% feldspar. The samples were shaped, dried and sintered between 1050 ^oC - 1250 ^oC at the interval of 50⁰C.  Flexural strength, fired shrinkage, porosity and water absorption tests were used to characterize the samples. The results showed that samples fired at 1200⁰C and 1250⁰C exhibited technological properties that meet up with ISO standards. The two feldspar deposits were found to be suitable for developing parian bodies

Keywords: Parian, Feldspar, Kaolin, Porcelain, Sintered, Whiteware.

References

• Kamseu E., Leonelli C., Boccaccini D.N., Veronesi P., Miselli P., Giancarlo P. and Chinje M.U., Characterisation of Porcelain Compositions Using Two China Clays from Cameroon, Ceramics International, 2007, 33, p. 851-857.
• Peter W.O., Stefan J. and Joseph K.B., Characterization of Feldspar and Quartz Raw Materials in Uganda for Manufacture of Electrical Porcelains, Journal of Australia Ceramic Society, 2006, 41(1), p. 29-35.
• Reed, J.S., Principles of Ceramics Processing, New York, Wiley & Sons, 1995
• McLaren E. A. and Cao P. T. Ceramics in Dentistry—Part I: Classes of Materials. Inside Dentistry; 2009
• Carty, W.M., 2002, Observation on the Glass Phase Composition in Porcelains. Chem. Eng. Sci. Proc., 2002, 23(2), p. 79-94.
• Holdren, G.R and Berner, R.A, Mechanism of Feldspar Weathering.
• low Temperature Feldspars in Sedimentary Rocks, American Journal of Science, 1999, p. 279, 435-479.
• Ima (2000). Ceramic Raw Materials. London Pergarmon Press
• Nelson,I and Stephen, A (2008): Weathering and Clays minerals.
• Matthew G.O., and Fatile B.O., Characterization of Vitrified Porcelain Tiles Using Feldspar from Three Selected Deposits in Nigeria. Research Journal of Recent Sciences, 2014, 3(9), p. 67-72.
• Martín-Márquez J., Rincón M.J. and Romero M., Effect of firing temperature on sintering of porcelain stoneware tiles, Ceramics Internacional, 2008, 34, p. 1867-1873.
• Boussak H., Chemani H., and Serier A., Characterization of Porcelain Tableware Formulation Containing Bentonite Clay, International Journal of Physical Sciences, 2014, 10(1), p. 38-45.