EFFECTS OF PRESSURE AND TEMPERATURE ON PHYSICAL AND MECHANICAL PROPERTIES OF HIGH DENSITY FIBERBOARD

Abstract

In this study, high density fiberboard was manufactured by using dry process. The effects of press temperature

and pressure on physical and mechanical properties were investigated. The fibers were obtained from SFC MDF

mill consisting of 70% Pinus spp. and 30% hardwoods. The laboratory conditions were as fallows; pres

temperatures were 160-170-180-190 °C, pressure as 50-55 kg/cm2, total pressing time as 100 seconds. The HDF

produced had 5±0,2 mm and having the density of 1,02-1,12 g/cm3. The physical and mechanical properties of

the panels were determined according to TS EN standards. It was found that increasing temperature and pressure

had positive effect on the properties.

Keywords

• Fiberboard,HDF,Physical and Mechanical Properties,Pressure

SERT LİF LEVHALARIN FİZİKSEL VE MEKANİK ÖZELLİKLERİNE SICAKLIK VE BASINCIN ETKİSİ

Abstract

Bu araştırmada, Kuru Yöntemle sert lif levha üretilmiştir. Üretim koşullarından pres sıcaklığı ve basıncının

levhaların fiziksel ve mekanik özellikleri üzerine etkisi araştırılmıştır. Lifler; Kastamonu SFC A.Ş.’den temin

edilmiş olup, %70 çam türleri, %30 yapraklı ağaç türleri karışımından oluşmaktadır. Laboratuar koşullarında

160-170-180-190 °C sıcaklık ve 50-55 kg/cm2 pres basıncı, 100 sn toplam pres süresi kullanılarak 5±0,2 mm

kalınlığında ve 1,02-1,12 g/cm3 özgül kütleli sert lif levhalar elde edilmiştir. Levhaların fiziksel ve mekanik

özellikleri, TS EN standartları kullanılarak belirlenmiştir. Bu çalışmada sıcaklık ve basınç artışının levhaların

fiziksel ve mekanik özelliklerini olumlu yönde etkilediği tespit edilmiştir.

Keywords

• Liflevha,HDF,Fiziksel ve Mekanik Özellikler,Basınç

References

1. Bozkurt, Y. ve Göker, Y., 1990, Yongalevha Endüstrisi, İ.Ü. Orman Fakültesi Yayınları, İstanbul, 975-404-191-1.
2. Eroğlu, H. ve Usta, M., 2000, Liflevha Üretim Teknolojisi, K.T.Ü. Orman Fakültesi Yayınları, Trabzon.
3. İstek, A. ve Eroğlu, H., 2002, Buğday Saplarından (Triticum aestivum L.,) Sert Lif Levha Üretimi, II. Ulusal Ormancılık Kongresi, cilt 3, sayfa 1038-1041, 15-18 Mayıs.
4. Kollmann, F.P.F., E.W. KUENZI, A.J. STAMM, 1975, Principles of Wood Science and Technology II, wood Based Materials, Springer Ferlag Berlin, p. 551-672.
5. Suchsland, O., Woodson, E.G., 1986, Fiberboard Manufacturing Practices in the United States. U.S. Department of Agriculture, Forest Service No:640, Lousiana, USA.
6. TS EN 316, Nisan 1998, Odun Lifi Levhalar – Tarifler Sınıflandırma ve Semboller, TSE, Ankara.
7. TS EN 326-1, Nisan 1999, Ahşap Esaslı Levhalar – Numune Alma Kesme ve Muayene, TSE, Ankara.
8. TS EN 322, Nisan 1999, Ahşap Esaslı Levhalar – Rutubet Miktarının Tayini, TSE, Ankara.

9. TS EN 323, Nisan 1999, Ahşap Esaslı Levhalar – Birim Hacim Ağırlığının Tayini, TSE, Ankara.
10. TS EN 317, Nisan 1999, Yongalevhalar ve Lif Levhalar – Su İçerisine Daldırma İşleminden Sonra Kalınlığına Şişme Tayini, TSE, Ankara.
11. TS EN 310, Nisan 1999, Ahşap Esaslı Levhalar – Eğilme Dayanımı ve Eğilme Elastikiyet Modülünün Tayini, TSE, Ankara.
12. TS EN 319, Nisan 1999, Yongalevhalar ve Lif Levhalar Levha Yüzeyine Dik Çekme Dayanımının Tayini, TSE, Ankara.