FAILURE BEHAVIOUR OF TWO SERIAL BOLTED CROSS-PLY LAMINATED COMPOSITE PLATES

Abstract

In this study, failure bahaviour of two serial bolted laminated composite plates was investigated experimentally. During the production of laminated composite plates, glass fibers and epoxy were used as reinforcement and matris materials, respectively. The orientation of laminas were preferred as cross-ply and symmetric, [02˚/902˚]s . After the production of plates, the specimens were pepared according to various dimensional parameters. The maximum failure loads were obtained from experiments via tensile test machine connected a computer. The bearing strengths were calculated using experimental failure loads and failure types were determined from observations of tested specimens. It is understand that, according to experimental study results, failure behavior of two serial bolted kompozit specimens were effected from geometrical parameters strictly. On the other hand, the magnitudes of maximum failure loads, bearing strengths and the creation of failure types were changed related to geometrical parameters.

Keywords

• Laminated composite, Failure behaviour, Failure analysis

SERİ ÇİFT CIVATA BAĞLANTILI ÇAPRAZ TAKVİYE EDİLMİŞ TABAKALI KOMPOZİT LEVHALARIN HASAR DAVRANIŞI

Abstract

Bu çalışmada, birbirine seri çift cıvata bağlantılı tabakalı kompozit plakaların hasar davranışı deneysel olarak incelenmiştir. Tabakalı kompozit levhaların üretiminde, takviye elemanı olarak cam lifleri ve matris malzemesi olarak epoksi kullanılmıştır. Tabaka dizilişi olarak, çapraz [02˚/902˚]stakviyeli simetrik oryantasyon seçilmiştir. Levhaların üretiminden sonra, belirlenen çeşitli boyutsal değişkenlere göre deney numuneleri hazırlanmıştır. Bilgisayara bağlı çekme cihazı kullanılarak yapılan deneyler ile bağlantılardaki maksimum hasar yükleri elde edilmiştir. Bu sonuçlar kullanılarak, yatak mukavemetleri hesaplanmış ve numunelerin incelenmesi ile hasar tipleri tespit edilmiştir. Deneysel çalışma sonuçlarına göre, seri çift cıvata bağlantılı kompozit numunelerde incelenen geometrik değişkenlerin, hasar davranışını önemli şekilde etkilediği anlaşılmıştır. Bir başka şekilde ifade etmek gerekirse, maksimum hasar yükleri ile yatak mukavemetlerinin değerlerinin ve hasar tiplerinin oluşumunun geometrik parametrelere bağlı olarak değiştiği tespit edilmiştir

Keywords

• Tabakalı kompozit, Hasar davranışı, Hasar analizi

References

1. Ataş A., Şen F., Arslan N. (2009): “Failure Analysis of Laminated Composite Plates with Two Parallel Pin-loaded holes”, Journal of Reinforced Plastics and Composites, Cilt 28, No. 10, s. 1265-1276.
2. Gibson R.F. (1994): “Principals of Composite Material Mechanics”, Singapore. Mc Graw- Hill.
3. Jones R. M. (1999): “Mechanics of Composite Material”. Philadelphia: Taylor & Francis.
4. Mallick P. K. (1993): “Fiber-reinforced Composites Materials, Manufacturing and Design”. Marcel Decker.
5. Pakdil M., Şen F., Sayman O., Benli S. (2007): “The Effect of Preload on Failure Response of Glass-Epoxy Laminated Composite Bolted-joints with Clearance”. Journal of Reinforced Plastics and Composites, Cilt 26, s. 1239-1252.
6. Scalea F. L. D., Cappello F., Cloud G. L. (1999): “On the Elastic Behavior of a Cross-ply Composite Pin-joint with Clearance fits”, J. of Thermoplastic Composite Materials, Cilt. 12, s. 13-22.
7. Sayman O., Siyahkoç R., Şen F., Özcan R. (2007): “Experimental Determination of Bearing Strength in Fiber Reinforced Laminated Composite Bolted-joints under Preload”, Journal of Reinforced Plastics and Composites, Cilt 26, s. 1051-1063.
8. Şen F., Pakdil M., Sayman O., Benli S. (2008): “Experimental Failure Analysis of Mechanically Fastened Joints with Clearance in Composite Laminates under Preload”, Materials & Design, Cilt 29, s. 1159-1169.

9. Şen F. (2007): “Failure Analysis of Composite Pin-Loaded Joints under Preload Moments”, PhD Thesis, Dokuz Eylül University, Izmir.
10. Şen F., Pakdil M., Çakan A. (2008): “Paralel Çift Pim Bağlantılı E-Glass/Epoksi Tabakalı Kompozit Plakalarda Hasar Yükleri ve Tipleri”, VII. Havacılık Sempozyumu Bildiriler Kitabı, s. 36-40, Kayseri.
11. Tong L., Mouritz A. P., Bannister M. (2002): “3D Fibre Reinforced Polymer Composites”, Elsevier, UK.