THERMAL CONDUCTIVITY OF ALUMINUM OXIDE PARTICLE FILLED POLYETHYLENE COMPOSITES

Abstract

In this study, the effective thermal conductivity of high density polyethylene composites is investigated experimentally as a function of filler concentration and the measured values are compared with the existing theoretical and empirical models. Samples are prepared by mixing commercial high density polyethylene and filler materials at various volumetric concentrations, the mixed powder is then placed in a die and melted at 185 °C under 4 MPa pressure. After cooling and solidification under pressure, the sample is taken out of the die. The thermal conductivity of the prepared samples is measured using the Shotherm QTM-D2 thermal conductivity meter working with a modified hot wire technique in a temperature range from about 0 °C to 70 °C.

Keywords

• Thermal conductivity, Composite, Polyethylene.

ALÜMİNYUM OKSİT TANE KATKILI POLİETİLEN MATRİKSLİ KOMPOZİTLERİN ISI İLETİM KATSAYISI

Abstract

Bu çalışmada, yüksek yoğunluklu polietilen kompozit malzemelerin ısı iletim katsayısı, dolgu malzemesi konsantrasyonunun bir fonksiyonu olarak deneysel şekilde araştırılmıştır ve elde edilen ölçüm değerleri, literatürdeki teorik ve ampirik model sonuçlarıyla karşılaştırılmıştır. Yüksek yoğunluklu polietilen ve toz katkı malzemesi kullanılarak değişik hacimsel konsantrasyonlarda karışımlar elde edilmiştir. Bu toz halindeki karışımlar, 4 MPa basınç altında 185 °C sıcaklıkta sıkıştırma işlemine tabi tutulmuştur ve soğumaya bırakılarak katılaşması sağlanmıştır. Hazırlanan örneklerin ısı iletim katsayıları, "Hot-Wire" yöntemi ile çalışan ve 0 °C den 70 °C ye kadar olan sıcaklık aralığında ölçüm yapabilecek şekilde geliştirilmiş olan "Shotherm QTM-D2" cihazı ile ölçülmüştür.

Keywords

• Isı iletim katsayısı, Kompozit, Polietilen